Road and bridge caulking asphalt and preparation method thereof

A kind of asphalt, road and bridge technology, which is applied in the field of road and bridge caulking asphalt and its preparation, can solve the problems such as poor application effect, and achieve the effect of good impact resistance, high and low temperature resistance, and stable structure

Inactive Publication Date: 2018-05-01
许炜玮
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the technologies disclosed in these patents are not very effective in some areas where the temperature difference between morning and evening is particularly large, especially in the desert edge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A road and bridge caulking asphalt, comprising the following ingredients in weight percentage: 60% of petroleum asphalt, 8% of compatibilizer, 0.8% of stabilizer, 0.15% of antioxidant, 0.03% of modified graphene oxide, and 0.35% of modified bagasse molecular sieve and SBS margin.

[0029] The compatibilizer is high aromatic olefin; the stabilizer is zinc oxide; the antioxidant is any one of antioxidant 168, antioxidant 2246-A, and antioxidant 1010.

[0030] The graphene oxide is aluminum hydroxide modified graphene oxide.

[0031] The modified bagasse molecular sieve is iron oxide modified bagasse molecular sieve.

[0032] A preparation method for road and bridge caulking asphalt, comprising the following steps:

[0033] A. After mixing graphene oxide and modified bagasse molecular sieve, add 50% compatibilizer, wet grinding, and mix well;

[0034] B. In the high-shear mixer, adjust the stirring speed to 5500r / min, heat the petroleum asphalt to 205°C, add the remaini...

Embodiment 2

[0046] A road and bridge caulking asphalt, comprising the following ingredients in weight percentage: 65% of petroleum asphalt, 5% of compatibilizer, 1% of stabilizer, 0.05% of antioxidant, 0.05% of modified graphene oxide, and 0.2% of modified bagasse molecular sieve and SBS margin.

[0047] The compatibilizer is high aromatic olefin; the stabilizer is zinc oxide; the antioxidant is any one of antioxidant 168, antioxidant 2246-A, and antioxidant 1010.

[0048] The graphene oxide is aluminum hydroxide modified graphene oxide.

[0049] The modified bagasse molecular sieve is iron oxide modified bagasse molecular sieve.

[0050] A preparation method for road and bridge caulking asphalt, comprising the following steps:

[0051] A. After mixing graphene oxide and modified bagasse molecular sieve, add 50% compatibilizer, wet grinding, and mix well;

[0052]B. In the high-shear mixer, adjust the stirring speed to 6000r / min, heat the petroleum asphalt to 180°C, add the remaining 5...

Embodiment 3

[0064] A road and bridge caulking asphalt, comprising the following components in weight percentage: 50% of petroleum asphalt, 10% of compatibilizer, 0.5% of stabilizer, 0.2% of antioxidant, 0.01% of modified graphene oxide, and 0.5% of modified bagasse molecular sieve and SBS margin.

[0065] The compatibilizer is high aromatic olefin; the stabilizer is zinc oxide; the antioxidant is any one of antioxidant 168, antioxidant 2246-A, and antioxidant 1010.

[0066] The graphene oxide is aluminum hydroxide modified graphene oxide.

[0067] The modified bagasse molecular sieve is iron oxide modified bagasse molecular sieve.

[0068] A preparation method for road and bridge caulking asphalt, comprising the following steps:

[0069] A. After mixing graphene oxide and modified bagasse molecular sieve, add 50% compatibilizer, wet grinding, and mix well;

[0070] B. In the high-shear mixer, adjust the stirring speed to 4000r / min, heat the petroleum asphalt to 220°C, add the remaining...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a road and bridge caulking asphalt. The road and bridge caulking asphalt comprises the following ingredients: a petroleum asphalt, a compatilizer, a stabilizer, an antioxidant,a flow modifier, a modified oxidized graphene, a modified bagasse molecular sieve, and SBS. The oxidized graphene and the bagasse molecular sieve are added, a net-shaped structure is formed in the inner part of the asphalt without crosslinking, the shock resistance effect is good; part of aluminum hydroxide and ferric oxide form a high-temperature-resistant high-stability hercynite structure at the high temperature, the high-temperature-resistant high-stability hercynite structure is adhered to the formed net-shaped structure, the structure is stabler, the high and low temperature resistanceproperty is better, the asphalt also has the functions of being waterproof, ultraviolet-proof and antiflaming at the same time; the bagasse molecular sieve is modified, so that the reaction effect isbetter in the subsequent process of reaction with the aluminum hydroxide. In conclusion, the road and bridge caulking asphalt can still be normally used for a long term even under the environment withthe limit difference of temperature.

Description

technical field [0001] The invention relates to the technical field of road surfaces, in particular to a road bridge caulking asphalt and a preparation method thereof. Background technique [0002] At present, road caulking and sealing materials have relatively mature technology and equipment abroad, and have also been widely used. The research and production of our caulking and sealing materials are still in the exploratory stage. Compared with foreign developed countries, the quality is far behind, and the production technology is far from mature. Generally, ordinary road asphalt is used, but the high and low temperature performance of ordinary road asphalt is poor. , easy to fall off, can not effectively prevent rainwater from leaking into the base from the joints and prevent debris such as sand and gravel from being embedded in the joints to cause the concrete panels to be crushed, which seriously affects the quality and service life of the road bridge deck. This is also...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08K13/06C08K3/04C08K3/22C08K9/02C08K7/24
Inventor 许炜玮刘丽坤闫小琳李梅庞游洋胡玉梅郭兵刘圣星黄伟冯志红
Owner 许炜玮
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement