Preparation method of coating wall cloth

A technology for wall coverings and coatings, applied in the direction of fireproof coatings, coatings, building components, etc., can solve the problems of low tensile strength, high cost, easy to pull damage, etc., and achieve simple preparation methods, low production costs, The effect of high tensile strength

Active Publication Date: 2018-05-08
浙江小轩窗家居股份有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a preparation method of paint wall coverings to solve the existing technical problems of paint wall coverings such as high cost, low tensile strength, non-environmental protection and easy damage ;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of coating wall cloth
  • Preparation method of coating wall cloth
  • Preparation method of coating wall cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1 discloses a kind of preparation method of paint wall covering, comprises following preparation steps:

[0026] Step 1. Production of fiber wall covering

[0027] First, the glass fiber material is acid-treated, and the acid used in the acid treatment is hydrochloric acid with a concentration of 5%, so that the SiO in the glass fiber 2 The mass percentage content is increased to more than 50%; then the acid-treated glass fiber material is washed with water to remove residual acid on the surface, and then dried to remove surface moisture; finally, the glass fiber material after water washing and drying is used on the surface Activating agent carries out surface activation treatment, and surfactant is titanate coupling agent, obtains fiber wall covering; Glass fiber in the present embodiment is alkali-resistant glass fiber, because its holding force is strong, modulus of elasticity, impact resistance, High tensile and bending strength, non-combustible, anti-f...

Embodiment 2

[0033] Embodiment 2 discloses a kind of preparation method of paint wall covering, comprises following preparation steps:

[0034] Step 1. Production of fiber wall covering

[0035] First, the glass fiber material is acid-treated, and the acid used in the acid treatment is dilute sulfuric acid with a concentration of 5%, so that the SiO in the glass fiber 2 The mass percentage content is increased to 58%; then the acid-treated glass fiber material is washed with water to remove residual acid on the surface, and then dried to remove surface moisture; finally, the glass fiber material after washing and drying is treated with surface active The surfactant is used for surface activation treatment, and the surfactant is a titanate coupling agent to obtain fiber wall covering; the glass fiber is E glass fiber. E glass fiber has good electrical insulation and mechanical properties, because of its weak acid resistance, it needs to be modified; VAE emulsion has high acid and alkali re...

Embodiment 3

[0041] Embodiment 3 discloses a kind of preparation method of paint wall covering, comprises following preparation steps:

[0042] Step 1. Production of fiber wall covering

[0043] First, the glass fiber material is acid-treated, and the acid used in the acid treatment is hydrochloric acid with a concentration of 5%, so that the SiO in the glass fiber 2 The mass percentage content is increased to 50%; then the glass fiber material after the acid treatment is washed with water to remove the residual acid solution on the surface, and then dried to remove the surface moisture; finally, the glass fiber material after the water washing and drying treatment is treated with surface active The surfactant is used for surface activation treatment, and the surfactant is a titanate coupling agent to obtain a fiber wall covering; wherein the glass fiber is an alkali-resistant glass fiber.

[0044] Step 2. Preparation of coating

[0045] Mix 38 parts of hydroxyacrylic resin, 20 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a coating wall cloth. The preparation method of the coating wall cloth comprises the following preparation steps of step one, production of fiber wall cloth, wherein a glass fiber material is subjected to acid treatment, then washed with water to remove surface residual acid and dried; a surfactant is used for surface activation treatment on the glass fiber material to obtain the fiber wall cloth; step two, preparation of a coating, wherein hydrogen acrylic resin, acrylic ester, flame retardant, film-forming agent and nano-silica are mixed uniformly and then ball-milled; then the mixture is compounded with VAE emulsion, pigment, defoamer and diluent to obtain the coating; step three, preparation of the coating wall cloth, wherein the coatingis applied to the surface of the fiber wall cloth by a roll coater, and the coating wall cloth is obtained after drying. The preparation method of the coating wall cloth makes improvement to solve thetechnical problems of the existing wall cloth, for example, poor flame retardancy, insusceptible stretching, low strength and poor flexibility; the coating wall cloth obtained by the preparation method has higher flame retardancy, tensile resistance, higher tensile strength and superior flexibility.

Description

technical field [0001] The invention relates to the field of wall coverings, in particular to a method for preparing paint wall coverings. Background technique [0002] Wall cloth is a special kind of "paper" and "cloth" that is pasted on the wall for decoration. It is a commonly used decorative material for interior walls of buildings. Wall coverings originated in France and were originally used to replace expensive tapestries, and later spread to European countries. The decoration of the wall covering mainly reflects the culture, while the functionality reflects the safety, environmental protection, energy saving and low carbon performance of the multifunctional aggregation. The color, pattern, and texture of the wall covering can be carefully designed to better meet the needs of various environments and meet the aesthetics of modern people at all levels, thereby creating a luxurious, warm, comfortable, and healthy environment for people. Wall decoration materials are in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N7/00D06N3/04D06N3/00C09D4/02C09D4/06C09D5/18C09D7/61C09D7/65
CPCC09D4/06C09D5/18D06N3/0022D06N3/0059D06N3/042D06N7/0002D06N2209/067D06N2209/10D06N2211/063
Inventor 陈雨薇