A kind of preparation method of fully mixed nickel slag ready-mixed concrete

A technology for ready-mixed concrete and nickel slag, applied in the field of concrete, can solve the problems of micro-cracks in cement components, cement should not be made into super-long components, and limit the use range of cement, and achieve the effect of reducing cost and good shrinkage performance.

Active Publication Date: 2018-10-23
YANCHENG GUOTAI CONCRETE +1
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Usually the hardening shrinkage of Portland cement concrete is its serious shortcoming, which will lead to problems such as cement not being suitable for making super-long components, and micro-cracks in cement components, which seriously limits the scope of use of cement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of fully mixed nickel slag ready-mixed concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] After crushing, grinding and grading, the nickel slag is soaked in a treatment tank filled with saturated lime water for 1 day, then taken out and dried. The quality of P.O 42.5 ordinary Portland cement is 200kg, the quality of water is 175kg, the quality of nickel slag powder is 160kg, the quality of nickel slag sand is 600kg for coarse nickel sand, the quality of fine nickel sand is 200kg, and the quality of nickel slag for coarse bone The quality of material is 1050kg. Each raw material component was manually compacted according to the above ratio according to the method of GB50081-2002 "Standard for Test Methods of Mechanical Properties of Ordinary Concrete" to prepare a cube standard test block with a side length of 150 mm. Place it in a standard curing box (at a temperature of about 25°C and a humidity of about 95%) for 48 hours, then remove the mold, and continue to maintain at 20°C with a humidity of about 95% for 28 days to obtain a standard test block of high-...

Embodiment 2

[0030] After crushing, grinding and grading, the nickel slag is soaked in a treatment tank filled with saturated lime water for 2 days, then taken out and dried. The quality of P.O 42.5 ordinary Portland cement is 200kg, the quality of water is 175kg, the quality of nickel slag powder is 160kg, the quality of nickel slag sand is 600kg for coarse nickel sand, the quality of fine nickel sand is 200kg, and the quality of nickel slag for coarse bone The quality of material is 1050kg. Each raw material component was manually compacted according to the above ratio according to the method of GB50081-2002 "Standard for Test Methods of Mechanical Properties of Ordinary Concrete" to prepare a cube standard test block with a side length of 150 mm. Place it in a standard curing box (at a temperature of about 25°C and a humidity of about 95%) for 48 hours, then remove the mold, and continue to maintain at 20°C with a humidity of about 95% for 28 days to obtain a standard test block of high...

Embodiment 3

[0032] After crushing, grinding and grading, the nickel slag is soaked in a treatment tank filled with saturated lime water for 3 days, then taken out and dried. The quality of P.O 42.5 ordinary Portland cement is 200kg, the quality of water is 175kg, the quality of nickel slag powder is 160kg, the quality of nickel slag sand is 600kg for coarse nickel sand, the quality of fine nickel sand is 200kg, and the quality of nickel slag for coarse bone The quality of material is 1050kg. Each raw material component was manually compacted according to the above ratio according to the method of GB50081-2002 "Standard for Test Methods of Mechanical Properties of Ordinary Concrete" to prepare a cube standard test block with a side length of 150 mm. Place it in a standard curing box (at a temperature of about 25°C and a humidity of about 95%) for 48 hours, then remove the mold, and continue to maintain at 20°C with a humidity of about 95% for 28 days to obtain a standard test block of high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of premixed concrete fully doped with nickel slag. The method comprises the following steps: (1) carrying out pretreatment on the nickel slag: pouring thenickel slag into a crusher for crushing; then, classifying the crushed nickel slag according to particle sizes, and grinding fine powder again to obtain nickel slag powder; (2) respectively dipping the nickel slag powder, relatively coarse nickel slag and coarse nickel slag into saturated limewater for 1-6 days, fishing out and drying for later use; (3) mixing: mixing the following raw materialsin parts by weight: 190-210 parts of cement, 170-180 parts of water, 150-170 parts of the nickel slag powder, 800 parts of the relatively coarse nickel slag and 1050 parts of the coarse nickel slag. According to the preparation method, the nickel slag is prepared into admixture, fine aggregate and coarse aggregate of the concrete, and the conventional admixture, fine aggregate and coarse aggregatein the concrete are completely replaced with the admixture, the fine aggregate and the coarse aggregate which are prepared from the nickel slag, so that the raw material cost of the concrete is significantly reduced. A certain amount of Mg(OH)2 is generated in a hydration process by using magnesium oxide mineral existing in the nickel slag, so that a certain volume is increased, and a concrete product which has good shrinkage property and even does not shrink can be prepared.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a method for preparing ready-mixed concrete fully mixed with nickel slag. Background technique [0002] Nickel slag is a kind of industrial waste slag formed during the smelting of nickel alloys. Calculated by the amount of nickel slag discharged per 1 ton of nickel produced in the metallurgical process, about 20-30 tons of nickel slag is discharged. In 2016 alone, the nickel slag produced nationwide reached 3000-4000 tons. The slag was piled up on the open field of the smelting factory nearby, occupying the land and causing environmental and health problems. Therefore, it is urgent to propose an effective way to treat and reuse nickel slag. Yang Dingyi, Li Hao et al. used nickel slag powder and larger particle size nickel slag sand to partially replace cement and sand, respectively, to prepare high-strength and wear-resistant concrete, and its strength grade reached the C40 st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/02C04B18/14
CPCC04B20/026C04B28/04C04B18/144C04B20/0076C04B20/023Y02W30/91
Inventor 仓定龙侯贵华陈佳男高峰陈龙成辉仓东婷成海翔徐嵘仓东芝
Owner YANCHENG GUOTAI CONCRETE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka