Acid-resistant non-cured waterproof coating and production technology thereof

A waterproof coating and production process technology, applied in the direction of asphalt coatings, coatings, etc., can solve the problems of being easily corroded and peeled off, difficult to achieve waterproof effect, poor acid resistance, etc., and achieve long service life, excellent water resistance and adhesion, Strong acid resistance

Active Publication Date: 2018-07-06
河南蓝翎环科防水材料有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current non-curing waterproof coatings have poor acid resistance, making them easily corroded and peeled off in an acidic environment, making it difficult to achieve long-term waterproofing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The present embodiment provides an acid-resistant non-cured waterproof coating, the composition of which includes by parts by weight:

[0033] 60 parts of modified emulsified asphalt, 40 parts of styrene-butadiene rubber, 20 parts of styrene-butadiene block copolymer, 15 parts of dimethyl silicone oil, 5 parts of hydrogenated rosin, 16 parts of aluminum tripolyphosphate, and 15 parts of epoxy resin , and 16 parts of anionic polyacrylamide.

[0034] Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 80 parts of base asphalt, 3 parts of SBR rubber powder, cetyl bromide 4 parts of pyridine.

[0035] The production process of this acid-resistant non-curing waterproof coating includes:

[0036] Mix modified emulsified asphalt, styrene-butadiene rubber, styrene-butadiene block copolymer and anionic polyacrylamide in parts by weight, heat to...

Embodiment 2

[0039] The present embodiment provides an acid-resistant non-cured waterproof coating, the composition of which includes by parts by weight:

[0040] 70 parts of modified emulsified asphalt, 30 parts of styrene-butadiene rubber, 30 parts of styrene-butadiene block copolymer, 10 parts of dimethyl silicone oil, 8 parts of hydrogenated rosin, 12 parts of aluminum tripolyphosphate, 30 parts of epoxy resin , and 10 parts of triethanolammonium salt.

[0041] Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 70 parts of base asphalt, 10 parts of SBR rubber powder, cetyl bromide 6 parts of pyridine.

[0042] The production process of this acid-resistant non-curing waterproof coating includes:

[0043] Mix the modified emulsified asphalt, styrene-butadiene rubber, styrene-butadiene block copolymer and triethanolammonium salt in parts by weight, and ...

Embodiment 3

[0046] The present embodiment provides an acid-resistant non-cured waterproof coating, the composition of which includes by parts by weight:

[0047] 65 parts of modified emulsified asphalt, 37 parts of styrene-butadiene rubber, 24 parts of styrene-butadiene block copolymer, 13 parts of dimethyl silicone oil, 6 parts of hydrogenated rosin, 14 parts of aluminum tripolyphosphate, 24 parts of epoxy resin , and 15 parts of succinate sulfonate.

[0048]Among them, the modified emulsified asphalt is cationic rubber elastomer modified emulsified asphalt, and the components of cationic rubber elastomer modified emulsified asphalt include: 75 parts of base asphalt, 7 parts of SBR rubber powder, cetyl bromide 5 parts pyridine.

[0049] The production process of this acid-resistant non-curing waterproof coating includes:

[0050] Mix the modified emulsified asphalt, styrene-butadiene rubber, styrene-butadiene block copolymer and succinate sulfonate in parts by weight, and heat to 210°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an acid-resistant non-cured waterproof coating, and belongs to the field of waterproof materials. The waterproof coating comprises the following components in parts by weight: modified emulsified asphalt, butadiene styrene rubber, styrene-butadiene segmented copolymer, dimethicone, hydrogenated rosin, aluminum triphosphate, epoxy resin and an anionic surfactant. The preparation technology comprises the following steps: mixing the modified emulsified asphalt, butadiene styrene rubber, styrene-butadiene segmented copolymer and the anionic surfactant in parts by weight to obtain a fused substrate; then mixing the epoxy resin and aluminum triphosphate with the fused substrate, heating at the temperature of 150 to 170 DEG C for 40 to 70 min, cooling to temperature of 60 to 80 DEG C, then adding dimethicone and hydrogenated rosin, and stirring for 70 to 90 min. The coating is good in waterproof performance and has relatively high acid resistance, long-lasting waterproof characteristic can be maintained in an acidic environment, and the adhesive performance and self-healing performance are preferable.

Description

technical field [0001] The invention relates to the field of waterproof materials, in particular to an acid-resistant non-curing waterproof coating and a production process thereof. Background technique [0002] Non-curing rubber asphalt waterproof coating, made of rubber and asphalt as the main component, mixed with additives, is a waterproof coating that maintains a viscous paste within the service life. It has a prominent effect on the waterproof treatment of special parts such as deformation joints in construction projects, and is widely used in non-exposed building waterproof projects. [0003] Non-curing rubber asphalt waterproof coating is a kind of creep waterproof coating, which also has good bonding ability with metal, non-metal and concrete substrates, and has dual functions of waterproof and metal anticorrosion. Non-curing rubber asphalt waterproof coating has many advantages, such as: it will never harden, the cured content is more than 99%, does not contain vo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D7/65C09D7/61
CPCC08K2003/321C08L2201/08C08L2205/035C09D195/00C08L9/06C08L53/02C08L83/04C08L93/04C08L63/00C08K3/32C08K5/3432
Inventor 李宏伟苏怀武牛恒李翔
Owner 河南蓝翎环科防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com