A kind of preparation method of composite bulletproof ceramic plate

A ceramic plate, aluminum hydroxide technology, applied in protective equipment, offensive equipment, armor, etc., can solve the problem of low performance of bulletproof plates, and achieve the effect of improving ballistic resistance, mechanical conductivity, and flexibility.

Active Publication Date: 2020-08-18
宁波众基精瓷科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems in the prior art, the present invention provides a method for preparing a composite bulletproof ceramic plate, which solves the problem of low overall performance of the existing bulletproof plate, and has the characteristics of bulletproof effect, good connectivity of the ceramic plate and long service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of a composite bulletproof ceramic plate, said preparation method according to the following steps:

[0031] Step 1, adding aluminum hydroxide to deionized water, then adding polyvinyl alcohol, and ultrasonically reacting for 20 minutes to obtain an aluminum hydroxide dispersion;

[0032] Step 2, adding the aluminum hydroxide dispersion to a vacuum distillation kettle for a vacuum distillation reaction for 1 hour to obtain a viscous liquid;

[0033] Step 3, add the viscous liquid into the mold and evaporate it with slight heat for 20 minutes, and solidify to obtain the precursor plate;

[0034] Step 4, put the precursor plate into the reaction kettle to heat and pressurize for 3 hours to obtain the first ceramic plate;

[0035] Step 5, putting the dense ceramic plate into absolute ethanol, then adding graphene powder and ultrasonically reacting for 3 hours to obtain the second ceramic plate;

[0036] Step 6: Put the second ceramic plate into the r...

Embodiment 2

[0046] A preparation method of a composite bulletproof ceramic plate, said preparation method according to the following steps:

[0047] Step 1, adding aluminum hydroxide to deionized water, then adding polyvinyl alcohol, and ultrasonically reacting for 40 minutes to obtain an aluminum hydroxide dispersion;

[0048] Step 2, adding the aluminum hydroxide dispersion to a vacuum distillation kettle for 3 hours of vacuum distillation to obtain a viscous liquid;

[0049] Step 3, add the viscous liquid into the mold and evaporate it with slight heat for 30 minutes, and solidify to obtain the precursor plate;

[0050] Step 4, put the precursor board into the reaction kettle to heat and pressurize for 8 hours to obtain the first ceramic board;

[0051] Step 5, put the dense ceramic plate into absolute ethanol, and then add graphene powder for ultrasonic reaction for 6 hours to obtain the second ceramic plate;

[0052] Step 6: Put the second ceramic plate into the reaction kettle for...

Embodiment 3

[0062] A preparation method of a composite bulletproof ceramic plate, said preparation method according to the following steps:

[0063] Step 1, adding aluminum hydroxide to deionized water, then adding polyvinyl alcohol, and ultrasonically reacting for 30 minutes to obtain an aluminum hydroxide dispersion;

[0064] Step 2, adding the aluminum hydroxide dispersion into a vacuum distillation kettle for a vacuum distillation reaction for 2 hours to obtain a viscous liquid;

[0065] Step 3, add the viscous liquid into the mold and evaporate it with slight heat for 25 minutes, and solidify to obtain the precursor plate;

[0066] Step 4, put the precursor board into the reaction kettle to heat and pressurize for 5 hours to obtain the first ceramic board;

[0067] Step 5, putting the dense ceramic plate into absolute ethanol, then adding graphene powder and ultrasonically reacting for 5 hours to obtain the second ceramic plate;

[0068] Step 6: Put the second ceramic plate into the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of functional ceramics, and specifically relates to a preparation method of a composite bulletproof ceramic plate. Step 1, adding aluminum hydroxide to deionized water, then adding polyvinyl alcohol, and ultrasonically reacting for 20-40 minutes to obtain aluminum hydroxide dispersion liquid; Step 2, adding the aluminum hydroxide dispersion to a vacuum distillation kettle for 1-3h underpressure distillation to obtain a viscous liquid; Step 3, adding the viscous liquid to the mold and evaporating with slight heat for 20-30min, and solidifying to obtain Precursor plate; step 4, put the precursor plate in the reactor to heat and pressurize for 3-8 hours to obtain the first ceramic plate; step 5, put the dense ceramic plate in absolute ethanol, and then add graphene powder for ultrasonic React for 3-6 hours to obtain the second ceramic plate; step 6, put the second ceramic plate in the reaction kettle for a second heating and pressurizing reaction for 5-7 hours to obtain the composite bulletproof ceramic plate. The invention solves the problem of low overall performance of the existing bulletproof plate, and has the characteristics of bulletproof effect, good connection of the ceramic plate and long service life.

Description

technical field [0001] The invention belongs to the technical field of functional ceramics, and in particular relates to a preparation method of a composite bulletproof ceramic plate. Background technique [0002] Some ceramic composite bulletproof panels are mainly composed of a bulletproof backplane and multiple bulletproof ceramic blocks located on the bulletproof backplane. Although the existing ceramic composite bulletproof panels are very cost-effective, there are at least the following types of ceramic composite bulletproof panels: Several problems: first, the overall weight of the existing ceramic composite bullet-proof panels is generally on the high side; second, in the existing ceramic composite bullet-proof panels, the ballistic performance of the joints between the bulletproof ceramic blocks is very weak; third, the current The bulletproof principle of the ceramic composite bulletproof plate relies on increasing the penetration resistance of the bullet to achiev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F41H5/00C04B37/00C04B35/10C04B41/85C04B41/83
CPCC04B35/10C04B37/008C04B41/009C04B41/5001C04B41/83C04B41/85F41H5/00C04B41/4869
Inventor 刘伟
Owner 宁波众基精瓷科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap