Environment-friendly hot melt glue capable of bonding biodegradable express bag and preparation method and application of environment-friendly hot melt glue

A biodegradable and environmentally friendly technology, applied in the direction of adhesive types, adhesives, rosin adhesives, etc., can solve the problems of limited development, loss of adhesion, and bonding restrictions of logistics enterprises, and achieve good substrate damage effects, Excellent bonding performance and good adhesion effect

Inactive Publication Date: 2018-08-14
GUANGDONG RURGA NEW MATERIAL TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These traditional SBC formula hot melt adhesives have the following problems for highly polar biodegradable courier bags: 1) Adhesion restrictions, the general courier bag bonding temperature is 5-45 ° C, while traditional courier bag hot melt adhesives can Biodegradable courier bags are difficult to bond, or the applicable temperature range is narrow, such as not applicable at 20°C, etc.
2) Use time limit: With the degradation of the biodegradable courier bag itself, the surface of the courier bag changes, resulting in difficulty in bonding
The above problems will lead to the following risks: 1) The express delivery process may experience different temperature environments. Traditional express bag hot melt adhesives have a narrow temperature range for biodegradable express bags and there is a risk of loss of viscosity, causing express items to fall out, etc.
2) The hot melt adhesive of the traditional express bag is difficult to bond the surface of the express bag after spontaneous degradation, resulting in a short service life of the biodegradable express bag and the failure of the express bag
3) The development of logistics enterprises is limited, and there is always no feasible solution for the bonding of biodegradable express bags

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An environment-friendly hot-melt adhesive capable of laminating a biodegradable express bag and a preparation method thereof, comprising the following steps.

[0029] Mix 30% of KN4010 naphthenic oil (Karamay), 25% of high molecular polymer (TSRC DP653N) and 0.5% of antioxidant, heat to 120-170°C, and stir until all components are completely Melt; then add 20% polyester polymer, 3% auxiliary resin (maleic anhydride grafted resin) and 21.5% tackifying resin, heat at 120-170°C until melting; vacuumize the reaction system until there is no Bubbles, stir and mix evenly, and you can get an environmentally friendly hot melt adhesive that can be attached to biodegradable express bags.

[0030] The hot-melt adhesive prepared in this example is suitable for a scraping device. Put the hot-melt adhesive in a courier bag hot-melt adhesive tank, and keep the temperature at 160°C until the rubber particles are completely melted before use. The width of the glue on the substrate is ab...

Embodiment 2

[0032] An environment-friendly hot-melt adhesive capable of laminating a biodegradable express bag and a preparation method thereof, comprising the following steps.

[0033] Mix 25% KN4010 naphthenic oil (Karamay), 20% polymer (Yuehua 1126) and 0.5% antioxidant, heat to 120-170°C, and stir until all components are completely Melt; then add 25% polyester polymer, 3% auxiliary resin (terpene phenol modified resin) and 26.5% tackifying resin, heat at 120-170°C until melting; vacuumize the reaction system until there is no Bubbles, stir and mix evenly, and you can get an environmentally friendly hot melt adhesive that can be attached to biodegradable express bags.

[0034] The hot-melt adhesive prepared in this example is suitable for scraping equipment. Put the hot-melt adhesive in a hot-melt adhesive tank and keep the temperature at 165°C until the rubber particles are completely melted before use. The thickness of the glue is about 150g / m 2 , The destruction temperature range ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses environment-friendly hot melt glue capable of bonding a biodegradable express bag and a preparation method and application of the environment-friendly hot melt glue. The environment-friendly hot melt glue is prepared from 15-35% of naphthenic oil, 10-30% of macromolecular polymer, 10-30% of polyester polymer, 0.5-5% of assistant resin, 20-50% of tackifying resin and 0.2-0.8% of an antioxidant. According to the hot melt glue, for the problem of sealing and bonding of the high-polarity biodegradable express bag, the bonding temperature range of the biodegradable express bag which is made from PBAT/PLA/PHA and other main raw materials reaches consistence with that, about 5-40 DEG C, of ordinary use PE express bags; through the hot melt glue, the problems that through atraditional SBC formula, a biodegradable substrate is difficult to bond, the substrate cannot be broken due to a weak adhesion force, and the suitable bonding temperature range is narrow are solved.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a hot-melt adhesive, in particular to an environment-friendly hot-melt adhesive which can be attached to a biodegradable express bag, and a preparation method and application thereof. Background technique [0002] Hot melt adhesives are widely used in the field of logistics, which plays a role in improving production efficiency and quality assurance in the process of industrialization in these fields. With the rapid popularization of Internet + as a new economic form. However, the degradation cycle of traditional plastic express bags is as long as 300-500 years, causing serious white pollution problems and a huge burden on the global environment. With the rapid development of the express industry, this problem has become more prominent, and biodegradable express bags have emerged as the times require. . The hot melt adhesives currently used in express bags are mainly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J191/00C09J157/02C09J193/04C09J11/08
CPCC08L2205/035C09J11/08C09J157/02C09J191/00C09J193/04C08L53/02C08L67/00C08L51/00C08L57/02C08L93/04C08L91/00
Inventor 万诚陆锐根陈兴
Owner GUANGDONG RURGA NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap