A joint refractory material and construction method for heat replacement of converter bottom

A refractory material and converter bottom technology, applied in the field of steelmaking, can solve the problems of low filler life, inability to ensure filler compactness, insufficient fluidity, etc., and achieve good resistance to slag erosion, normal and safe production, and good self-flowing properties Effect

Active Publication Date: 2021-07-23
SHOUGANG CORPORATION
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of quickly replacing the bottom of the converter, the main difficulty lies in the compactness of the filler in the gap between the magnesia-carbon refractories built on the steel shell of the furnace bottom and the magnesia-carbon refractories built on the steel shell of the furnace body However, in the existing technology, the gaps are basically compacted by the self-flow of the filler. Due to insufficient fluidity, the compactness of the filler cannot be ensured, resulting in a low life of the filler, or even only More than a dozen furnaces, so there is a need for a seam refractory material for converter bottom heat replacement that can be pumped mechanically and has a long service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A joint refractory material for heat replacement of the converter bottom according to Embodiment 1 of the present invention is composed of a first component and a second component, wherein the first component is: fused magnesia 82wt% , ultra-high temperature asphalt balls 3wt%, graphite 4wt%, metal aluminum powder 9wt%, metal silicon powder 2wt%; the second component includes thermosetting phenolic resin, ethylene glycol and hexamethylenetetramine, and thermosetting phenolic resin accounts for the first 9 wt% of the components, ethylene glycol accounts for 12 wt% of the first component, and curing agent accounts for 0.5 wt% of the first component.

[0041] Further, in Example 1 of the present invention, the maximum particle size of magnesia is 8mm, and the content of MgO in the magnesia particles is 98wt%.

[0042] Put the magnesia, asphalt, graphite, metal powder and curing agent in the above weight ratio into the mixer for 3 minutes, then add the pre-mixed resin and a...

Embodiment 2

[0048]A joint refractory material for heat replacement of the converter bottom according to Embodiment 2 of the present invention is composed of a first component and a second component, wherein the first component is: 75wt% of sintered magnesia, Ultra-high temperature asphalt balls 7wt%, graphite 6wt%, metal aluminum powder 9wt%, metal silicon powder 3wt%; the second component includes epoxy resin, ethylene glycol and hexamethylenetetramine, and epoxy resin accounts for the first component 10% by weight of the part, 12% by weight of the ethylene glycol of the first component, and 1% by weight of the curing agent of the first component.

[0049] Further, the maximum particle size of the magnesia in Example 2 of the present invention is 5mm, and the MgO content in the magnesia particles is 96wt%.

[0050] Put the magnesia, asphalt, graphite, metal powder and curing agent in the above weight ratio into the mixer for 6 minutes, then add the pre-mixed resin and alcohol, and stir f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a joint refractory material for heat replacement of the furnace bottom of a converter, a configuration method and a construction method thereof. Wherein, the joint refractory material is configured by a first component and a second component, and the first component by weight percentage is: magnesia 63-85wt%, asphalt 3-10wt%, graphite 4-10wt% %, metal powder 2-17wt%; the second component includes 5-15wt% resin, 5-15wt% alcohol and 0.5-1.5wt% curing agent based on the weight of the first component. The invention can meet the requirements of the life span of 1000-2000 furnaces when the bottom of the converter is replaced in the new furnace service or in the mid-term of the furnace service, and ensures the normal and safe production of the converter.

Description

technical field [0001] The invention belongs to the technical field of steelmaking, and in particular relates to a seam refractory material for heat replacement of a converter bottom and a construction method. Background technique [0002] The converter is mainly used to produce carbon steel, alloy steel and smelt copper and nickel, and is currently the most commonly used steelmaking equipment. The life of the converter lining is an important factor affecting the continuity of the steelmaking process. [0003] In order to obtain greater output, the converter has been pursuing a longer furnace life for a long time, and the furnace life can even reach more than 10,000 furnace times. However, in the current steelmaking process, the life of the furnace lining at the bottom of the converter is difficult to synchronize with the life of the furnace lining. According to statistics, when the furnace age of most converters reaches 2,000 furnace times, it is difficult to ensure that t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/043
CPCC04B35/043C04B2235/402C04B2235/425C04B2235/428C04B2235/96
Inventor 崔园园钟凯尹娜高攀曹勇李海波王新华朱国森田志红崔阳彭开玉刘风刚贾祥超邵俊宁
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products