Plating solution

A technology of electroplating solution and solution, which is applied in the field of electroplating solution, can solve the problems of corrosion configuration cost, poor heat resistance of electroplating solution, pinholes and pitting of plating layer, etc., and achieves not easy to spot corrosion, good heat resistance and long service life Effect

Inactive Publication Date: 2018-08-24
CHENGDU LIANLIDA HARDWARE PROD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, when the mesh belt resistance furnace is used for quenching, the oil and dust on the surface of the workpiece are mixed together and sintered into stubborn solid grease. , It is difficult to completely remove the above dirt during electroplating. Hydrogen bubbles tend to adhere to the dirt and are difficult to discharge, resulting in pinholes and pitting in the coating, and as the bubbles gradually grow, the coating will automatically burst. , produces peeling phenomenon, which leads to the disadvantages of poor heat resistance of the plating solution, serious corrosion and high configuration cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An electroplating solution is prepared from the following raw materials in parts by weight: 1 part of sodium potassium tartrate, 4 parts of thiohydantoin, 15 parts of sodium n-octyl sulfate, and 40 parts of nickel sulfate solution.

Embodiment 2

[0015] An electroplating solution is prepared from the following raw materials in parts by weight: 4 parts of sodium potassium tartrate, 7 parts of thiohydantoin, 19 parts of sodium n-octyl sulfate, and 46 parts of nickel sulfate solution.

Embodiment 3

[0017] An electroplating solution is prepared from the following raw materials in parts by weight: 6 parts of sodium potassium tartrate, 11 parts of thiohydantoin, 20 parts of sodium n-octyl sulfate, and 50 parts of nickel sulfate solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a plating solution, made from, by weight, 1-6 parts of potassium sodium tartrate, 4-11 parts of thiohydantoin, 15-20 parts of sodium octyl sulfate, and 40-50 parts of nickel sulfate solution. The plating solution has stable composition; a plating layer made with the plating solution has good heat resistance, rarely experiences spot corrosion and has long life.

Description

technical field [0001] The invention relates to the field of electroplating, in particular to an electroplating solution. Background technique [0002] During the machining process, thick dirt will form on the surface of parts. If the above dirt is not removed before heat treatment, it will be hard to clean after quenching and sintering into stubborn solid oil and rust, and bubbles will adhere to it during plating to form gas retention pinholes in the coating. The surface of the heat treatment workpiece will inevitably adhere to a layer of oil. When the dust falls on the surface and mixes with the grease, it will be difficult to clean it after a long time, so that the surface of the workpiece will form small oil spots that are not obvious. When air bubbles stay on it, pinholes are formed. In addition, when the mesh belt resistance furnace is used for quenching, the oil stains on the surface of the workpiece are mixed with dust and other impurity particles, and sintered int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/12
CPCC25D3/12
Inventor 姚小林
Owner CHENGDU LIANLIDA HARDWARE PROD