Production process of wool terylene blended smooth double-faced woolen goods

A production process, double-sided woolen technology, applied in the processing of textile materials, textiles, textiles and papermaking, etc., can solve the limitation of wool and cashmere application fields and market expansion, the thickening of wool and sheep wool tops, and affect the appearance of the fabric. and wearability and other issues, to achieve the effect of improving the feel and style, rich hair feeling, and smooth hair direction

Active Publication Date: 2018-08-28
江阴市长泾花园毛纺织有限公司
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, wool and sheep wool strips become thicker, stiffer, smaller in size, fuzzy in surface structure, and less elastic, which seriously affects the appearance and wearability of fabrics, and limits the application fields and market expansion of wool and sheep wool to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of production technology of wool polyester blended smooth wool double-faced woolen, described production technology comprises following process steps:

[0033] Step 1: Pretreatment of raw materials: Put Australian wool tops and sheep wool top fibers in a washing machine for cleaning. The cleaning solution formula is: wool cleaning agent 5g / L, wool protection agent 2g / L, at 80-90 °C Wash down for 20min, bath ratio is 1:15.

[0034] The second step: weaving the raw materials into yarn: the mass percentages of selected raw materials are: 20% Australian wool tops with a specification of 64s, 60% sheep wool tops with a specification of 64s and 20% polyester fiber strips. The raw material is made into 13 / 1 public count slub yarn through wool blending, wool beating, opening, carding, drawing, air spinning and automatic winding process, and the relative humidity is controlled in the spinning process to be 75 ~ 50%. 85%, temperature 25~30℃;

[0035] (1) Blending method:...

Embodiment 3

[0069] On the basis of embodiment 1, the difference between embodiment 3 and embodiment 1 is:

[0070] Pretreatment of raw materials: Put Australian wool tops and sheep wool top fibers in a washing machine for cleaning. The cleaning solution formula is: wool cleaning agent 10g / L, wool protection agent 5g / L, washing at 90°C for 30 minutes, liquor ratio for 1:20.

[0071] Spin raw material into yarn:

[0072] Hemao method: The amount of Hemao oil added is 3% of the quality of raw materials, the amount of water added is 15 times that of Hemao oil, the amount of antistatic agent added is 3% of the quality of raw materials, and the moisture regain of Hemao is controlled at 30-40 %. Before the mixture is put on the carding machine, it must be stuffed for 16 hours.

[0073] Carding process: the feeding quantity of the carding machine is 180g / time, the feeding cycle is 45 seconds, the speed of the delivery roller is 40r / min, and the delivery speed is 15m / min.

[0074] Spinning pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention provides a production process of wool terylene blended smooth double-faced woolen goods. The production process of the smooth double-faced woolen goods includes the steps: sufficiently mixing wool fibers and terylene fibers; spinning the mixed wool fibers and terylene fibers into yarns of 13/1 metric number by an open-end spinning frame; weaving the spun yarns on a rapier loom; performing edge sewing, fulling, scouring, dewatering, drying, decating, teasel raising, drying, anti-shrinking finishing, dyeing, softening finishing, scalding, cutting, decating and the like on a woven gray fabric to prepare a finished product. The total number of warp yarns is 6100-6300, the acting reed width is 195-200cm, porter/permeating number is 35/9, weft density is 285-290 yarns/10cm, and theweight of a fabric billet is 930-950g/m<2>. The fabric is fine, smooth and soft in hand feeling, compact in texture, bright in color and high in color fastness and does not easily felt after being washed with water.

Description

technical field [0001] The invention relates to a production process of woolen cloth, in particular to a production process of wool polyester blended smooth wool double-faced wool. Background technique [0002] As people pursue leisure, comfortable and casual life trends, there are new requirements for fabrics and their raw materials. Wool fiber is widely used in high-end clothing fabrics as a thermal fiber, and polyester fiber is also consumed for its good thermal performance. are widely recognized. However, wool and sheep wool strips become thicker, stiffer, smaller in size, fuzzy in surface structure, and less elastic, which seriously affects the appearance and wearability of fabrics, and limits the application fields and market expansion of wool and sheep wool to a certain extent. Contents of the invention [0003] The object of the present invention is to provide a wool polyester blended smooth wool double-faced woolen fabric, which has a fine and soft hand feeling, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D03D13/00D03D15/00D03D27/10D06B3/02D06B3/28D06B13/00D06M11/13D06M11/50D06P1/00D06P1/16D06P1/38D06P3/872D06M101/10D03D15/233D03D15/283D03D15/47
CPCD02G3/04D03D13/008D03D15/00D03D27/10D06B3/02D06B3/28D06B13/00D06M11/13D06M11/50D06P1/0032D06P1/16D06P1/38D06P3/8252D06M2101/10D06M2200/45D10B2331/04D10B2211/02
Inventor 赵军伟蔡红艳
Owner 江阴市长泾花园毛纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap