Space marble and preparation method thereof

A marble and space technology, applied in the field of space marble and its preparation, can solve problems such as high hardness, and achieve the effect of light weight, convenient transportation and easy transportation

Inactive Publication Date: 2018-09-04
广州市壁虎美派科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Add a smoothing agent, the surface of the product will be smooth and hard after solidification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of space marble of the present invention comprises filler, smoothing agent, sound insulation material, heat insulation material, modifier and water, and described filler is magnesium oxide, and addition amount is 43%; Described smoothing agent is magnesium chloride, addition amount The sound insulation material is vitrified microbeads, and the addition amount is 20%; the heat insulation material is foam particles, and the addition amount is 15%; the addition amount of water is 12%; the modifier addition amount is smooth 0.5% of the additive amount.

[0024] The above components are processed according to the following steps: Step S1, preparation of lubricant solution: mix and stir the lubricant magnesium chloride, modifier and water respectively, and then let it stand for 12 hours to obtain the lubricant solution, and the amount of lubricant magnesium chloride added The ratio of water addition is 1:1.2;

[0025] Step S2, material mixing: the smoothing agent solu...

Embodiment 2

[0028] A kind of space marble of the present invention comprises filler, smoothing agent, sound insulation material, heat insulation material, modifier and water, and described filler is magnesium oxide, and the addition amount is 50%; Described smoothing agent is magnesium chloride, and addition amount The sound insulation material is vitrified microspheres, and the addition amount is 15%; the heat insulation material is foam particles, and the addition amount is 10%; the addition amount of water is 14%; the modifier addition amount is smooth 0.5% of the additive amount.

[0029] The above components are processed according to the following steps: Step S1, preparation of lubricant solution: mix and stir the lubricant magnesium chloride, modifier and water respectively, and then let it stand for 12 hours to obtain the lubricant solution, and the amount of lubricant magnesium chloride added The ratio to the amount of water added is 1:1.3;

[0030] Step S2, material mixing: the...

Embodiment 3

[0033] A kind of space marble of the present invention comprises filler, smoothing agent, sound insulation material, heat insulation material, modifier and water, and described filler is magnesium oxide, and addition amount is 47.6%; Described smoothing agent is magnesium chloride, addition amount The sound insulation material is vitrified microspheres, and the addition amount is 16.6%; the heat insulation material is foam particles, and the addition amount is 12%; the addition amount of water is 13%; the modifier addition amount is smooth 0.5% of the additive amount.

[0034] The above components are processed according to the following steps: Step S1, preparation of lubricant solution: mix and stir the lubricant magnesium chloride, modifier and water respectively, and then let it stand for 12 hours to obtain the lubricant solution, and the amount of lubricant magnesium chloride added The ratio of water addition is 1:1.2;

[0035] Step S2, material mixing: the smoothing agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a space marble comprising a filling agent, a smoothing agent, a sound insulation material, a heat insulation material, a modifier and water; the filling agent is magnesium oxide; the smoothing agent is magnesium oxide; the sound insulation material is a glass bead; the heat insulation material is a foam particle; and the space marble is prepared by three steps including smoothing agent solution preparation, material mixing as well as mold pouring for solidification. The invention provides a space marble material for a wall, which is good in sound and heat insulation effects, light in weight, simple in preparation process and low in production cost.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a space marble and a preparation method thereof. Background technique [0002] Wall thermal insulation is the key to building energy saving and living comfort. Laying thermal insulation and sound insulation materials on walls has become the first choice in the construction industry because of its relatively convenient construction. At present, organic thermal insulation materials mainly include expanded polystyrene board (EPS), extruded polystyrene board (XPS), spray polyurethane (SPU), polystyrene particles, etc. Its advantages are mainly light weight, high density, and good thermal insulation effect, but there are also many disadvantages, such as aging resistance, large deformation coefficient, poor stability, poor safety and stability, easy to burn, poor ecological environmental protection, and difficult construction , high cost, etc. Foamed tiles have been developed in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B38/08C04B111/28
CPCC04B28/32C04B38/08C04B2111/28C04B22/066C04B22/124C04B18/027C04B22/002C04B22/126C04B22/16C04B22/149C04B24/045C04B22/165C04B14/06C04B24/122C04B24/2623C04B20/002
Inventor 刘文华
Owner 广州市壁虎美派科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com