Method for melting preparing of glass through glass electric melting furnace

A glass electric and electric melting furnace technology, applied in the direction of electric furnace, furnace, furnace type, etc., can solve the problems of glass energy consumption, environmental pollution, etc., and achieve the effects of reducing loss, saving raw materials, and reducing current

Inactive Publication Date: 2018-09-28
江苏宝恒新材料科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a method for melting glass in an electric glass melting furnace, which solves the existing defects of energy consumption and environmental pollution when melting glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for melting preparing of glass through glass electric melting furnace
  • Method for melting preparing of glass through glass electric melting furnace
  • Method for melting preparing of glass through glass electric melting furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0022] A method for melting glass in an electric glass melting furnace. The melting method is carried out on the electric melting furnace. The bottom of the electric melting furnace is provided with bottom electrodes and the top is provided with top electrodes. The bottom of the electric melting furnace is also provided with a flow hole. .

[0023] As a further optimization of this scheme, the melting method is as follows: by pouring the batch material into the electric melting furnace, through the mutual cooperation of the top insertion electrode and the bottom insertion electrode, successively from the batch material layer, the silicate reaction layer, and the semi-molten layer , and finally to the clarified homogenization layer.

[0024] As a further optimization of this solution, the compounding material layer includes a cold-batch material layer and a hot-batch material layer, and the temperature of the cold-batch material layer is 150-200°C.

[0025] As a further optimi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thermal efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for melting preparing of glass through a glass electric melting furnace. The melting method is conducted on the electric melting furnace. A bottom inserting electrodeis arranged at the inner bottom of the electric melting furnace, a top inserting electrode is arranged at the top, and a fluid hole is formed in the bottom of the electric melting furnace. The invention provides the method for melting preparing of the glass through the glass melting furnace, and the defects of high energy consumption, more volatile substances, environmental pollution and the likewhen melting preparing of the glass is conducted are overcome.

Description

technical field [0001] The invention relates to the field of glass manufacturing, in particular to a method for melting glass in an electric glass melting furnace. Background technique [0002] Glass production has a history of thousands of years, but mass production of glass products began in the 1940s and 1950s. In recent decades, glass technology has continued to develop, and the heat sources for melting glass have developed from coal direct fire, coal gas, coal tar, and heavy oil to electric boosting and full electric melting; glass furnaces have developed from crucible furnaces to pool furnaces, gas-electric hybrids Heating pool furnaces are electric furnaces that have been used up to now. [0003] Glass all-electric fusion technology was introduced from the West in the 1980s and replicated in China in the 1990s. After the new century, it will be fully rolled out in the country. The glass melting furnace has the following advantages: First, the thermal efficiency is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B5/027
CPCC03B5/027
Inventor 孙国刚徐惠豪潘志成
Owner 江苏宝恒新材料科技有限公司