Two-component glue for blending fluorescent powder and preparation method thereof

A fluorescent powder, two-component technology, applied in the direction of adhesives, epoxy glue, adhesive types, etc., can solve the problems that affect the luminous quality and life of LED lamps, poor UV resistance, poor adhesion, etc., to achieve Improve luminous quality and service life, good UV resistance and good adhesion

Inactive Publication Date: 2018-10-12
东莞市山水新材料科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the glue used to fix the phosphor on the LED chip has defects such as easy aging, poor adhesion and poor UV resistance, which affects the luminous quality and life of the LED lamp.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Each component and weight part of described A agent:

[0024] 45 parts of modified epoxy resins;

[0025] 43 parts of aliphatic epoxy resin;

[0026] 1.5 parts of auxiliary agent;

[0027] Each component and parts by weight of the B agent:

[0028] 97 copies of imported methylhexahydrobenzene;

[0029] Accelerator 1 part.

[0030] In this embodiment, the auxiliary agent is a defoamer.

[0031] In the embodiment of the present invention, the preparation method of the two-component fluorescent powder-adjusting glue includes the following steps:

[0032] Step S1. Weigh each component of the agent A according to parts by weight, mix and stir the weighed modified epoxy resin and aliphatic epoxy resin evenly, add and weigh according to parts by weight during the stirring process Additives to eliminate foam generated during stirring;

[0033] Step S2, weighing each component of the agent B according to parts by weight, and mixing and stirring the weighed components even...

Embodiment 2

[0038] Each component and weight part of described A agent:

[0039] 50 parts of modified epoxy resins;

[0040] 48 parts of aliphatic epoxy resin;

[0041] 2 parts of auxiliary agent;

[0042] Each component and parts by weight of the B agent:

[0043] 98 parts of imported methylhexahydrobenzene;

[0044] Accelerator 2 parts.

[0045] In this embodiment, the auxiliary agent is a defoamer.

[0046] In the embodiment of the present invention, the preparation method of the two-component phosphor-adjusting glue is the same as or similar to the steps in embodiment 1. The only difference between it and embodiment 1 is the curing process in step S4. In this embodiment In the example, the curing process is as follows: the curing temperature is 120° C., and the curing time is 60 minutes.

Embodiment 3

[0048] Each component and weight part of described A agent:

[0049] 55 parts of modified epoxy resins;

[0050] 52 parts of aliphatic epoxy resin;

[0051] 3 parts of defoamer;

[0052] Each component and parts by weight of the B agent:

[0053] 99 parts of imported methylhexahydrobenzene;

[0054] Accelerator 3 parts.

[0055] In the embodiment of the present invention, the preparation method of the two-component phosphor-adjusting glue is the same as or similar to the steps in embodiment 1. The only difference between it and embodiment 1 is the curing process in step S4. In this embodiment In the example, the curing process is as follows: the curing temperature is 130° C., and the curing time is 45 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses two-component glue for blending fluorescent powder. The glue is composed of an agent A and an agent B, wherein the weight ratio of the agent A to the agent B is 1:1; the agentA is composed of the following components in parts by weight: 45-55 parts of modified epoxy resin, 43-52 parts of aliphatic epoxy resin and 1.5-3 parts of an assistant; and the agent B is composed ofthe following components in parts by weight: 97-99 parts of imported methylhexahydrophthalic anhydride and 1-3 parts of an accelerant. The two-component glue for blending fluorescent powder provided by the invention has the advantages of good adhesive strength, aging resistance, light degradation resistance, good ultraviolet resistance and the like. When applied to LED light fittings, the two-component glue for blending fluorescent powder can effectively improve the luminous quality and service life of the LED light fittings.

Description

technical field [0001] The invention relates to a glue, in particular to a two-component fluorescent powder-adjusting glue and a preparation method thereof. Background technique [0002] There are three main methods for LED lamps to use phosphor powder to achieve white light: 1. Coating yellow phosphor powder that can be excited by blue light on the blue LED chip, the blue light emitted by the chip and the yellow light emitted by the phosphor complement each other to form white light; 2. Coat green and red phosphors on the blue LED chip, and combine the blue light emitted by the chip with the green light and red light emitted by the phosphor to obtain white light; 3. Coat three primary colors or multiple colors on the purple or ultraviolet LED chip The fluorescent powder of different colors uses long-wave ultraviolet light (370nm-380nm) or purple light (380nm-410nm) emitted by the chip to excite the fluorescent powder to achieve white light emission. [0003] At present, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00H01L33/50
CPCC08L2201/08C08L2205/025C09J163/00H01L33/501C08L63/00
Inventor 邓辉陶满平
Owner 东莞市山水新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap