Raw liquid coloring heavy oxford fabric and production method thereof

A technology for dope dyeing and production methods, applied in textiles, textiles and papermaking, improved hand-feeling fibers, etc., can solve problems such as lack of unevenness and thick feeling, troubles in dyeing and finishing garment processing, and inability to satisfy consumers, so as to improve wearability. Comfort, meet mass production, low cost effect

Inactive Publication Date: 2018-10-19
鲁丰织染有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing heavyweight Oxford fabrics have a single style, are airtight and have a bad hand feeling, which cannot meet the needs of consumers
And the cloth surface yarn is flat, without a sense of unevenness and thickness, which affects the appearance of wearing and causes troubles for subsequent dyeing and finishing and garment processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A solution-dyed heavyweight Oxford fabric with a warp count of 40 and a weft count of 20; a warp yarn density of 90 threads / inch and a weft thread density of 60 threads / inch; Pigmented viscose blend.

[0021] The production method steps of dope dyed heavyweight Oxford spinning fabric are as follows:

[0022] The warp yarns are sized with sizing, the sizing rate is 8%, and the moisture regain rate is 8%. Then the warp yarns and weft yarns are woven in the weaving workshop. The relative humidity of the weaving workshop is 55%. It is 4.0KN ± 0.2, the injection pressure is 0.35mpa, the injection time of the main nozzle is 90-100 degrees, and the injection time of the auxiliary nozzle is 65-70 degrees.

[0023] The slurry is composed of the following raw materials in parts by weight: 70 parts of potato starch, 25 parts of acrylic acid and 5 parts of wax flakes.

[0024] The stock solution dyed heavyweight Oxford fabric obtained in Example 1 is tested: the cloth surface is ...

Embodiment 2

[0026] A solution-dyed heavyweight Oxford fabric with a warp count of 50 and a weft count of 10, a warp density of 120 threads / inch, and a weft density of 45 threads / inch. Pigmented viscose blend.

[0027] The production method steps of dope dyed heavyweight Oxford spinning fabric are as follows:

[0028] The warp yarns are sized with sizing, the sizing rate is 10%, and the moisture regain rate is 7%. Then the warp yarns and weft yarns are woven in the weaving workshop. The relative humidity of the weaving workshop is 65%. It is 4.0KN ± 0.2, the injection pressure is 0.38mpa, the injection time of the main nozzle is 90-100 degrees, and the injection time of the auxiliary nozzle is 65-70 degrees.

[0029] The slurry is composed of the following raw materials in parts by weight: 90 parts of potato starch, 28 parts of acrylic acid and 7 parts of wax flakes.

[0030] The stock solution dyed heavyweight Oxford fabric obtained in Example 2 was tested: the cloth surface is granular...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of textiles, and particularly relates to a raw liquid coloring heavy oxford fabric and a production method thereof. The number of warp is 40-50, the numberof weft is 10-20, the warp density is 90-120 / inch, the weft density is 45-60 / inch, the warp direction weaving shrinkage is 4-6%, and the weft direction weaving shrinkage is 15-18%. Compared with an existing heavy oxford fabric, the raw liquid coloring heavy oxford fabric has a unique style, fabric surface granulation is plump, the hand feeling is smooth and soft, the air permeability is good, theweft direction elastic elongation is 12-15%, and the humidity absorbing and quick drying functions are good. Investment is not needed to improve looms by means of the production method, the raw liquid coloring heavy oxford fabric can be woven on an existing Bigano air-jet loom, the cost is low, and the demand of production in large batches can be met.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a dope-dyed heavyweight Oxford fabric and a production method thereof. Background technique [0002] Existing heavyweight Oxford fabrics have a single style, are airtight and feel bad, and cannot meet the needs of consumers. In addition, the yarn on the cloth surface is flat, without a feeling of unevenness and thickness, which affects the appearance of wearing and causes troubles for subsequent dyeing and finishing and garment processing. Contents of the invention [0003] In view of the deficiencies in the prior art, the purpose of the present invention is to provide a kind of dope-colored heavyweight Oxford fabric with unique style, granular and full surface, delicate and soft hand feeling, good air permeability, elastic elongation in weft direction, moisture absorption and quick drying Good; the present invention also provides its production method, which has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D13/00D03D15/00D06M15/11D06M13/203D06M13/02D06M101/06D06M101/32D03D15/225D03D15/283D03D15/47D03D15/54
CPCD03D13/008D06M13/02D06M13/203D06M15/11D10B2201/24D10B2331/04D10B2401/14D06M2101/06D06M2200/50D06M2200/40D06M2101/32D03D15/54D03D15/47
Inventor 张战旗齐元章宋琳张艳仲伟浩刘桂杰牛继玲
Owner 鲁丰织染有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More