Preparation method of polypropylene composition

A polypropylene composition, polypropylene technology, applied in the field of materials to achieve the effects of inhibiting thermal and oxygen degradation, wide application range, and avoiding adverse effects

Inactive Publication Date: 2018-11-02
SINOPEC YANGZI PETROCHEM +1
View PDF14 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the actual processing process, it is also necessary to comprehensively consider the influence of the pore size, pore distribution, pore structure, and desorption temperature of the odor adsorbent, which is often difficult to fully meet the needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polypropylene composition
  • Preparation method of polypropylene composition
  • Preparation method of polypropylene composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Take by weighing 50kg polypropylene powder (melt flow rate 0.2g / 10min), 25g antioxidant 1010, 50g antioxidant 168, 25g halogen absorbent calcium stearate, 500 grams of medical stone (2500 orders of particle size), 500 grams of zinc ricinoleate and 5 kg of talcum powder, after being fully mixed by stirring, are added to a twin-screw extruder with a length-to-diameter ratio L / D of 48: 1, the feeding speed is 50 g / min, and the screw speed is 100 rpm The supercritical carbon dioxide fluid is added to the extruder from the second heating zone of the twin-screw extruder, the quality of the supercritical carbon dioxide fluid is 20% of the polypropylene mass, and the addition speed is 10g / min. The twin-screw extruder is divided into 10 heating zones, the temperature of the first heating zone is 180°C, and the temperature of the other heating zones is 160°C-220°C. Vacuum devolatilize in the 8th area, extrude the granulated material strips to obtain the product through water-cool...

Embodiment 2

[0050] Take by weighing 50kg polypropylene powder (melt flow rate 0.5g / 10min), 50g antioxidant 1010, 100g antioxidant 168, 25g halogen absorbent calcium stearate, 1500 grams of medical stone (2500 orders of particle size), 250 grams of zinc ricinoleate and 7.5 kg of talcum powder, after being fully mixed by stirring, are added to a twin-screw extruder whose length-to-diameter ratio L / D is 48: 1, and the feeding speed is 50 g / min, and the screw speed is 100 rpm. points; supercritical carbon dioxide fluid is added to the extruder from the second heating zone of the twin-screw extruder, the quality of the supercritical carbon dioxide fluid is 10% of the polypropylene mass, and the addition speed is 5g / min. The twin-screw extruder is divided into 10 heating zones, the temperature of the first heating zone is 180°C, and the temperature of the other heating zones is 160°C-220°C. In the 8th heating zone, the product is vacuumized and devolatilized, extruded and granulated, and then w...

Embodiment 3

[0052] Take by weighing 50kg polypropylene powder (melt flow rate 2.5g / 10min), 75g antioxidant 1076, 100g antioxidant 168, 50g halogen absorbent calcium stearate, 2500 grams of medical stone (2500 orders of particle size), 350 grams of zinc ricinoleate and 10 kg of talcum powder, after being fully mixed by stirring, are added to a twin-screw extruder with a length-to-diameter ratio L / D of 48:1, the feeding speed is 50 g / min, and the screw speed is 100 rpm The supercritical carbon dioxide fluid is added to the extruder from the second heating zone of the twin-screw extruder, the quality of the supercritical carbon dioxide fluid is 30% of the polypropylene mass, and the addition speed is 15g / min. The twin-screw extruder is divided into 10 heating zones, the temperature of the first heating zone is 180°C, and the temperature of the other heating zones is 160°C-220°C. In the 8th heating zone, the product is vacuumized and devolatilized, extruded and granulated, and then water-cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a polypropylene composition and belongs to the technical field of materials. The composition at least comprises 100 parts of polypropylene, 0.05-0.15 part of a primary antioxidant, 0.1-0.3 parts of an auxiliary antioxidant and 0.05-0.2 parts of a halogen absorbent. Supercritical carbon dioxide is used for assisting in extrusion; heat and oxygen degradation of polypropylene is effectively inhibited in an extrusion process; at the same time, dissolution of micromolecular volatile matters is greatly accelerated; and the micromolecular volatile matters are removed in a pressure release extraction manner in front of a neck mold of an extruder. The method is simple in technology, wide in application scope and low in production cost.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a preparation method of a low-odor propylene polymer composition. Background technique [0002] Polypropylene (PP) is a polymer compound obtained by polymerizing propylene. Due to its rich raw materials and relatively simple synthesis process, compared with other general-purpose thermoplastics, PP has low relative density, low price, and outstanding stress resistance, cracking and wear resistance, and is the fastest growing among general-purpose thermoplastics. Varieties, increasingly important in economic construction and people's lives, have become the fastest growing varieties of plastics, and are widely used in various fields such as automobiles, home appliances, daily necessities, and packaging. However, polypropylene itself and various additives usually bring in a large odor, which limits its application in some fields, and with the development of the nationa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/10C08K13/02C08K5/134C08K5/526C08K5/098C08K3/34C08K5/3492C08K5/527C08K13/04C08K7/26B29B9/06B29C47/92B29C48/92
CPCB29B9/06C08K3/34C08K5/098C08K5/1345C08K5/34924C08K5/526C08K5/527C08K7/26C08K13/02C08K13/04C08K2201/003C08K2201/014C08L23/10Y02P20/54
Inventor 左胜武袁小亮邱敦瑞王晶徐振明傅勇
Owner SINOPEC YANGZI PETROCHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com