Formula of anticorrosive material for novel multi-purpose tower for urban use

An anti-corrosion material and multi-functional technology, applied in anti-corrosion coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of high cost of underground wiring and difficult maintenance, and achieve the improvement of urban greening effect and good waterproof and anti-corrosion function. Effect

Inactive Publication Date: 2018-11-06
HEFEI HAIYIN TOWER
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among them, with the development of cities, power poles and towers are rarely seen in urban areas or densely populated areas. Most of them use und

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The formula of a new type of multifunctional anti-corrosion material for urban poles and towers according to the present invention is made of the following raw materials in parts by weight: 20-30 parts of epoxy resin, 20-30 parts of polyester resin, 10-12 parts of titanium dioxide, sulfuric acid 6-10 parts of barium, 2-3 parts of zinc oxide, 4-6 parts of leveling agent, 0.2-0.8 parts of carbon black, 10-15 parts of adhesive, 0.1-0.3 parts of foaming agent, 2-3 parts of penetrating agent , 4-8 parts of curing agent, 3.5-4.8 parts of iron red.

Embodiment 2

[0016] A kind of anticorrosion material formula for new multifunctional pole and tower used in cities according to the present invention is made of the following raw materials in parts by weight: 25 parts of epoxy resin, 25 parts of polyester resin, 11 parts of titanium dioxide, 8 parts of barium sulfate, zinc oxide 2.3 parts, 5 parts of leveling agent, 0.6 parts of carbon black, 12.8 parts of adhesive, 0.19 parts of foaming agent, 2.4 parts of penetrating agent, 5 parts of curing agent, 4.2 parts of iron red.

Embodiment 3

[0018] The formula of a new type of multifunctional anti-corrosion material for urban poles and towers according to the present invention is made of the following raw materials in parts by weight: 20-30 parts of epoxy resin, 20-30 parts of polyester resin, 10-12 parts of titanium dioxide, sulfuric acid 6-10 parts of barium, 2-3 parts of zinc oxide, 4-6 parts of leveling agent, 0.2-0.8 parts of carbon black, 10-15 parts of adhesive, 0.1-0.3 parts of foaming agent, 2-3 parts of penetrating agent , 4-8 parts of curing agent, 3.5-4.8 parts of iron red, 4-10 parts of polyamide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of spraying plastic materials for towers and particularly relates to a formula of an anticorrosive material for a novel multi-purpose tower for urban use.The anticorrosive material is prepared from 20-30 parts by weight of epoxy resin, 20-30 parts by weight of polyester resin, 10-12 parts by weight of titanium dioxide, 6-10 parts by weight of barium sulfate, 2-3 parts by weight of zinc oxide, 4-6 parts by weight of a leveling agent, 0.2-0.8 parts by weight of carbon black, 10-15 parts by weight of a binder, 0.1-0.3 parts by weight of a foaming agent, 2-3 parts by weight of a penetrating agent, 4-8 parts by weight of a curing agent and 3.5-4.8 parts by weight of iron oxide red. The anticorrosive material solves the problems of the existing anticorrosive material, has good waterproof and anti-corrosion functions, and contains a large number of small pores due to a small amount of a foaming agent. The small pores are convenient for water storage and retard the water loss so that some green plants are easily planted in the anti-corrosion spraying plastic layer and thus the urban greening effect is improved.

Description

technical field [0001] The invention relates to the technical field of plastic-sprayed materials for poles and towers, and specifically belongs to a formula of novel multifunctional antiseptic materials for urban poles and towers. Background technique [0002] The pole tower is one of the basic equipment in the overhead power distribution line. According to the materials used, it can be divided into three types: wooden poles, cement poles and metal poles. Cement rods have the advantages of long service life and small maintenance workload, and are widely used. The most used cement rod is the tip rod, the taper is generally 1 / 75, which is divided into ordinary reinforced concrete rods and prestressed reinforced concrete rods. [0003] Among them, with the development of cities, power poles and towers are rarely seen in urban areas or densely populated areas. Most of them use underground wiring, but the cost of underground wiring is high and maintenance is difficult. Therefore...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D167/00C09D5/08C09D7/61
CPCC08K2003/2241C08K2003/2272C08K2003/2296C08K2003/3045C09D5/08C09D7/61C09D163/00C09D167/00C08L67/00C08K13/02C08K3/22C08K3/30C08K3/04C08L63/00
Inventor 李光海赵宏伟
Owner HEFEI HAIYIN TOWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap