Preparation method of water-repellent polyester/cotton brushed fabric

A water-repellent and polyester-cotton technology, which is applied to fabric surface trimming, textile material treatment, plant fibers, etc., can solve the problems of affecting the fabric's aesthetics, poor waterproof performance, and short service life, and achieve a strong water-repellent effect , short fluffing time and prolonging the service life

Active Publication Date: 2018-11-20
石狮市展耀纺织科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

More and more people prefer multifunctional and aesthetically pleasing textiles, but common raised fabrics have poor waterproof performance, and tend to ball up after fluffing, which affects the aesthetics of the fabric and has a short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-repellent polyester/cotton brushed fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The preparation method of water-repellent polyester-cotton sanded fabric includes the following steps:

[0046] Step 1. Weaving grey cloth:

[0047] The polyester-cotton blended yarn is woven to obtain a polyester-cotton fabric, wherein the polyester-cotton blended yarn includes 65% polyester yarn and 35% cotton yarn in terms of mass percentage.

[0048] Step two, cold reactor:

[0049] The polyester-cotton fabric obtained in step 1 is cold piled to obtain cold pile grey fabrics. The cold pile temperature is 30°C, and the cold pile time is 10 hours. The cold pile additives include the following components in terms of water volume: methacrylic acid shrinkage Glycerides 4g / L, caprylic acid capric acid polyethylene glycol glycerides 2g / L, acetic acid 2g / L.

[0050] Step three, rinse:

[0051] The cold pile fabric obtained in step 2 is rinsed to obtain a rinsing cloth; in the rinsing process, the rinsing temperature is 50° C., the rinsing time is 1 hour, and clean water is used for r...

Embodiment 2

[0068] The preparation method of water-repellent polyester-cotton sanded fabric includes the following steps:

[0069] Step 1. Weaving grey cloth:

[0070] The polyester-cotton blended yarn is woven to obtain a polyester-cotton fabric. The polyester-cotton blended yarn includes 70% polyester yarn and 30% cotton yarn in terms of mass percentage.

[0071] Step two, cold reactor:

[0072] The polyester-cotton fabric obtained in step 1 is cold piled to obtain cold pile grey fabrics. The cold pile temperature is 33°C and the cold pile time is 11 hours. The cold pile additives include the following components in terms of water volume: methacrylic acid shrinkage Glycerides 5g / L, caprylic acid capric acid polyethylene glycol glycerides 3g / L, acetic acid 3g / L.

[0073] Step three, rinse:

[0074] The cold pile fabric obtained in step 2 is rinsed to obtain a rinse cloth; in the rinsing process, the rinsing temperature is 60° C., the rinsing time is 2 hours, and clean water is used for rinsing. Th...

Embodiment 3

[0091] The preparation method of water-repellent polyester-cotton sanded fabric includes the following steps:

[0092] Step 1. Weaving grey cloth:

[0093] The polyester-cotton blended yarn is woven to obtain a polyester-cotton fabric. The polyester-cotton blended yarn includes 70% polyester yarn and 30% cotton yarn in terms of mass percentage.

[0094] Step two, cold reactor:

[0095] The polyester-cotton fabric obtained in step 1 is cold piled to obtain cold pile grey fabrics. The cold pile temperature is 35°C and the cold pile time is 12 hours. The cold pile additives include the following components in terms of water volume: methacrylic acid shrinkage Glyceride 7g / L, caprylic acid capric acid polyethylene glycol glyceride 3g / L, acetic acid 3g / L.

[0096] Step three, rinse:

[0097] The cold pile fabric obtained in step 2 is rinsed to obtain a rinse cloth; during the rinsing process, the rinsing temperature is 65° C., the rinsing time is 2 hours, and clean water is used for rinsing. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Air permeabilityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of water-repellent polyester / cotton brushed fabric, and belongs to the field of fabric. The preparation method of the water-repellent polyester / cotton brushed fabric comprises steps of grey cloth weaving, cold-batch, rinsing, carbon grinding, back boiling, dyeing, soaping, water repellent treatment, softening treatment, primary drying and secondary drying. The prepared water-repellent polyester / cotton brushed fabric has the advantages of high fiber strength, excellent waterproof performance, high color fastness and long service life.

Description

Technical field [0001] The invention belongs to the technical field of fabrics, and specifically relates to a preparation method of water-repellent polyester-cotton sanded fabric. Background technique [0002] In recent years, science and technology are being updated faster and faster, people’s living standards are getting higher and higher, people in modern society are increasingly pursuing fashion, especially after 00s, in the modern Internet environment, they are pursuing personality Supplies have relatively high pursuit. More and more people like textiles with multi-performance and aesthetics. Common raised fabrics have poor waterproof performance and tend to become spherical after being raised, which affects the aesthetics of the fabric and has a short service life. [0003] Therefore, there is a need for a polyester-cotton sanded fabric with simple preparation process, good water resistance, good raising effect, high fiber strength, strong color fastness, and fluorine conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/188D06M13/224D06M13/292D06M13/513D06M15/17D06M15/333D06M15/53D06M15/643D02G3/04D06B3/10D06B3/18D06B15/00D06B17/02D06C11/00D06M101/06D06M101/32
CPCD02G3/04D06B3/10D06B3/18D06B15/00D06B17/02D06C11/00D06M13/188D06M13/2246D06M13/292D06M13/513D06M13/5135D06M15/17D06M15/333D06M15/53D06M15/643D06M2101/06D06M2101/32D06M2200/12D10B2201/02D10B2331/04
Inventor 白莉王义栋任晓晖
Owner 石狮市展耀纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com