Production process of fluorocarbon thermal insulation decorative integrated board
A production process and integrated board technology, which can be used in devices for coating liquids on surfaces, pretreatment surfaces, coatings, etc., which can solve the problems of reducing the quality of finished products, easy generation of air bubbles, color difference, etc., and achieve the effect of ensuring quality stability.
Inactive Publication Date: 2018-11-23
苏州普莱特环保新材料有限公司
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] Existing boards will also be coated with fluorocarbon coatings on the surface to improve the durability of the boards in actual use, but the existing coating process is prone to various production process problems such as air bubbles and color difference, which greatly reduces the quality of the finished product. quality
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0056] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with specific embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.
[0057] A production process of fluorocarbon thermal insulation and decoration integrated board, the production process steps of fluorocarbon thermal insulation and decoration integrated board are as follows:
[0058] Step 1: base material inspection, length and width detection: about 10 centimeters from both ends of the rough board, and the midline position, measure one place with a steel tape, accurate to 1 mm, take the average of these three measured values as Board length (width) value;
[0059] Thickness detection: use external calipers and vernier calipers to measure, 10 cm away from both sides of the board and...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a production process of a fluorocarbon thermal insulation decorative integrated board. The production process of the fluorocarbon thermal insulation decorative integrated boardcomprises the steps of first step, substrate inspection and length and width detection, wherein measuring is conducted on positions about 10 cm from both ends of a rough board and a midline positionrespectively with a steel tape, accurate to 1 mm, and the average of three measured values is taken as the length (width) of a board surface; thickness detection, wherein external calipers and verniercalipers cooperate to measure, 10 cm from both sides and both ends of the board, one value is measured at each intersection point, a total of 4 values are measured, 10 cm from both sides of the board, 1 value at an intersection point of a transverse center line is measured, there are two intersection points, and a total of 6 values are measured, accurate to 1 millimeter. The production process can effectively paint fluorocarbon thermal insulation decoration to ensure the quality stability of a coating surface of a panel.
Description
technical field [0001] The invention relates to the technical field of production of fluorocarbon thermal insulation and decorative panels, in particular to a production process of a fluorocarbon thermal insulation and decorative integrated panel. Background technique [0002] Fluorocarbon coatings refer to coatings with fluororesin as the main film-forming substance, also known as fluorocarbon coatings, fluorine coatings, fluororesin coatings, etc. Among various coatings, fluororesin coatings have high electronegativity due to the introduction of fluorine elements. The carbon-fluorine bond is strong, and has particularly superior properties, such as fire resistance, heat resistance, low temperature resistance, chemical resistance, and has unique non-stick and low friction properties. [0003] Existing boards will also be coated with fluorocarbon coatings on the surface to improve the durability of the boards in actual use, but the existing coating process is prone to variou...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/24B05D7/00B05D5/00B05D3/00B05D3/02
CPCB05D3/002B05D3/007B05D3/0254B05D5/00B05D7/24B05D7/584
Inventor 李炳兴
Owner 苏州普莱特环保新材料有限公司