Foaming inkjet material and preparation method thereof

A technology of inkjet materials and raw materials, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems that PVC materials are not environmentally friendly, reduce the positive code rate of finished products, and high manufacturing costs, and achieve brilliant printing images, simple processing, three-dimensional strong effect

Active Publication Date: 2018-12-07
HUIZHOU YIDU IMAGE TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] PVC foam wallpaper mainly uses high-molecular polyvinyl chloride paste resin as the main raw material, adding plasticizers, foaming agents, flame retardants, viscosity reducers, fillers and other auxiliary materials for foam molding. PVC materials are not environmentally friendly. Use will age and produce harmful substances
Another type of coated wallpaper needs to be coated multiple times to achieve the embossed thickness. The process is cumbersome, which reduces the code rate of the finished product, consumes a lot of materials, and high manufacturing costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foaming inkjet material and preparation method thereof
  • Foaming inkjet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Foaming inkjet material, its raw material is: 25 parts of acrylic emulsions, 15 parts of polyurethane emulsions, 16 parts of polyvinyl alcohol glue (prepared by 12 parts of deionized water and 4 parts of PVA micelle), 5 parts of matte powder, 10 parts of 1 part sodium lauryl sulfate, 3 parts coconut oil fatty acid diethanolamide, 1 part aziridine, 25 parts deionized water.

[0029] Prepare as follows:

[0030] 1. Prepare polyvinyl alcohol glue: pre-weigh PVA colloids and deionized water, add deionized water to the mixing pot, turn on the mixer, slowly add PVA colloids, stirring speed 900r / min, after stirring for 20min, turn on the heating mode, Set the temperature to 80°C. When the temperature rises to 80°C, keep it warm for 1 hour, then change the interlayer water to cooling water, and when it cools to 50°C, filter it into a small bucket with a 300-mesh filter, seal it and let it stand for 24 hours before use;

[0031] 2. Preparation of basic coating glue: Weigh each ...

Embodiment 2

[0034] Foam inkjet material, its raw material is: 21 parts of acrylic emulsions, 12 parts of polyurethane emulsions, 16 parts of polyvinyl alcohol glue (prepared by 13 parts of deionized water and 3 parts of PVA colloids), 4 parts of matte powder, 10 parts of 1 part sodium lauryl sulfate, 4 parts coconut oil fatty acid diethanolamide, 1 part aziridine, 30 parts deionized water.

[0035] Prepare as follows:

[0036] 1. Prepare polyvinyl alcohol glue: pre-weigh PVA granules and deionized water, add deionized water to the mixing pot, turn on the mixer, slowly add PVA granules, stirring speed 900r / min, after stirring for 15min, turn on the heating mode, Set the temperature to 80°C. When the temperature rises to 80°C, keep it warm for 0.5h, then change the interlayer water to cooling water, and when it cools to 50°C, filter it into a small bucket with a 300-mesh filter, seal it and let it stand for 24 hours before use;

[0037] 2. Preparation of basic coating glue: Weigh each comp...

Embodiment 3

[0040] Foaming inkjet material, its raw material is: 30 parts of acrylic emulsion, 18 parts of polyurethane emulsion, 20 parts of polyvinyl alcohol glue (prepared by 15 parts of deionized water and 5 parts of PVA micelle), 8 parts of matte powder, 6 parts of Part sodium lauryl sulfate, 5 parts coconut oil fatty acid diethanolamide, 2 parts aziridine, 20 parts deionized water.

[0041] Prepare as follows:

[0042]1. Prepare polyvinyl alcohol glue: pre-weigh PVA colloids and deionized water, add deionized water to the mixing pot, turn on the mixer, slowly add PVA colloids, stirring speed 900r / min, after stirring for 30min, turn on the heating mode, Set the temperature to 80°C. When the temperature rises to 80°C, keep it warm for 1 hour, then change the interlayer water to cooling water, and when it cools to 50°C, filter it into a small bucket with a 300-mesh filter, seal it and let it stand for 24 hours before use;

[0043] 2. Prepare basic coating glue: weigh each component ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
particle diameteraaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of wall decoration materials and discloses a foaming inkjet material. The foaming inkjet material is prepared from 20-30 parts by weight of an acrylic emulsion, 10-20 parts by weight of a polyurethane emulsion, 10-20 parts by weight of polyvinyl alcohol glue, 3-8 parts by weight of matte powder, 5-12 parts by weight of sodium lauryl sulfate, 2-5 parts by weight of coconut fatty acid diethanolamide, 0.5-2 parts by weight of aziridine and 20-30 parts by weight of deionized water. The invention also discloses a preparation method of the foaming inkjetmaterial. The preparation method comprises: preparing polyvinyl alcohol glue, preparing base coating glue and preparing foaming inkjet glue. The foaming inkjet material has the advantages of environmental protection, wide application range, bright printing color and fast coating ink absorption speed.

Description

technical field [0001] The invention belongs to the technical field of wall surface decoration materials, in particular to a foaming inkjet material and a preparation method thereof. Background technique [0002] Wallpaper is also called wallpaper, which has the characteristics of rich colors, various patterns, safety and environmental protection, convenient construction, easy cleaning, surface water resistance, fire prevention and mildew resistance in interior decoration, and is widely used in residences, offices, hotels, coffee shops, specialty stores interior decoration. The wallpaper used in China is mainly PVC wallpaper, which is laminated with foamed or micro-foamed PVC layers on the surface and then embossed, which has a strong sense of concave and convex textures. The PVC layer is waterproof and can be washed directly with cloth, and the product price is cheap. Another kind of coated wallpaper, by repeatedly coating the ink-absorbing coating on the base material, af...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D175/04C09D129/04C09D7/42
CPCC08L2205/03C09D7/42C09D133/04C08L75/04C08L29/04
Inventor 罗晓琪卢家荣
Owner HUIZHOU YIDU IMAGE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com