Silicon-modified inorganic slurry fireproof heat insulation plate with Class A permeability and preparation method thereof

A fire-proof insulation board and permeability technology, applied in the field of building insulation board, can solve the problems of uneven penetration of inorganic materials, high wire coefficient and high water absorption rate, and achieve the effects of short curing period, high strength and moderate porosity

Inactive Publication Date: 2018-12-11
CHENGDU FIRST NEW MATERIAL CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a silicon-modified inorganic slurry permeability grade A fire insulation board to solve the problems of low strength, high conduction coefficient, high water absorption, uneven penetration of inorganic materials and construction problems of current A grade fire insulation boards. Another object of the present invention is to provide a method for preparing a silicon-modified inorganic slurry permeability Class A fireproof insulation board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 7 parts of low-density polystyrene foam insulation board, 65 parts of ordinary Portland cement, 1.5 parts of silicone water repellent, 1.5 parts of cement composite early strength agent, 5 parts of fly ash, 16 parts of water, ethylene-vinyl acetate 4 parts of copolymerized emulsion. Weigh the above-mentioned raw materials in corresponding parts by weight, add water, ordinary Portland cement, silicone water repellent, cement composite early strength agent, fly ash, and silicon-modified acrylic emulsion into the high-speed multifunctional mixer in sequence. Mix evenly under the conditions of 500r / min and 20-40°C to form a homogeneous slurry; place the low-density polystyrene foam insulation board on the conveyor belt of the plate permeator, and place it on the low-density polystyrene foam insulation board Pour homogeneous slurry on the upper surface of the low-density polystyrene foam insulation board for vacuum adsorption, the vacuum degree of vacuum adsorption is 0.2MPa...

Embodiment 2

[0023] 8 parts of low-density polystyrene foam insulation board, 68 parts of ordinary Portland cement, 1.5 parts of silicone water repellent, 1.5 parts of cement composite early strength agent, 5 parts of fly ash, 11 parts of water, ethylene-vinyl acetate 5 parts of copolymerized emulsion.

[0024] Weigh the above-mentioned raw materials in corresponding parts by weight, add water, ordinary Portland cement, silicone water repellent, cement composite early strength agent, fly ash, and silicon-modified acrylic emulsion into the high-speed multifunctional mixer in sequence. Mix evenly under the conditions of 800r / min and 30°C to form a homogeneous slurry; place the low-density polystyrene foam insulation board on the conveyor belt of the board permeator, and place it on the low-density polystyrene foam insulation board. Pour the homogeneous slurry on the surface, and carry out vacuum adsorption on the lower surface of the low-density polystyrene foam insulation board. The vacuum ...

Embodiment 3

[0027] 9 parts of low-density polystyrene foam insulation board, 70 parts of ordinary Portland cement, 1.5 parts of silicone water repellent, 1.5 parts of cement composite early strength agent, 5 parts of fly ash, 8 parts of water, ethylene-vinyl acetate 5 parts of copolymerized emulsion.

[0028] Weigh the above-mentioned raw materials in corresponding parts by weight, add water, ordinary Portland cement, silicone water repellent, cement composite early strength agent, fly ash, and silicon-modified acrylic emulsion into the high-speed multifunctional mixer in sequence. Mix evenly under the conditions of 1000r / min and 40°C to form a homogeneous slurry; place the low-density polystyrene foam insulation board on the conveyor belt of the board permeator, and place it on the low-density polystyrene foam insulation board. Pour the homogeneous slurry on the surface, and carry out vacuum adsorption on the lower surface of the low-density polystyrene foam insulation board. The vacuum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a silicon-modified inorganic slurry fireproof heat insulation plate with Class A permeability and a preparation method thereof, and relates to the technical field of building heat insulation plates. The heat insulation plate is mainly prepared from the following raw materials in parts by weight: 5 to 10 parts of low density polystyrene foam heat insulation plate, 50 to 70 parts of common silicate cement, 0.5 to 2 parts of organosilicone water repellent, 2 to 5 parts of cement composite early strength agent, 3 to 6 parts of fly ash, 10 to 20 parts of water, and 5 to 10 parts of vinyl-acetate vinyl copolymerizing emulsion. The heat insulation plate with Class A permeability has the characteristics that the heat-insulation property, fireproof property and the like areexcellent; the compressive strength is high, the heat conduction efficient is low, the hydrophobic effect is good, the curing cycle is shorter, the production efficiency is high, and the fireproof property is high.

Description

technical field [0001] The invention relates to the technical field of building thermal insulation boards, in particular to a silicon-modified inorganic slurry permeability grade A fireproof thermal insulation board and a preparation method thereof. Background technique [0002] Insulation board is a kind of building energy-saving material. Its own thermal insulation performance can effectively reduce the energy consumption of buildings, which is in line with the development direction of national green and energy-saving buildings. At present, the fire protection rating of insulation boards commonly used in the construction field is B1 or lower. Its energy-saving effect is remarkable, but its fire resistance performance is poor. In actual use, there have been many fire incidents, causing heavy losses. Therefore, new buildings are increasingly favoring insulation materials with a fire rating of A. However, common A-grade thermal insulation materials on the market, such as roc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/28
CPCC04B28/04C04B2111/28C04B2201/20C04B2201/32C04B2201/50C04B24/2676C04B24/40C04B2103/14C04B18/08C04B24/26
Inventor 青林高如玉
Owner CHENGDU FIRST NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap