Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for preparing sterilizing and sleep promoting silk floss from mulberry silk byproduct

A technology to promote sleep and by-products, applied in the biochemical treatment of enzymes/microbes, animal raw materials, animal fibers, etc., can solve problems such as failure to achieve results, achieve the effects of reducing odor, improving degumming and refining efficiency, and increasing mechanical strength

Inactive Publication Date: 2018-12-18
罗永恒
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some people rely on supplements to promote sleep, but they also fail to achieve results

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing sterilizing and sleep promoting silk floss from mulberry silk byproduct
  • Method for preparing sterilizing and sleep promoting silk floss from mulberry silk byproduct
  • Method for preparing sterilizing and sleep promoting silk floss from mulberry silk byproduct

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Preparation of strain suspension: 25 parts of Candida, 18.5 parts of Bacillus, 18 parts of Lactic Acid Bacteria, 17 parts of Mucor, 12 parts of Thiobacillus denitrifica, and 10 parts of Alcaligenes were used as starting strains. It conducts mutagenesis, the energy of mutagenesis is set to 30kev, and the dose of mutagenesis is 4×10 15 ion / cm 2 After the treatment, the mutagenized strains were obtained, and 190 parts of normal saline was added to the mutagenized strains to prepare a strain suspension;

[0032] Preparation of immobilized strains: Mix 9 parts of polyvinyl alcohol and 1.8 parts of sodium alginate, heat in a water bath at 80°C, and keep stirring to prevent cohesion. After the mixture is completely dissolved, add in a mass ratio of 1:1 : 1 corn cob, wheat straw, pine chips as raw materials prepared 6 parts of biochar, 5.5 parts of diatomaceous earth, stirred and mixed evenly, cooled to 30 ° C, then added 3.2 parts of the prepared strain suspension, stirred an...

Embodiment 2

[0039] Preparation of strain suspension: 20 parts of Candida, 19.5 parts of Bacillus, 15 parts of Lactobacillus, 16 parts of Mucor, 11.5 parts of Thiobacillus denitrifica, and 12 parts of Alcaligenes were used as the starting strains, and ion beam was used to It conducts mutagenesis, the energy of mutagenesis is set to 30kev, and the dose of mutagenesis is 4×10 15 ion / cm 2 After the treatment, the mutagenized strains are obtained, and 200 parts of normal saline are added to the mutagenized strains to prepare a strain suspension;

[0040] Preparation of immobilized strains: Mix 11 parts of polyvinyl alcohol and 1.5 parts of sodium alginate, heat in a water bath at 80°C, and keep stirring to prevent cohesion. After the mixture is completely dissolved, add in a mass ratio of 1:1 : 1 corncob, wheat straw, pine debris prepared as raw materials, 8 parts of biochar, 5 parts of diatomaceous earth, stir and mix evenly, then cool to 30 ° C, then add 3.5 parts of the prepared strain sus...

Embodiment 3

[0047] Preparation of strain suspension: 22 parts of Candida, 18 parts of Bacillus, 16 parts of Lactic Acid Bacteria, 15 parts of Mucor, 10 parts of Thiobacillus denitrifica, and 11 parts of Alcaligenes were used as starting strains. It conducts mutagenesis, the energy of mutagenesis is set to 30kev, and the dose of mutagenesis is 4×10 15 ion / cm 2 After the treatment, the mutagenized strains were obtained, and 180 parts of normal saline was added to the mutagenized strains to prepare a strain suspension;

[0048] Preparation of immobilized strains: Mix 10 parts of polyvinyl alcohol and 1 part of sodium alginate, heat in a water bath at 80°C, and keep stirring to prevent cohesion. After the mixture is completely dissolved, add in a mass ratio of 1:1 : 7 parts of biochar prepared from 1 corncob, wheat straw, and pine chips, and 6 parts of diatomaceous earth were stirred and mixed evenly, then cooled to 30°C, and then 3.8 parts of the prepared strain suspension were added, stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of silk processing and specifically relates to a method for preparing sterilizing and sleep promoting silk floss from a mulberry silk byproduct. The methodcomprises the steps: (1) adding a mulberry silk byproduct, water and immobilized bacteria into a corruption vat to be fermented, sending electric field into in a fermentation process and filtering and dewatering after fermentation; (2) taking hydrogen peroxide, percarbonyl amine and alkaline ion liquid, adding water to be prepared into a water solution, adjusting a pH value, putting the fermentedmulberry silk byproduct into the water solution to be soaked under the normal temperature according to a bath ratio of 1 to (20 to 30), heating and degumming; (3) adding hydrogen peroxide, EDTA and oxalic acid into water to obtain a mixed solution, then putting the degummed mulberry silk byproduct into the mixed solution to be soaked and bleached; (4) utilizing clean water to wash the bleached mulberry silk byproduct to obtain thick silk floss and finally, treating the thick silk floss by an expanding agent, a softening agent, a tourmaline sol solution, nano medical stone water suspension andtraditional Chinese herbal medicine liquid to obtain the sterilizing and sleep promoting silk floss.

Description

technical field [0001] The invention belongs to the technical field of silk processing, and in particular relates to a method for preparing silk floss with sterilizing and sleep-promoting properties by using mulberry silk by-products. Background technique [0002] With the rapid development of social economy, the acceleration of work rhythm and the increase of work pressure, there are more and more sub-healthy people. Unhealthy emotions such as anxiety and depression have seriously affected people's sleep quality. Some people rely on supplements to promote sleep, but they also fail to achieve results. [0003] People need to sleep most of the time to eliminate fatigue, improve the body's resistance, restore energy, etc. Sleep can effectively promote health. Bedding accompanies people to sleep and stays in contact with the human body for a long time. Good bedding can promote people's sleep. Along with improving day by day of people's living standard, more and more consumers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01C3/00D01C3/02D06M16/00D06M15/333D06M15/13D06M101/10
CPCD01C3/00D01C3/02D06M15/13D06M15/333D06M16/00D06M16/003D06M2101/10
Inventor 罗永恒
Owner 罗永恒
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com