Technology and device for preparing plastic barrel through reprocessed plastics

A technology of recycled plastics and plastic barrels, which is applied in the field of plastic products, can solve the problems of reduced impact resistance and toughness of plastics, and low utilization value of waste plastics, and achieve the effects of low requirements, good economic benefits, and long service life

Pending Publication Date: 2018-12-21
常州群达环保科技股份有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the service life, service conditions (sun exposure) and acid and alkali corrosion of waste plastics, the impact strength and toughness of the plastics are reduced, so that the use value of waste plastics is not high; how to make waste plastics into plastic pallets Material is a technical problem for technicians to consider and solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology and device for preparing plastic barrel through reprocessed plastics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A process for preparing plastic barrels from recycled plastics, comprising the following steps:

[0030] (1) Waste plastics are washed and dried with water, cut into strips, cleaned by ultrasonic filtration in an ultrasonic machine with ethanol, acetone and deionized water in sequence, and then washed twice with 120# gasoline and deionized water in sequence, and dried to Moisture is lower than 1wt%, and clean waste plastic strips are obtained;

[0031] (2) Melt modification: put clean waste plastic strips into the reactor, control the pressure at 7~13MPa, and the temperature at 350~420°C, add titanate, superfine talc powder masterbatch, flame retardant, in the catalyst , hydrogenation cracking under the condition of stirring for 30min, to obtain modified liquid plastics, the catalyst is alumina loaded cobalt; the addition amount of titanate is 4% of the quality of waste plastics and the addition amount of ultrafine talcum powder is 4% of waste plastics 8% of the mass; ...

Embodiment 2

[0035] A process for preparing plastic barrels from recycled plastics, comprising the following steps:

[0036] (1) Waste plastics are washed and dried with water, cut into strips, cleaned by ultrasonic filtration in an ultrasonic machine with ethanol, acetone and deionized water in sequence, and then washed twice with 120# gasoline and deionized water in sequence, and dried to Moisture is lower than 1wt%, and clean waste plastic strips are obtained;

[0037] (2) Melt modification: put clean waste plastic strips into the reactor, control the pressure at 7~13MPa, and the temperature at 350~420°C, add titanate, superfine talc powder masterbatch, flame retardant, in the catalyst , Hydrocracking 30min under the condition of stirring to obtain modified liquid plastics, the catalyst is cobalt loaded on alumina; the addition amount of titanate is 7% of the quality of waste plastics and the addition amount of ultrafine talcum powder is 15% of the mass; the flame retardant is a mixtur...

Embodiment 3

[0041] A process for preparing plastic barrels from recycled plastics, comprising the following steps:

[0042] (1) Waste plastics are washed and dried with water, cut into strips, cleaned by ultrasonic filtration in an ultrasonic machine with ethanol, acetone and deionized water in sequence, and then washed twice with 120# gasoline and deionized water in sequence, and dried to Moisture is lower than 1wt%, and clean waste plastic strips are obtained;

[0043] (2) Melt modification: put clean waste plastic strips into the reactor, control the pressure at 7~13MPa, and the temperature at 350~420°C, add titanate, superfine talc powder masterbatch, flame retardant, in the catalyst , Stirring under the condition of hydrocracking for 30min to obtain modified liquid plastics, the catalyst is alumina loaded cobalt; the addition of titanate is 8% of the quality of waste plastics and the addition of ultrafine talcum powder is 1% of waste plastics 15% of the mass, the flame retardant is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of plastic products, in particular to a technology and device for preparing a plastic barrel through reprocessed plastics. The technology comprises the following steps that firstly, waste plastics are washed through water and dried and are shorn into strips, ethyl alcohol, acetone and deionized water are sequentially used for conducting ultrasonic filtering and cleaning in an ultrasonic machine, then 120# gasoline and deionized water are used for sequentially conducting two-time cleaning, drying is conducted till the water content is lower than 1 wt%, and the clean waste plastic strips are obtained; secondly, fusion modification is conducted; thirdly, vacuum defoaming is conducted; and fourthly, injection molding is conducted. According to the technology for preparing the plastic barrel through the reprocessed plastics, waste is utilized, influences on the surrounding environment can be reduced, the machining technology is simple and convenient to conduct, the requirement for mechanical equipment is not high, cost is low, and good economic benefits are achieved. The device used in the technology for preparing the plastic barrel through the reprocessed plastics is simple in structure, reasonable in design, small in occupied area, long in service life and convenient to mount and dismount, and the usage process is safe and environment-friendly.

Description

technical field [0001] The invention relates to the technical field of plastic products, in particular to a process and a device for preparing plastic buckets from recycled plastics. Background technique [0002] A plastic bucket is a bedding device used in storage. Due to the service life, service conditions (sun exposure) and acid and alkali corrosion of waste plastics, the impact strength and toughness of the plastics are reduced, so that the use value of waste plastics is not high; how to make waste plastics into plastic pallets Material is a technical problem that technicians have to consider to solve. Contents of the invention [0003] The object of the present invention is to provide a process for preparing plastic barrels from recycled plastics, and another object of the present invention is to provide a device for preparing plastic barrels from recycled plastics. [0004] In order to solve the problems of the technologies described above, the technical scheme ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29D22/00B29B13/02B29B13/00B29B17/00
CPCB29B13/00B29B13/022B29B17/00B29D22/003B29B2017/0021B29B2013/005B29B2017/0015Y02W30/62
Inventor 许波
Owner 常州群达环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap