Preparation process of fire and corrosion prevention wooden door

A preparation process and anti-corrosion technology, which is applied in fire-resistant coatings, biocide-containing paints, anti-fouling/underwater coatings, etc., can solve the problems of easy corrosion and flame retardancy of wooden doors, and achieve excellent fire performance, good market prospects, The effect suitable for promotion

Inactive Publication Date: 2018-12-21
江苏兄弟智能家居有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a preparation process for a fireproof and anticorrosion wooden door, which solves related defects such as easy corrosion and poor flame retardancy of the existing wooden door

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of preparation technology of fireproof anticorrosion wooden door, described preparation technology comprises the following steps:

[0019] (1) Preparation of fire-proof and anti-corrosion coating: prepared from the following raw materials by weight, 15 parts of water-based resin, 10 parts of polydimethylsiloxane, 0.4 parts of mica powder, 2 parts of silicone-modified styrene-acrylic emulsion, dispersed 4 parts of agent, 10 parts of flame retardant, 3 parts of fungicide, 4 parts of film-forming aid, 1 part of pH regulator, 2 parts of stabilizer;

[0020] Put the water-based resin, flame retardant, and fungicide in the reactor and mix evenly, stir for 10-15 minutes, then add the dispersant, mica powder, and silicone-modified styrene-acrylic emulsion into the reactor and mix, and then add the film-forming Additives, pH regulators and stabilizers continue to stir and disperse evenly to obtain fireproof and anticorrosion coatings.

[0021] (2) After polishing both si...

Embodiment 2

[0025] A kind of preparation technology of fireproof anticorrosion wooden door, described preparation technology comprises the following steps:

[0026] (1) Preparation of fire-resistant and anti-corrosion coating: prepared from the following raw materials by weight, 30 parts of water-based resin, 16 parts of polydimethylsiloxane, 1.2 parts of mica powder, 4 parts of silicone-modified styrene-acrylic emulsion, dispersed 8 parts of agent, 14 parts of flame retardant, 6 parts of fungicide, 6 parts of film-forming aid, 3 parts of pH regulator, and 4 parts of stabilizer;

[0027] Put the water-based resin, flame retardant, and fungicide in the reactor and mix evenly, stir for 10-15 minutes, then add the dispersant, mica powder, and silicone-modified styrene-acrylic emulsion into the reactor and mix, and then add the film-forming Additives, pH regulators and stabilizers continue to stir and disperse evenly to obtain fireproof and anticorrosion coatings.

[0028] (2) After polishin...

Embodiment 3

[0032] A kind of preparation technology of fireproof anticorrosion wooden door, described preparation technology comprises the following steps:

[0033] (1) Preparation of fire-resistant and anti-corrosion coating: prepared from the following raw materials by weight, 15-30 parts of water-based resin, 13 parts of polydimethylsiloxane, 0.8 parts of mica powder, and 3 parts of silicone-modified styrene-acrylic emulsion , 6 parts of dispersant, 12 parts of flame retardant, 5 parts of fungicide, 5 parts of film-forming aid, 2 parts of pH regulator, 3 parts of stabilizer;

[0034] Put the water-based resin, flame retardant, and fungicide in the reactor and mix evenly, stir for 10-15 minutes, then add the dispersant, mica powder, and silicone-modified styrene-acrylic emulsion into the reactor and mix, and then add the film-forming Additives, pH regulators and stabilizers continue to stir and disperse evenly to obtain fireproof and anticorrosion coatings.

[0035] (2) After polishing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a preparation process of a fire and corrosion prevention wooden door. The preparation process comprises the following steps that (1) a fire and corrosion prevention coating is prepared, wherein the raw materials comprise 15-30 parts of water-based resin, 10-16 parts of polydimethyl siloxane, 0.4-1.2 parts of mica powder, 2-4 parts of organic silicone modified styrene-acrylic emulsion,4-8 parts of a dispersant, 10-14 parts of a flame retardant, 3-6 parts of a bactericide, 4-6 parts of a film-forming assistant, 1-3 parts of a pH regulator and 2-4 parts of a stabilizer, the water-based resin, the flame retardant and the bactericide are put into a reaction kettle to be mixed evenly, then the dispersant, the mica powder and the organic silicone modified styrene-acrylic emulsion are added into the reaction kettle to be mixed, after mixing, the film-forming assistant, the pH regulator and the stabilizer are added, stirring continues to be carried out to disperse the materials evenly, and thus the fire and corrosion prevention coating is obtained; and (2) after the two sides of a door plate of the wooden door are polished smoothly, the fire and corrosion prevention coating issmeared, after air-drying of the coating, finish paint is smeared, and after air-drying of the finish paint, a layer of the fire and corrosion prevention coating is smeared.

Description

technical field [0001] The invention relates to the technical field of wooden door preparation, in particular to a preparation process of a fireproof and anticorrosion wooden door. Background technique [0002] With the continuous improvement of people's living standards, wooden doors have gradually developed from basic decoration and safety requirements to multi-functional requirements. Ordinary wooden doors should also have some specific functions for specific places of use. Since the essential materials of wooden doors are wood, Its fire-proof and flame-retardant properties are generally poor, which will increase the danger in the event of a fire; moreover, when the use time is long or the air humidity in the place of use is high or the environment is poor, the wooden door has a high probability of corrosion. It is easy to rot and mold, which seriously affects the appearance and performance of wooden doors, and also has certain hazards to the health of people around. Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More