Composition of water-based high-extensibility explosion-proof coating

A technology of elongation and composition, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of hidden dangers and low film yield, and achieve the effects of preventing broken, avoiding splashing, and buffering collision force

Active Publication Date: 2018-12-28
东周化学工业(昆山)有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the market, in the production of most mobile phones, in order to prevent fragmentation, the film is put on the inside during use. At the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition of water-based high-extensibility explosion-proof coating
  • Composition of water-based high-extensibility explosion-proof coating
  • Composition of water-based high-extensibility explosion-proof coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0032] As an embodiment of the present invention, calculated in parts by weight, it is characterized in that the composition at least contains:

[0033] 35~45 parts of water-based polyacrylate, 35~45 parts of anionic polyurethane aqueous dispersion, 0.3~1 part of leveling agent, 0.2~1 part of wetting agent, 10~20 parts of pure water, 0~ dimethyl maleate 10 servings.

[0034] As an embodiment of the present invention, calculated in parts by weight, it is characterized in that the composition at least contains:

[0035] 43 parts of aqueous polyacrylate, 43 parts of anionic polyurethane aqueous dispersion, 0.8 parts of leveling agent, 0.6 parts of wetting agent, 15 parts of pure water, and 6 parts of dimethyl maleate.

[0036] Water-based polyacrylate

[0037] Polyacrylate is obtained by copolymerizing acrylate monomers or methacrylate monomers with other olefin monomers. Polyacrylates prepared with different monomers and ratios have different properties.

[0038] Starting from the film-fo...

Embodiment approach 1

[0065] Embodiment 1. A composition of a water-based high-extension explosion-proof coating, the composition at least comprising:

[0066] Waterborne polyacrylate, anionic polyurethane waterborne dispersion, leveling agent, wetting agent, pure water, dimethyl maleate.

Embodiment approach 2

[0067] Embodiment 2. The composition of a water-based high-extensibility explosion-proof coating of embodiment 1, calculated in parts by weight, characterized in that the composition at least contains:

[0068] 35~45 parts of water-based polyacrylate, 35~45 parts of anionic polyurethane aqueous dispersion, 0.3~1 part of leveling agent, 0.2~1 part of wetting agent, 10~20 parts of pure water, 0~ dimethyl maleate 10 servings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a composition of a water-based high-extensibility explosion-proof coating. The composition is prepared from, at least, water-based polyacrylate, anionic polyurethane water-baseddispersion, a leveling agent, a wetting agent, pure water and dimethyl maleate. The water-based glass explosion-proof adhesive is the coating with water as a diluent, and volatized organic solvent isvery little and is only 5%-10% of a solvent type coating, so there is no problem of free TDI volatilization, and the coating is an environment-friendly product. The water-based glass explosion-proofadhesive can be prevented from being scattered after bursting and can also produce no residue after tearing again.

Description

Technical field [0001] The invention relates to the field of glass production, and more particularly to a composition of a water-based high-extension explosion-proof paint. Background technique [0002] Since the 1990s, the solvent-based coatings, paints and adhesives industries have gradually shifted from traditional varieties that are highly polluting, high-energy-consuming, and extremely dependent on petroleum industrial products to environmentally friendly, resource- and energy-saving products, and various environmentally friendly products. Varieties continue to emerge, among which the water-based coatings and water-based adhesive industries have made considerable progress. Water-based coatings have the advantages of low price, safe use, saving resources and energy, and reducing environmental pollution and public hazards. Therefore, they have become the main direction of the current development of the coating industry. Water-soluble coatings mainly refer to water-soluble res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/02C09D175/14C09D7/20
CPCC09D133/02C09D175/14C09D7/20C08L75/14C08L33/02
Inventor 林松香徐汉坤欧阳云
Owner 东周化学工业(昆山)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap