Processes for Improving Processing Quality of Ta18 Small Diameter Titanium Alloy Cold Rolled Tube

A process method and a technology of processing quality, applied in metal processing equipment, metal rolling, metal rolling, etc., can solve problems such as easy cracking due to cold deformation, rough surface finish, high deformation resistance, etc., to avoid cold rolling cracks, surface Smooth, improve the effect of aperture

Active Publication Date: 2020-04-21
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This titanium alloy has the disadvantages of rolling process such as large deformation resistance, strong work hardening, easy cracking due to cold deformation, and poor surface finish.
The TA18 tube billet obtained by hot extrusion often has the characteristics of rough surface finish, serious wall thickness eccentricity, and many defects on the inner and outer surfaces of the billet. After subsequent cold rolling, it cannot meet the shape, size, and surface quality requirements of TA18 titanium alloy pipe.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] In order to solve the above-mentioned technical problems existing in the prior art, the present invention provides a process method for improving the processing quality of TA18 small-diameter titanium alloy cold-rolled pipes that can obtain titanium alloy pipes with uniform wall thickness and smooth surface by cold rolling . The process method includes the preparation of tube billets, the selection and adjustment of deformation rolling tools and the preparation of lubricating coolants, and the deformation rate of each pass is 20% to 25%, the feeding amount is 2 to 5mm, and the three-roll cold rolling mill Each stroke angle is 53 °, and the rolling process parameters of 10-18 times / min are carried out at least two passes of diameter reduction, wall reduction and wall thickness deviation cold rolling several processes to complete the described small The rolling work of the caliber TA18 titanium alloy cold-rolled pipe, in which, when the total number of rolling passes exce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process method for improving the processing quality of a TA18 small-opening-diameter titanium alloy cold rolling pipe, and belongs to the technical field of sectional material cold rolling processes. According to the process method for improving the processing quality of the TA18 small-opening-diameter titanium alloy cold rolling pipe, the titanium alloy pipe with the even wall thickness and smooth surface can be obtained in a cold rolling mode. The process method comprises working procedures of preparation of a pipe blank, selecting and adjusting of deformation rolling tools, preparation of a lubrication coolant, and two or more passes of diameter decreasing, wall reducing and wall thickness difference adjusting cold rolling to roll the TA18 small-opening-diameter titanium alloy cold rolling pipe, wherein when the number of the total rolling passes is more than two, after two passes of rolling are completed each time, the working procedures of preparation ofthe pipe blank, adjusting of the deformation rolling tools and preparation of the lubrication coolant need to be carried out again, and then the corresponding passes of diameter decreasing, wall reducing and wall thickness difference adjusting rolling is carried out till a finished TA18 small-opening-diameter titanium alloy cold rolling pipe product with the opening diameter and wall thickness meeting the requirements is rolled.

Description

technical field [0001] The invention relates to a process method, in particular to a process method for improving the processing quality of TA18 small-diameter titanium alloy cold-rolled pipes, and belongs to the technical field of profile cold-rolling processes. Background technique [0002] TA18 titanium alloy belongs to α+β two-phase titanium alloy, in which the content of α-stable elements is 3%, and the content of β-stable elements is 2.5%. This titanium alloy has the disadvantages of rolling process such as large deformation resistance, strong work hardening, easy cracking due to cold deformation, and poor surface finish. The TA18 tube billet obtained by hot extrusion often has the characteristics of rough surface finish, serious wall thickness eccentricity, and many defects on the inner and outer surfaces of the billet. After subsequent cold rolling, it cannot meet the shape, size, and surface quality requirements of TA18 titanium alloy pipe. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B23/00B21B45/02B21B37/00
CPCB21B23/00B21B37/00B21B45/0206B21B45/0242
Inventor 冯庆江健
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products