Environmentally friendly putty powder

A kind of putty powder, an environment-friendly technology, applied in the field of decoration coatings, can solve the problems of infringing on human health and poor living effect, and achieve the effects of improving environmental protection performance, increasing utilization rate, and reducing side effects

Inactive Publication Date: 2019-01-15
贵州省漆彩金州涂料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] House decoration is inseparable from the use of putty powder, but in many existing putty powders, due to the strong side effects of some raw materials, it will emit gas that is harmful to human health, resulting in poor living effects and other situations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment provides an environment-friendly putty powder and a processing method thereof. The putty powder includes the following raw materials with a particle size of 50 μm in parts by weight:

[0030] 30 parts of plant ash, 20 parts of steel sand, 60 parts of white cement, 10 parts of white mud, 12 parts of talcum powder, 4 parts of nanometer ferric oxide, 3 parts of hydroxyethyl cellulose, 3 parts of EVA plastic material, TiO 2 3 parts, SiO 2 1 part, 3 parts of cellulose ether, Al 2 o 3 2 parts, 0.5 parts of aluminum sulfate, 3 parts of sodium lignosulfonate, and 3 parts of plant-derived raw materials.

[0031] In this embodiment, the plant ash is made by mixing and processing pine burning ashes, durian burning ashes, and jackfruit burning ashes in a ratio of 35:5:9;

[0032] Wherein, the plant ash has a particle size of 50 μm and a whiteness of 92%.

[0033] In the present embodiment, the preparation method of the environment-friendly putty powder is as fol...

Embodiment 2

[0039] This embodiment provides an environment-friendly putty powder and a processing method thereof. The environment-friendly putty powder includes the following raw materials with a particle size of 40 μm in parts by weight:

[0040] An environment-friendly putty powder, comprising the following raw materials in parts by weight whose particle size is 40 μm:

[0041] 45 parts of plant ash, 15 parts of steel sand, 80 parts of white cement, 5 parts of white mud, 20 parts of talcum powder, 4 parts of nanometer ferric oxide, 3 parts of hydroxyethyl cellulose, 3 parts of EVA plastic material, TiO 2 1 part, SiO 2 3 parts, 2 parts of cellulose ether, Al 2 o 3 4 parts, 1 part of aluminum sulfate, 5 parts of sodium lignosulfonate, and 2 parts of plant-derived raw materials.

[0042] Preferably, the plant ash is made by mixing and processing pine burning ashes, durian burning ashes, and jackfruit burning ashes in a ratio of 35:5:9;

[0043] Wherein, the plant ash has a particle siz...

Embodiment 3

[0050] This embodiment provides an environment-friendly putty powder and a processing method thereof. The environment-friendly putty powder includes the following raw materials with a particle size of 35 μm in parts by weight:

[0051] 40 parts of plant ash, 18 parts of steel sand, 70 parts of white cement, 8 parts of white mud, 12 parts of talcum powder, 5 parts of nanometer ferric oxide, 3 parts of hydroxyethyl cellulose, 4 parts of EVA plastic material, TiO 2 2 parts, SiO 2 2 parts, 2 parts of cellulose ether, Al 2 o 3 2 parts, 0.8 parts of aluminum sulfate, 7 parts of sodium lignosulfonate, and 10 parts of plant-derived raw materials.

[0052] Preferably, the plant ash is made by mixing and processing pine burning ashes, durian burning ashes, and jackfruit burning ashes in a ratio of 35:5:9;

[0053] Wherein, the plant ash has a particle size of 35 μm and a whiteness of 98%.

[0054] In the present embodiment, the preparation method of the environment-friendly putty po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of decoration coating, and particularly relates to environmentally friendly putty powder. The putty powder includes 30-45 parts of plant ash, 15-20 parts of steel shot, 60-80 parts of white cement, 5-10 parts of white clay, 5-20 parts of talc powder, 4-7 parts of nanometer ferric oxide, 2-3 parts of hydroxyethyl cellulose, 3-4 parts of an EVA plastic raw material, 1-3 parts of TiO2, 1-3 parts of SiO2, 2-3 parts of cellulose ether, 2-4 parts of Al2O3, 0.5-1 part of aluminum sulfate, 1-7 parts of sodium lignosulfonate and 2-10 parts of a plant-sourceraw material. The plant ash prepared by mixing pine tree burning ash, durian burning ash, and jack fruit burning ash is adopted as a main raw material, is adhesive and is adopted as a matrix. The plant ash is mixed with other organic and inorganic raw materials to prepare the putty powder. The inorganic matter quantity demanded is directly reduced through application of a large amount of plant rawmaterials, thus reducing dosage of compounds having side effects, and reducing side effects of the finished product putty powder.

Description

technical field [0001] The invention relates to the technical field of decoration coatings, in particular to an environment-friendly putty powder. Background technique [0002] Putty powder is a kind of building decoration material, the main components are talcum powder and glue. I just bought a layer of white putty on the surface of the blank room. Usually the whiteness of the putty is above 90° and the fineness is above 330°. Putty powder is a kind of base material for leveling the wall, which lays a good foundation for future decoration (painting and wallpaper). Putty is divided into two kinds: putty inside wall and putty on exterior wall. External wall putty can resist wind and sun, so it has good gelation, high strength and low environmental index. The comprehensive index of putty in the inner wall is good, and it is hygienic and environmentally friendly. Therefore, the inner wall is not for external use and the outer wall is not for internal use. [0003] House deco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 肖坤学李光明
Owner 贵州省漆彩金州涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com