A kind of superabsorbent resin superfine powder surface modification method and modification liquid

A technology of superabsorbent resin and ultrafine powder, which is applied in the field of superabsorbent resin ultrafine powder surface modification method and modifying liquid, which can solve the problems of not finding a more reasonable modification method, so as to improve permeability and enhance Dryness, improve the effect of moisture resistance

Active Publication Date: 2021-08-13
ZHONGKAI UNIV OF AGRI & ENG
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For ultra-fine superabsorbent resin powder with small particle size, it is easy to quickly absorb solution and agglomerate during the modification process, so far no reasonable modification method has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of superabsorbent resin superfine powder surface modification method and modification liquid
  • A kind of superabsorbent resin superfine powder surface modification method and modification liquid
  • A kind of superabsorbent resin superfine powder surface modification method and modification liquid

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0060] Correspondingly, the present invention also provides a method for preparing a superabsorbent resin surface modification liquid, which includes:

[0061] (1) dispersing the dispersant in water to obtain a mixed solution;

[0062] (2) uniformly dispersing the surface crosslinking agent and the initiator in the mixed solution to obtain the oil-in-water type surface modification solution;

[0063] Correspondingly, the present invention also provides a superabsorbent resin, which is modified by the above-mentioned surface modification method.

Embodiment 1

[0066] Surface modification fluid formula:

[0067] 50 parts of water, 34 parts of dispersant, 11 parts of surface crosslinking agent, 0.3 parts of initiator, 5 parts of white carbon black;

[0068] Among them, the dispersant is methanol, the surface crosslinking agent includes 2 parts of ethylene glycol diglycidyl ether, 6 parts of 1,4-butanediol, and 3 parts of trimethylhydroxypropane triacrylate; 0.1 part of morphine hydrochloride (Va044) and 0.2 part of ammonium persulfate;

[0069] Surface modification method:

[0070] (1) Add the dispersant and white carbon black into the water, and evenly stir to obtain the mixed solution;

[0071] (2) Surface crosslinking agent and initiator are added in the mixed solution, and the surface modification solution is obtained after stirring;

[0072] (3) Weigh 14 parts of the above-mentioned reaction solution, and evenly spray on the surface of 100 parts of superabsorbent resin superfine powder, stir vigorously during the spraying proc...

Embodiment 2

[0076] Surface modification fluid formula:

[0077] 60 parts of water, 24 parts of dispersant, 11 parts of surface crosslinking agent, 0.3 parts of initiator, 5 parts of white carbon black;

[0078] Among them, ethanol is selected as the dispersant, and the surface crosslinking agent includes 2 parts of ethylene glycol diglycidyl ether, 6 parts of 1,4-butanediol, 3 parts of nonamethylhydroxypropane triacrylate; the initiator includes azobisisobutyl 0.1 part of imidazoline hydrochloride (Va50) and 0.2 part of ammonium persulfate;

[0079] Surface modification method:

[0080] (1) Add the dispersant and white carbon black into the water, and evenly stir to obtain the mixed solution;

[0081] (2) Surface crosslinking agent and initiator are added in the mixed solution, and the surface modification solution is obtained after stirring;

[0082] (3) Weigh 12 parts of the above reaction solution, and evenly spray on the surface of 100 parts of superabsorbent resin superfine powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for surface modification of superfine superabsorbent resin powder, which comprises the steps of dispersing a dispersant in water, adding a surface crosslinking agent and an initiator to obtain an oil-in-water type surface modification liquid; uniformly distributing the surface modification liquid Coated on the surface of superabsorbent resin superfine powder; and successively treated at 50-80°C and 110-150°C to obtain surface-modified superfine superabsorbent resin powder; meanwhile, the invention also discloses a surface The modifying liquid comprises, in parts by weight: 40-70 parts of water, 20-50 parts of dispersant, 5-20 parts of surface crosslinking agent, and 0.01-2 parts of initiator. The invention adopts a specific surface modifying liquid to realize the modification of the superfine superabsorbent resin powder with a mesh size of less than 150, and improve the moisture resistance, yellowing resistance and absorption permeability of the superfine superabsorbent resin powder.

Description

technical field [0001] The invention relates to a method for modifying a superabsorbent resin, in particular to a method for modifying the surface of superfine powder of a superabsorbent resin and a modifying liquid. Background technique [0002] Super Absorbent Polymer (SAP) is a new type of functional polymer material. A synthetic resin with hydrophilic groups that can absorb a large amount of water and swell while keeping the water from flowing out. At present, superabsorbent resin (superfine superabsorbent resin powder) products generally absorb air moisture and cause yellowing or stickiness during storage, which brings a lot of inconvenience during production and use, and will cause Serious impact on the product, such as affecting the transportation, storage and application of the product, how to effectively prevent the superabsorbent resin superfine powder from absorbing air moisture and causing yellowing has become the concern and hard work of the superabsorbent resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/12C08L101/12
CPCC08J3/128C08J2300/12
Inventor 刘其海贾振宇
Owner ZHONGKAI UNIV OF AGRI & ENG