Ceramic tile adhesive

An adhesive and ceramic tile technology, applied in the field of ceramic tile adhesives, can solve the problems of poor peeling and bonding, tile bonding and sinking, poor flow resistance of mortar, etc. Effect

Inactive Publication Date: 2019-02-22
REAL ESTATE CONSTR ANGANG GROUP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of the decoration industry, the traditional cement mortar bonded ceramic tiles, due to the poor flow resistance of the mortar, when pasting vertical components such as walls, the tiling must start from the low end, and the tiles need to be used Only the locator can achieve neat bonding. The tiles after bonding often appear hollow, falling off and bonding is not strong, the tiles are bonded and sink, and the problem of uneven bonding, especially for exterior wall decoration, will also bring safety problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The present invention will be described in detail below, but it should be noted that the implementation of the present invention is not limited to the following embodiments.

[0015] A ceramic tile adhesive, comprising the following raw materials in parts by weight: 40-45 parts of cement, 40-45 parts of silica sand, 15-20 parts of heavy calcium powder, 3-5 parts of redispersible latex powder, and 2-5 parts of additives;

[0016] Among them, the cement is Portland cement; the fineness of silica sand is less than 200 mesh, the mud content is less than 0.5% by weight, and the water content is less than 0.5% by weight; the fineness of heavy calcium powder is less than 200 mesh, and the water content is less than 0.5%. Less than 0.5% by weight; additive is the mixture of cellulose ether, lignocellulose, starch ether, can according to cellulose ether: lignocellulose: starch ether=(1-5): (0.8-3): (0.8- 5). The non-volatile content of the redispersible latex powder is greater ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Ash contentaaaaaaaaaa
Login to view more

Abstract

The invention relates to a ceramic tile adhesive. The ceramic tile adhesive is prepared from the following raw materials in parts by weight: 40-45 parts of cement, 40-45 parts of silica sand, 15-20 parts of heavy calcium powder, 3-5 parts of re-dispersible latex powder, and 2-5 parts of an additive; the cement is silicate cement; as for the silica sand, the fineness is 200 meshes or below, the mudcontent is smaller than 0.5% by weight, and the water content is smaller than 0.5% by weight; as for the heavy calcium powder, the fineness is 200 meshes or below, and the water content is smaller than 0.5% by weight; and the additive is a mixture of cellulose ether, lignocellulose and starch ether. The ceramic tile adhesive has the advantages that various organic polymers are added, the bondingstrength is high, the hardening speed is high, and the service life of various ceramic tiles is greatly prolonged; and the ceramic tile adhesive is convenient to construct, and can be used only by adding the right amount of fresh water to be stirred, and the pasted ceramic tiles can be directly pasted without being soaked in water.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a ceramic tile adhesive used for bonding ceramic tiles and facing tiles. Background technique [0002] With the rapid development of the decoration industry, the traditional cement mortar bonded ceramic tiles, due to the poor flow resistance of the mortar, when pasting vertical components such as walls, the tiling must start from the low end, and the tiles need to be used Only the locator can achieve neat jointing. After bonding, the tiles often appear empty, falling off and bonding is not strong, the tiles are bonded and sink, and the problem of uneven bonding, especially for exterior wall decoration, will also bring safety problems. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the object of the present invention is to provide a ceramic tile adhesive, which improves the bonding strength between the tile and the base material, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/20C04B111/27
CPCC04B28/04C04B2111/00482C04B2111/00646C04B2111/20C04B2111/27C04B14/06C04B14/28C04B24/383C04B24/38C04B18/26C04B2103/0057
Inventor 高前时维华石爽蒋金博靳文奎
Owner REAL ESTATE CONSTR ANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap