A kind of preparation method of reflective film water-soluble acrylic resin

A water-soluble acrylic, reflective film technology, applied in reflective/signal paints, coatings, etc., can solve problems such as explosive bubbles

Active Publication Date: 2020-07-17
浙江龙游道明光学有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at adding hydrophilic emulsifiers and other substances to the water-soluble acrylic resin existing in the prior art, which leads to certain defects in the water resistance of the water-soluble acrylic resin, and coating in the production of reflective film Defects such as easy bursting of thicker water-based acrylic resins provide a new preparation method for reflective film water-soluble acrylic resins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of reflective film water-soluble acrylic resin
  • A kind of preparation method of reflective film water-soluble acrylic resin
  • A kind of preparation method of reflective film water-soluble acrylic resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A method for preparing a reflective film with a water-soluble acrylic resin, comprising the following raw materials in parts by weight:

[0044] 4 parts methyl methacrylate,

[0045] 10 parts of ethyl acrylate,

[0046] 3 parts lauryl methacrylate,

[0047] 1 part of hydroxyethyl methacrylate,

[0048] 3 parts acrylic,

[0049] 15 parts of 1-ethoxy-2 propanol,

[0050] 3 parts of dimethylethanolamine,

[0051] 40 parts of deionized water,

[0052] Benzoyl peroxide 0.2 parts,

[0053] The preparation steps are as follows:

[0054] (1) At room temperature, weigh 30% of the total weight of methyl methacrylate, 30% of the total weight of ethyl acrylate, 30% of the total weight of lauryl methacrylate, and 30% of the total weight of hydroxyethyl methacrylate. %, 30% of the total weight of acrylic acid, 45% of the total weight of 1-ethoxyl-2 propanol, 15% of the total weight of benzoyl peroxide, and they are mixed and prepared to form mixed solution A;

[0055] (2) Pu...

Embodiment 2

[0063] A method for preparing a reflective film with a water-soluble acrylic resin, comprising the following raw materials in parts by weight:

[0064] 10 parts of methyl methacrylate,

[0065] 17 parts of ethyl acrylate,

[0066] Lauryl methacrylate 7 parts,

[0067] 4 parts of hydroxyethyl methacrylate,

[0068] Acrylic acid 5 parts,

[0069] 22 parts of 1-ethoxy-2 propanol,

[0070] 5 parts of dimethylethanolamine,

[0071] 50 parts of deionized water,

[0072] Benzoyl peroxide 0.4 parts,

[0073] The preparation steps are as follows:

[0074] (1) At room temperature, weigh 15% of the total weight of methyl methacrylate, 20% of the total weight of ethyl acrylate, 20% of the total weight of lauryl methacrylate, and 25% of the total weight of hydroxyethyl methacrylate. %, 25% of the total weight of acrylic acid, 45% of the total weight of 1-ethoxyl-2 propanol, 15% of the total weight of benzoyl peroxide, and they are mixed and prepared to form mixed solution A;

[00...

Embodiment 3

[0083] A method for preparing a reflective film with a water-soluble acrylic resin, comprising the following raw materials in parts by weight:

[0084] 7 parts of methyl methacrylate,

[0085] 13.5 parts of ethyl acrylate,

[0086] Lauryl methacrylate 5 parts,

[0087] 2.5 parts of hydroxyethyl methacrylate,

[0088] 4 parts acrylic,

[0089] 18.5 parts of 1-ethoxy-2 propanol,

[0090] 4 parts of dimethylethanolamine,

[0091] 45 parts of deionized water,

[0092] Benzoyl peroxide 0.3 parts,

[0093] The preparation steps are as follows:

[0094] (1) At room temperature, weigh 22.5% of the total weight of methyl methacrylate, 25% of the total weight of ethyl acrylate, 25% of the total weight of lauryl methacrylate, and 27.5% of the total weight of hydroxyethyl methacrylate. %, 27.5% of the total weight of acrylic acid, 50% of the total weight of 1-ethoxy-2 propanol, and 25% of the total weight of benzoyl peroxide, and they are mixed and prepared to form mixed solution ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of water-soluble acrylic resin for a reflection film. The water-soluble acrylic resin is prepared from the following raw materials in parts by weight: methyl methacrylate, ethyl acrylate, lauryl methacrylate, hydroxyethyl methylacrylate, acrylic acid, 1-ethyoxyl-2 propyl alcohol, dimethylethanolamine, deionized water and benzoperoxide through the following preparation steps of preparing a mixed solution A, feeding the mixed solution A into a reaction container to react, performing stirring, and continuously inputting nitrogen gas; stopping the nitrogen gas input, and raising and maintaining the temperature; preparing and dripping a mixed solution B, and after the dripping completion, maintaining the temperature; preparing and dripping a mixed solution C, and after the dripping completion, maintaining the temperature; preparing a mixed solution D, performing high-speed stirring dispersion, turning off a machine, and pouring out the materialsto obtain the transparent water-soluble acrylic resin for the reflection film. The water-soluble acrylic resin obtained by the invention has the advantages of good water resistance, intensity and elongation balance; and when the water-soluble acrylic resin is applied to the reflection film production, a reverse adhesion phenomenon and sudden and violent bubbling cannot easily occur in the coating,so that the appearance is full and flat.

Description

technical field [0001] The invention relates to an acrylic resin, in particular to a preparation method of a water-soluble acrylic resin for a reflective film. Background technique [0002] Reflective film is a retroreflective material that has been made into a thin film and can be directly applied. From the development history, the reflective film is mainly divided into four categories, from the earliest glass bead exposed reflective film to the glass bead embedded reflective film, and then to the later capsule reflective film and microprism reflective film. At present, the reflective film used for vehicle license plates and the reflective film used in some projects and advertisements are mainly glass beads embedded reflective film. [0003] The glass bead embedded reflective film is mainly composed of five layers: surface layer, glass bead layer, focusing layer, metal plating layer, and pressure-sensitive adhesive layer. Because of the special weather resistance and chemi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/08C09D5/33C09D7/65C08F220/18C08F220/14C08F220/20C08F220/06
CPCC08F220/18C09D5/004C09D7/65C09D133/08C08L61/20C08F220/14C08F220/1812C08F220/20C08F220/06
Inventor 郑小平胡锋蓝庆东张思哲刘玫舒林飞
Owner 浙江龙游道明光学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com