Forming process of aluminum alloy pipe and aluminum alloy pipe

A technology of aluminum alloy tube and forming process, which is applied in the forming process of aluminum alloy tube and the field of aluminum alloy tube, which can solve the problem that the surface brightness of aluminum alloy tube is difficult to adapt to high-precision special devices, the surface roughness of aluminum alloy tube is high, and the performance of strengthening layer Problems such as uneven layers can be achieved to improve surface quality and performance, excellent comprehensive mechanical properties, and reduce surface damage

Inactive Publication Date: 2019-03-08
南通长海铝业有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above process can form a reinforced layer on the surface of aluminum alloy pipe fittings to improve its wear resistance, the performance of the reinforced layer is uneven, the surface quality is not high, the surface roughness of the aluminum alloy pipe is still high, and the surface of the aluminum alloy pipe is smooth. The brightness is difficult to adapt to the requirements of high-precision special devices, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming process of aluminum alloy pipe and aluminum alloy pipe
  • Forming process of aluminum alloy pipe and aluminum alloy pipe
  • Forming process of aluminum alloy pipe and aluminum alloy pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0087] A forming process of an aluminum alloy tube, comprising the following steps:

[0088] Extrude through the die first to get the aluminum alloy tube billet, then pass through the die, use the outer mold and the inner film to reversely extrude the wall thickness of the aluminum alloy tube billet, and before the reverse extrusion, the outer surface of the tube billet Evenly apply a layer of lubricant to reduce the diameter and wall thickness of the tube blank, and initially obtain an aluminum alloy tube with precise dimensions;

[0089] Then clean it. After cleaning, use the heat treatment high-temperature walk-in furnace to perform rapid annealing in the temperature range. The annealing temperature in the high-temperature range is 420°C for 10 minutes, and rapid cooling with water mist is performed to soften the aluminum alloy. After complete annealing, use The outer mold is cold drawn separately to reduce the outer diameter.

[0090] Among them, the outer model used is a...

Embodiment 2

[0092] A forming process of an aluminum alloy tube, comprising the following steps:

[0093] Extrude through the die first to get the aluminum alloy tube billet, then pass through the die, use the outer mold and the inner film to reversely extrude the wall thickness of the aluminum alloy tube billet, and before the reverse extrusion, the outer surface of the tube billet Evenly apply a layer of lubricant to reduce the diameter and wall thickness of the tube blank, and initially obtain an aluminum alloy tube with precise dimensions;

[0094] Then clean, after cleaning, use heat treatment high-temperature walk-in furnace to perform rapid annealing in the temperature range. The annealing temperature in the high-temperature range is 450°C for 15 minutes, and rapid cooling with water mist is performed to soften the aluminum alloy. After complete annealing, use The outer mold is cold drawn separately to reduce the outer diameter.

[0095] Wherein, the making material of outer mold is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of aluminum alloy pipe processing, and relates to a forming process of an aluminum alloy pipe and the aluminum alloy pipe. The forming process of the aluminum alloy pipe comprises the following steps that an aluminum alloy raw material is extruded to obtain an aluminum alloy pipe blank; the obtained aluminum alloy pipe blank is drawn, and then annealingtreatment is carried out; and after the obtained aluminum alloy pipe blank is completed annealed, cold drawing is carried out again, the deformation amount of the outer diameter of the pipe in the cold drawing process is less than 5%, and thus a finished product of the aluminum alloy pipe is obtained. According to the forming process of the aluminum alloy pipe and the aluminum alloy pipe, the process is simple, the implementation is easy, and the surface quality and service performance of the material can be simultaneously increased on the premise of not changing the mechanical properties ofthe material.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy tube processing, and in particular relates to a forming process of an aluminum alloy tube and the aluminum alloy tube. Background technique [0002] Aluminum alloy has the characteristics of high specific strength and specific stiffness, good plasticity, good thermal conductivity and easy recycling. It is the most widely used non-ferrous metal structural material in industry. , electronic products or chemical industry and other fields have been widely used. [0003] Aluminum alloy tubes can be divided into seamless aluminum tubes and ordinary extruded aluminum tubes according to the extrusion method; they can be divided into ordinary aluminum tubes and precision aluminum tubes according to the precision, and the precision aluminum tubes generally need to be reprocessed after extrusion, such as cold Refreshments. Aluminum alloy precision tubes are widely used in various industries of natio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/06B21C3/02C22F1/04C21D9/08
CPCB21C3/02B21C37/06C21D9/08C22F1/002C22F1/04
Inventor 张大平葛建荣李旭
Owner 南通长海铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap