Synthetic method capable of improving cement adaptability of polycarboxylate superplasticizer

A synthesis method and technology of water reducing agent, which are applied in the field of building materials, can solve the problems that the adaptability of cement cannot meet the requirements and the use effect is not good, and achieve the effects of wide adaptability, excellent weather resistance and excellent plastic retention performance of cement.

Inactive Publication Date: 2019-03-08
SUZHOU XINGBANG CHEM BUILDING MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The adaptability of the existing polycarboxylate superplasticizer to cement cannot meet the requirements, and the use effect is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Provide a kind of synthetic method that improves the cement adaptability of polycarboxylate superplasticizer, comprise the steps: add a certain amount of methallyl alcohol polyoxyethylene ether or isoprene in the 2000ml four-necked flask that stirrer is equipped with Alcohol polyoxyethylene ether monomer and deionized water are heated in a constant temperature water bath at a temperature of 50°C. After all the raw materials are dissolved and the temperature rises to 80°C, acrylic acid, sodium methacrylsulfonate and Initiator, after the initiator is added dropwise, heat preservation reaction for 1h, wherein, the acrylic acid: the molar ratio of the methallyl alcohol polyoxyethylene ether monomer or isoprenyl alcohol polyoxyethylene ether monomer is 4:1, the methallyl alcohol polyoxyethylene ether monomer or isoprenyl alcohol polyoxyethylene ether monomer: the molar ratio of the sodium methacryl sulfonate is 1:0.3, the initiator The addition amount accounts for the mass p...

Embodiment 2

[0019] Provide a kind of synthetic method that improves the cement adaptability of polycarboxylate superplasticizer, comprise the steps: add a certain amount of methallyl alcohol polyoxyethylene ether or isoprene in the 2000ml four-necked flask that stirrer is equipped with Alcohol polyoxyethylene ether monomer and deionized water are heated in a constant temperature water bath at a temperature of 60°C. After all the raw materials are dissolved and the temperature rises to 90°C, acrylic acid, sodium methacrylsulfonate and Initiator, wait until the initiator is added dropwise, heat preservation reaction for 1.5h, wherein, the molar ratio of the acrylic acid: the methallyl alcohol polyoxyethylene ether monomer or the isoprenyl alcohol polyoxyethylene ether monomer 3.5:1, the methallyl alcohol polyoxyethylene ether monomer or the isoprenyl alcohol polyoxyethylene ether monomer: the mol ratio of the sodium methacryl sulfonate is 1:0.5, the trigger The addition of agent accounts fo...

Embodiment 3

[0021] Provide a kind of synthetic method that improves the cement adaptability of polycarboxylate superplasticizer, comprise the steps: add a certain amount of methallyl alcohol polyoxyethylene ether or isoprene in the 2000ml four-necked flask that stirrer is equipped with Alcohol polyoxyethylene ether monomer and deionized water are heated in a constant temperature water bath at a temperature of 40°C. After all the raw materials are dissolved and the temperature rises to 70°C, acrylic acid, sodium methacrylsulfonate and Initiator, after the initiator is added dropwise, heat preservation reaction for 2h, wherein, the acrylic acid: the molar ratio of the methallyl alcohol polyoxyethylene ether monomer or isoprenyl alcohol polyoxyethylene ether monomer is 4.5:1, the methallyl alcohol polyoxyethylene ether monomer or isoprenyl alcohol polyoxyethylene ether monomer: the molar ratio of the sodium methacryl sulfonate is 1:0.1, the initiator The adding amount accounts for the mass p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a synthetic method capable of improving cement adaptability of a polycarboxylate superplasticizer. The method comprises the following steps: methyl allyl alcohol polyoxyethylene ether monomers or isoamyl allyl alcohol polyoxyethylene ether monomers in water are heated, acrylic acid, sodium methallyl sulfonate and an initiator are added dropwise to an aqueous solution sequentially for a reaction, and the polycarboxylate superplasticizer is obtained by posttreatment. According to the scheme, the prepared polycarboxylate superplasticizer has the advantages of low mixing quantity, high dispersity, high cement adaptability, excellent weather resistance and the like and has excellent flowing retention ability, and the synthetic method is implementable.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a synthesis method for improving the adaptability of polycarboxylate water reducer cement. Background technique [0002] Water reducer is a concrete admixture that can reduce the amount of mixing water while maintaining the slump of concrete basically unchanged. The water reducing agent will disperse the cement particles after being added to the concrete mixture, which can improve its workability, reduce the unit water consumption, improve the fluidity of the concrete mixture, reduce the unit cement consumption, and save cement. Most of the water reducers are anionic surfactants, including lignin sulfonate, naphthalene sulfonate formaldehyde polymer, etc. Polycarboxylate water reducer is also one of them. The adaptability of the existing polycarboxylate water reducer to cement cannot meet the requirements, and the use effect is not good. Contents of the invention [0003] Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/16C08F283/06C08F220/06C08F228/02C04B103/30
CPCC04B24/165C04B2103/302C08F283/065C08F220/06C08F228/02
Inventor 王香港沈焱钱佳佳毛荣良
Owner SUZHOU XINGBANG CHEM BUILDING MATERIALS
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com