Hollow glass sheet cleaning agent

A glass flake and glass technology, applied in the directions of detergent compounding agent, detergent composition, surface active detergent composition, etc., can solve the problems of glass surface damage, inability to clean well, incomplete cleaning, etc., and achieve good cleaning effect

Inactive Publication Date: 2019-03-12
安徽东耀建材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The glass sheets of insulating glass often have dust and impurities attached to them before and during processing. Generally, they are cleaned with water guns or high-pressure fans. Although this can remove the dust on the surface, some impurities cannot be removed. Good cleaning, but now many cleaning agents will cause damage to the surface of the glass, and if the cleaning is not thorough, there will be too many flaws in the process of bonding the glass sheet to the glass sheet, and it will not be good after bonding. Cleaning up will cause many defective products to appear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hollow glass sheet cleaning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A cleaning agent for glass sheets of hollow glass, characterized in that: it is made of the following materials by weight,

[0031] 8 parts of tall oil amphopropionate sodium, 8 parts of lauryl hydroxy sultaine, 4 parts of fatty alcohol polyoxyethylene hydrocarbon ether salt, 4 parts of absolute ethanol, 4 parts of sodium hypochlorite, babassu oleoyl amphoteric acid 4 parts of sodium, 6 parts of bamboo vinegar, 3 parts of 4% active protease, 6 parts of polyglycerol monolaurate, 7 parts of maltodextrin, 9 parts of blending agent, 35 parts of deionized water;

[0032] The preparation method comprises the following steps,

[0033] Ⅰ Add deionized water into the pot, then add the above-mentioned materials in turn, and stir while adding;

[0034] Ⅱ After stirring for 20-24 minutes, apply ultrasonic treatment;

[0035] Ⅲ Stir at 55-65°C for 16-21 minutes after ultrasonic treatment, then cool to 18-22°C;

[0036] The time interval for adding the materials in I is 2-4 minute...

Embodiment 2

[0048] A cleaning agent for glass sheets of hollow glass, characterized in that: it is made of the following materials by weight,

[0049] 4 parts of tall oil amphopropionate sodium, 4 parts of lauryl hydroxy sultaine, 1 part of fatty alcohol polyoxyethylene hydrocarbon ether salt, 1 part of absolute ethanol, 1 part of sodium hypochlorite, babassu oleoyl amphoteric acid 1 part of sodium, 2 parts of bamboo vinegar, 1 part of 4% active protease, 2 parts of polyglycerol monolaurate, 3 parts of maltodextrin, 5 parts of blending agent, 35 parts of deionized water;

[0050] The preparation method comprises the following steps,

[0051] Ⅰ Add deionized water into the pot, then add the above-mentioned materials in turn, and stir while adding;

[0052] Ⅱ After stirring for 20-24 minutes, apply ultrasonic treatment;

[0053] Ⅲ Stir at 55-65°C for 16-21 minutes after ultrasonic treatment, then cool to 18-22°C;

[0054] The time interval for adding the materials in I is 2-4 minutes;

...

Embodiment 3

[0065]Embodiment 3 A cleaning agent for glass sheets of hollow glass, characterized in that: it is made of the following materials by weight,

[0066] 5 parts of tall oil amphopropionate sodium, 6 parts of lauryl hydroxy sultaine, 2 parts of fatty alcohol polyoxyethylene hydrocarbon ether salt, 3 parts of absolute ethanol, 2 parts of sodium hypochlorite, babassu oleoyl amphoteric acid 3 parts of sodium, 4 parts of bamboo vinegar, 2 parts of 4% active protease, 5 parts of polyglycerol monolaurate, 6 parts of maltodextrin, 7 parts of blending agent, 32 parts of deionized water;

[0067] The preparation method comprises the following steps,

[0068] Ⅰ Add deionized water into the pot, then add the above-mentioned materials in turn, and stir while adding;

[0069] Ⅱ After stirring for 20-24 minutes, apply ultrasonic treatment;

[0070] Ⅲ Stir at 55-65°C for 16-21 minutes after ultrasonic treatment, then cool to 18-22°C;

[0071] The time interval for adding the materials in I i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of hollow glass processing and manufacturing, in particular to a hollow glass sheet cleaning agent. The hollow glass sheet cleaning agent is prepared from,by weight, 4-8 parts of sodium tallamphopropionate, 4-8 parts of lauryl hydroxysultaine, 1-4 parts of fatty alcohol polyoxyethylene ether salt, 1-4 parts of absolute ethyl alcohol, 1-4 parts of sodium hypochlorite, 1-4 parts of sodium babassuamphoacetate, 2-6 parts of bamboo vinegar, 1-3 parts of 4% active protease, 2-6 parts of polyglycerol monolaurate, 3-7 parts of maltodextrin, 5-9 parts of ablender and 30-35 parts of deionized water. A method is reasonable, effectiveness in cleaning is achieved, and glass damages are avoided.

Description

technical field [0001] The invention relates to the technical field of hollow glass processing and manufacturing, in particular to a cleaning agent for glass sheets of hollow glass. Background technique [0002] Insulating glass is a high-performance sound-insulating and heat-insulating glass made of two (or three) pieces of glass, using a high-strength and high-air-tight composite adhesive to bond the glass pieces to an aluminum alloy frame containing a desiccant. The performance of insulating glass is superior to that of ordinary double-layer glass, so it has been recognized by all countries in the world. Insulating glass is to separate two or more pieces of glass evenly with effective support and bond and seal the periphery, so that a dry gas is formed between the glass layers. Space glassware. Its main materials are glass, warm edge spacer, angle bolts, butyl rubber, polysulfide glue, and desiccant. [0003] Insulating glass is composed of two or more layers of flat gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11D1/94C11D3/33C11D3/37C11D3/20C11D3/04C11D3/386C11D3/22C11D3/60C11D3/382
CPCC11D1/74C11D1/92C11D1/94C11D3/046C11D3/201C11D3/2079C11D3/222C11D3/33C11D3/3707C11D3/382C11D3/38618
Inventor 张耀东
Owner 安徽东耀建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com