Low temperature-resistant heat-resistant long-life PVC (Polyvinyl Chloride) automobile wire cable material

An automotive wire, low temperature resistant technology, applied in the field of auto parts, can solve problems such as easy cracking, and achieve the effect of improving insulation performance and inhibiting discharge damage

Inactive Publication Date: 2019-03-15
百通赫思曼工业(苏州)有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the automotive wire is bent and used under extremely low temperature conditions, it is extremely easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A PVC automotive wire and cable material with low temperature resistance, heat resistance and long service life, comprising the following components: 100 parts by weight of polyvinyl chloride (PVC), 45 parts by weight of plasticizer, 5 parts by weight of composite stabilizer, 3 parts by weight The composite flame retardant of 5 parts by weight, the additive of 5 parts by weight, the composite lubricant of 0.5 parts by weight, the auxiliary stabilizer of 0.6 parts by weight, the color masterbatch of 1 part by weight;

[0021] The preparation method of the PVC automobile wire and cable material comprises the following preparation steps:

[0022] S1. Add 100 parts by weight of PVC to the high-speed mixer, then add composite stabilizer and half of the weight of plasticizer, mix at low speed for one minute, then turn to high speed for five minutes, add the remaining plasticizer, Turn low speed to high speed mixing until 90°C, then add compound flame retardant, additive, comp...

Embodiment 2

[0033] A PVC automotive wire and cable material with low temperature resistance, heat resistance and long service life, comprising the following components: 100 parts by weight of polyvinyl chloride (PVC), 50 parts by weight of plasticizer, 8 parts by weight of composite stabilizer, 4 parts by weight Composite flame retardant, additive of 15 parts by weight, composite lubricant of 0.6 parts by weight, auxiliary stabilizer of 0.9 parts by weight, color masterbatch of 1.5 parts by weight;

[0034] The preparation method of the PVC automobile wire and cable material comprises the following preparation steps:

[0035] S1. Add 100 parts by weight of PVC to the high-speed mixer, then add composite stabilizer and half of the weight of plasticizer, mix at low speed for one minute, then turn to high speed for five minutes, add the remaining plasticizer, Turn low speed to high speed mixing until 90°C, then add compound flame retardant, additive, compound lubricant, auxiliary stabilizer ...

Embodiment 3

[0046] A PVC automotive wire and cable material with low temperature resistance and heat resistance and long service life, comprising the following components: 100 parts by weight of polyvinyl chloride (PVC), 55 parts by weight of plasticizer, 11 parts by weight of composite stabilizer, 5 parts by weight of Composite flame retardant, 25 parts by weight of additives, 0.8 parts by weight of composite lubricant, auxiliary stabilizer of 1.3 parts by weight, color masterbatch of 2 parts by weight;

[0047] The preparation method of the PVC automobile wire and cable material comprises the following preparation steps:

[0048] S1. Add 100 parts by weight of PVC to the high-speed mixer, then add composite stabilizer and half of the weight of plasticizer, mix at low speed for one minute, then turn to high speed for five minutes, add the remaining plasticizer, Turn low speed to high speed mixing until 90°C, then add compound flame retardant, additive, compound lubricant, auxiliary stabi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low temperature-resistant heat-resistant long-life PVC (Polyvinyl Chloride) wire cable material which is prepared from the following components: 100 weight parts of PVC, 45 to 55 weight parts of a plasticizer, 5 to 11 weight parts of a composite stabilizer, 3 to 5 weight parts of a composite flame retardant, 5 to 25 weight parts of additives, 0.5 to 0.8 weight part of a composite lubricating agent, 0.6 to 1.3 weight parts of auxiliary stabilizers and 1 to 2 weight parts of colour masterbatches; the low temperature-resistant heat-resistant long-life PVC wire cable material takes the PVC as a base material; N-C8-C10 alcohol tribenzoate and dioctyl sebacate are added into the base material, so that the mixture can bear the low temperature of -40 DEG C and the high temperature of 105 DEG C; the auxiliary stabilizers, such as a special calcium-zinc composite stabilizer, hydrotalcite and beta-diketone, are added and cooperate the plasticizer, so that the long-term aging performance of the formula can be ensured; kaolin and silicone are added to improve the insulating property of the PVC material, so that the discharge damage in a wire transmission process can beinhibited.

Description

technical field [0001] The invention relates to the technical field of automobile parts, in particular to a PVC automobile wire and cable material with low temperature resistance, heat resistance and long service life. Background technique [0002] At present, most of the domestic automobile wire and cable materials are ordinary cable materials. If the automobile wiring harness is overloaded for a long time, the temperature of the wire will exceed the maximum allowable temperature, which will accelerate the aging of the wire insulation, damage it, and cause a fire. During the operation of automobile wires, the insulation of the wires will be heated and the performance will gradually degrade until it fails. Automobile wires are prone to cracking when they are bent and used under extremely low temperature conditions. Electric wires should ensure that the insulating material has the required mechanical properties within the life of the vehicle, so there are higher requirements...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L83/04C08K13/02C08K5/12C08K5/11C08K3/26C08K5/07C08K3/34
CPCC08L27/06C08L2201/08C08L2203/202C08L83/04C08K13/02C08K5/12C08K5/11C08K3/26C08K5/07C08K3/346
Inventor 彭海合
Owner 百通赫思曼工业(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com