Metal oxide composite nano material based on eggshell membrane template, preparation method and application thereof
A technology for composite nanomaterials and eggshell membranes, applied in the field of their preparation and metal oxide composite nanomaterials, can solve the problems of complicated operation, high processing cost, low efficiency, etc., and achieves simple and feasible preparation method and simple preparation method. Fast, easy-to-prepare results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] A metal oxide composite nanomaterial based on an eggshell membrane template, and its preparation method specifically includes the following steps:
[0033] (1) Eggshell membrane pretreatment: collect discarded eggshells, wash the eggshells with deionized water repeatedly, tear off the eggshell membranes from the eggshells with tweezers, and dry them at room temperature for later use.
[0034] (2) Preparation of carrier eggshell membranes: soak 1 g of dried eggshell membranes in 15 mL of 10% by volume dilute HCl solution for 10 min, then wash with deionized water three times, and store at room temperature. Dry to obtain carrier eggshell membrane;
[0035] (3) Preparation of CuO-ZnO solution: 2.42 g of Cu(NO 3 ) 2 ·3H 2 O and 2.97 g Zn(NO 3 ) 2 ·6H 2 O was added to 100 mL deionized water, and stirred until completely dissolved to obtain a CuO-ZnO solution;
[0036] (4) Preparation of CuO-ZnO-loaded eggshell membrane: Add 1 g of carrier eggshell membrane obtained in...
Embodiment 2
[0039] A metal oxide composite nanomaterial based on an eggshell membrane template, and its preparation method specifically includes the following steps:
[0040] (1) Eggshell membrane pretreatment: collect discarded duck eggshells, wash the eggshells with deionized water repeatedly, tear off the eggshell membranes from the duck eggshells with tweezers, and dry them at room temperature for later use.
[0041] (2) Preparation of carrier eggshell membrane: 1 g of dried eggshell membrane was soaked in 15 mL of 10% by volume dilute HCl solution for 30 min, then washed three times with deionized water, and then incubated at room temperature. Dry to obtain carrier eggshell membrane;
[0042] (3) Preparation of CuO-ZnO solution: 4.84 g of Cu(NO 3 ) 2 ·3H 2 O and 5.94 g Zn(NO 3 ) 2 ·6H 2O was added into 100 mL of deionized water, and stirred until completely dissolved to obtain a CuO-ZnO solution;
[0043] (4) Preparation of CuO-ZnO-loaded eggshell membrane: Add 2 g of the carr...
Embodiment 3
[0046] A metal oxide composite nanomaterial based on an eggshell membrane template, and its preparation method specifically includes the following steps:
[0047] (1) Eggshell membrane pretreatment: collect discarded goose eggshells, wash the eggshells with deionized water repeatedly, tear off the eggshell membranes from the goose eggshells with tweezers, and dry them at room temperature for later use.
[0048] (2) Preparation of carrier eggshell membrane: 1 g of dried eggshell membrane was soaked in 15 mL of 10% by volume dilute HCl solution for 20 min, then washed three times with deionized water, and incubated at room temperature. Dry to obtain carrier eggshell membrane;
[0049] (3) Preparation of CuO-ZnO solution: 3.63 g of CuCl 2 and 4.5 g ZnCl 2 Add to 100 mL deionized water, stir until completely dissolved to obtain CuO-ZnO solution;
[0050] (4) Preparation of CuO-ZnO-loaded eggshell membrane: Add 0.5 g of carrier eggshell membrane obtained in step (2) into 100 mL ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com