A composite flooring and inorganic material technology, applied in the field of building materials, can solve the problems of large amount of organic solvent usage, health hazards of environmental processing personnel, etc., and achieve the effects of less health hazards, increased bonding force and toughness, and increased strength and hardness. Effect

Inactive Publication Date: 2019-03-22
方勤良
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there is a large amount of organic solvent used in the existing composite floor, which will cause considerable harm to the environment and the health of processing personnel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: Inorganic material composite floor, comprising the following components by weight: magnesium oxide, 30 parts, sawdust, 9.6 parts, fiber, 0.38 part, coastal saline soil, 5.6 parts, concrete slag, 2.2 parts, boric acid, 0.5 part, Pulp powder, 1.92 parts, magnesium sulfate solution, 46 parts, modifier, 0.57 parts, inorganic glue, 0.77 parts, reinforcing agent, 0.38 parts.

[0018] The coastal saline soil is dehydrated and ground at low temperature, the temperature of the low temperature dehydration is 8-12°C, the water content of the coastal saline soil after dehydration is less than or equal to 6%, and the mesh number of the coastal saline soil after grinding is greater than or equal to 400 mesh.

[0019] The concrete slag has been ground and its mesh size is greater than or equal to 300 mesh.

[0020] The inorganic glue is a solvent-free two-component polyurethane glue.

[0021] The concentration of the magnesium sulfate solution is 40%.

[0022] The fibe...

Embodiment 2

[0042] Embodiment 2: Inorganic material composite floor, comprising the following components by weight: magnesium oxide, 25 parts, sawdust, 6.6 parts, fiber, 0.2 part, coastal saline soil, 3.6 parts, concrete slag, 1.5 parts, boric acid, 0.3 part, Pulp powder, 1.5 parts, magnesium sulfate solution, 38 parts, modifier, 0.4 parts, inorganic glue, 0.6 parts, reinforcing agent, 0.2 parts.

[0043] The coastal saline soil is dehydrated and ground at low temperature, the temperature of the low temperature dehydration is 8-12°C, the water content of the coastal saline soil after dehydration is less than or equal to 6%, and the mesh number of the coastal saline soil after grinding is greater than or equal to 400 mesh.

[0044] The concrete slag has been ground and its mesh size is greater than or equal to 300 mesh.

[0045] The inorganic glue is a solvent-free two-component polyurethane glue.

[0046] The concentration of the magnesium sulfate solution is 40%.

[0047] The fiber is ...

Embodiment 3

[0067] Embodiment 3: Inorganic material composite floor, comprising the following components by weight: magnesium oxide, 35 parts, sawdust, 12.6 parts, fiber, 0.5 part, coastal saline soil, 7.6 parts, concrete slag, 2.9 parts, boric acid, 0.7 part, Pulp powder, 2.4 parts, magnesium sulfate solution, 54 parts, modifier, 0.7 parts, inorganic glue, 0.9 parts, reinforcing agent, 0.5 parts.

[0068] The coastal saline soil is dehydrated and ground at low temperature, the temperature of the low temperature dehydration is 8-12°C, the water content of the coastal saline soil after dehydration is less than or equal to 6%, and the mesh number of the coastal saline soil after grinding is greater than or equal to 400 mesh.

[0069] The concrete slag has been ground and its mesh size is greater than or equal to 300 mesh.

[0070] The inorganic glue is a solvent-free two-component polyurethane glue.

[0071] The concentration of the magnesium sulfate solution is 40%.

[0072] The fiber is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
flexural strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic material composite floor which is prepared from the following components in parts by weight: 25-35 parts of magnesium oxide, 6.6-12.6 parts of sawdust, 0.2-0.5 part of fiber, 3.6-7.6 parts of seashore saline soil, 1.5-2.9 parts of concrete slag, 0.3-0.7 part of boracic acid, 1.5-2.4 parts of pulp powder, 38-54 parts of a magnesium sulfate solution, 0.4-0.7 partof a modifier, 0.6-0.9 part of inorganic glue and 0.2-0.5 part of an enhancer. The inorganic material composite floor has the advantages of environmental protection and small harm on health of a processing person.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an inorganic material composite floor. Background technique [0002] With the continuous improvement of living standards, people's requirements for decorative materials are getting higher and higher. The application of plastics in the existing decorative panels still accounts for a large proportion, and the plastic composite floor will be harmful to the environment no matter in the manufacturing process or after it is scrapped. Causes certain pollution. Inorganic material composite flooring such as glass magnesium board is a board made of magnesium oxide, magnesium chloride and other magnesium gelling materials. It is a new type of building decoration material with low manufacturing cost and high environmental friendliness. , is a popular research direction of building materials at present. For the current glass magnesium sheet, for example, the patent application publ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B111/10C04B111/60
CPCC04B28/32C04B2111/1062C04B2111/60C04B2201/20C04B2201/50C04B18/26C04B14/361C04B18/16C04B22/0013C04B18/241C04B24/282C04B14/42C04B14/28C04B2103/54C04B14/22C04B18/144C04B18/0418C04B18/08C04B22/142C04B22/10
Inventor 方勤良
Owner 方勤良
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka