National batik cerate and preparation method thereof

A wax agent and national technology, applied in the field of ethnic batik wax agent and its preparation, can solve the problems of uneven waxing, poor permeability and low adhesion, and achieve uniform waxing, strong adhesion and good retention. Effect

Inactive Publication Date: 2019-03-26
福泉市筑梦服装有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of paraffin wax is relatively high, and it is easy to crack naturally when it is used for wax painting, and it will produce color lines during the dyeing process, but its adhesion is low, and it is easy to fall off during the dyeing process, resulting in black spots
Beeswax has good adhesion and is not easy to fall off, but its hardness is low, and it is difficult to naturally crack and produce color lines during the dyeing process. At the same time, it also has the problem of high cost
In view of the above problems, in the prior art, by simply mixing paraffin wax and beeswax, it can be naturally cracked while having good adhesion, but it still has problems such as poor permeability and uneven waxing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1. A national batik wax preparation, the wax is made of the following raw materials: 55kg of paraffin wax, 30kg of beeswax, 15kg of natron, 2.5kg of polyether modified silicone, 40kg of stearic acid, 2.5kg of polyethylene wax, and 15kg of triethanolamine .

[0018] The preparation method of the above-mentioned national batik wax agent is characterized in that: the method comprises the following steps;

[0019] A: Heat and melt paraffin wax, beeswax, natron, polyether-modified silicone and stearic acid respectively, and mix them uniformly to obtain product A;

[0020] B: Cool product A to room temperature to obtain product B;

[0021] C: Heat product B until completely melted, and stir for 15 minutes to obtain product C;

[0022] D: Add polyethylene wax and triethanolamine to product C, stir evenly to obtain product D;

[0023] E: Cool product D to room temperature, that is.

Embodiment 2

[0024] Example 2. A national batik wax preparation, the wax is made of raw materials: 50kg of paraffin wax, 20kg of beeswax, 10kg of natron, 2kg of polyether modified silicone, 30kg of stearic acid, 2kg of polyethylene wax, and 10kg of triethanolamine.

[0025] The preparation method of above-mentioned national batik wax agent, the method comprises the following steps;

[0026] A: Heat and melt paraffin wax, beeswax, natron, polyether-modified silicone and stearic acid respectively, and mix them uniformly to obtain product A;

[0027] B: Cool product A to room temperature to obtain product B;

[0028] C: Heat product B until completely melted, and stir for 15 minutes to obtain product C;

[0029] D: Add polyethylene wax and triethanolamine to product C, stir evenly to obtain product D;

[0030] E: Cool product D to room temperature, that is.

Embodiment 3

[0031] Example 3. A national batik wax preparation, the wax is made from the following raw materials: 60kg of paraffin wax, 40kg of beeswax, 20kg of natron, 3kg of polyether modified silicone, 50kg of stearic acid, 3kg of polyethylene wax, and 20kg of triethanolamine.

[0032] The preparation method of above-mentioned national batik wax agent, the method comprises the following steps;

[0033] A: Heat and melt paraffin wax, beeswax, natron, polyether-modified silicone and stearic acid respectively, and mix them uniformly to obtain product A;

[0034] B: Cool product A to room temperature to obtain product B;

[0035] C: Heat product B until completely melted, and stir for 15 minutes to obtain product C;

[0036] D: Add polyethylene wax and triethanolamine to product C, stir evenly to obtain product D;

[0037] E: Cool product D to room temperature, that is.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a national batik cerate and a preparation method thereof. The cerate is prepared from paraffin, beewax, sodium silicate, polyether modified organosilicon, stearic acid, polyethylene wax and triethanolamine. The national batik cerate is low in cost, good in permeating effect, strong in adhesive capacity, uniform in waxing, and unlikely to generate fracture and pigment figure.

Description

technical field [0001] The invention relates to a mixed wax, in particular to a national batik wax preparation and a preparation method thereof. Background technique [0002] Batik is an ancient folk traditional textile printing and dyeing handicraft of ethnic minorities in my country. It was called wax in ancient times. It is also known as the three major printing techniques in ancient my country together with twisting (tie-dyeing) and clipping (hollow printing). Guizhou, Yunnan Miao, Buyi and other ethnic groups are good at batik. Batik is to use a wax knife dipped in melted wax to draw flowers on the cloth and then dip them with indigo. After dyeing and removing the wax, the cloth surface will show various patterns of blue background white flowers or white background blue flowers. The natural wax of the wax cracks, making the cloth surface present a special "ice pattern", which is particularly attractive. Because batik has rich patterns, elegant tones and unique style, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/46D06P1/52D06P1/613D06P1/645D06P1/653D06P5/12
CPCD06P1/46D06P1/5221D06P1/613D06P1/645D06P1/6533D06P5/12
Inventor 袁方舟袁方均丁噹
Owner 福泉市筑梦服装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap