A kind of production method of hrb500e high-strength earthquake-resistant steel bar

A technology of anti-seismic steel bar and production method, which is applied in the field of metallurgical steelmaking and processing, can solve the problems of insufficient heating capacity of a heating furnace, reduced production efficiency of a rolling heating furnace, and reduced production efficiency, and achieves great energy saving, consumption reduction, economic benefits and variety and quality. Benefit, ensure the strength and yield ratio index and mechanical properties stability, reduce the effect of processing cost and alloy cost

Active Publication Date: 2020-07-28
SHANDONG SHIHENG SPECIAL STEEL GROUP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, there are currently the following main problems: 1. The rolling start temperature needs to be above 1070°C, and the heating capacity of the conventional heating furnace is insufficient. In order to increase the furnace temperature, sufficient heating is required, which inevitably reduces the production speed. This effect alone will cause a reduction in production efficiency 20-30%, and it will also cause large power consumption and coal consumption indicators. For example, the blast furnace gas consumption per ton of steel will be 500m 3 left and right, increasing rolling costs
Due to the high content of V elements, the steel rolling furnace still needs to heat the billet to above 1050°C to realize the solid solution of V elements in the steel, so as to effectively exert the precipitation strengthening of V and N elements on the steel in the subsequent rolling and cooling process , Fine grain strengthening effect, therefore, the steel rolling process is forced to adopt a high-temperature heating temperature system different from ordinary HRB400 and HRB400E, resulting in a reduction in production efficiency and an increase in energy consumption of the steel rolling heating furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Methods for producing HRB500E high-strength seismic steel bars include:

[0060] Making billets, its components are: C: 0.20-0.25%, Si: 0.40-0.70%, Mn: 1.30-1.60%, P≤0.045%, S≤0.045%, V: 0.040-0.050%, N: 0.0080- 0.0120%, the rest is Fe and unavoidable impurities;

[0061] Put the steel billet into the heating furnace, the temperature of the furnace is 1100°C, and it is heated to 950°C, and the heating time is ≥1.5 hours before it is released from the furnace;

[0062] After rough rolling, intermediate rolling, and pre-finish rolling, the steel billet is subjected to controlled rolling water cooling, and the rolled piece passes through a 3-meter controlled rolling cooling section and a 30-meter controlled rolling recovery section; the water pressure in the controlled rolling water-piercing section is controlled at 0.40MPa ;The temperature of the rolled piece after the controlled rolling recovery section is 975°C; after cooling, the rolled piece after the surface tempera...

Embodiment 2

[0084] Methods for producing HRB500E high-strength seismic steel bars include:

[0085] Making billets, its components are: C: 0.20-0.25%, Si: 0.40-0.70%, Mn: 1.30-1.60%, P≤0.045%, S≤0.045%, V: 0.020-0.030%, N: 0.0050- 0.0080%, the rest is Fe and unavoidable impurities;

[0086] Put the billet into the heating furnace, the temperature of the furnace is 1060°C, heat it to 910°C, and leave the furnace after the heating time is ≥1.5 hours;

[0087] After rough rolling, intermediate rolling and pre-finish rolling, the steel billet is subjected to controlled rolling water cooling, and the rolled piece passes through a 6-meter controlled rolling cooling section and a 60-meter controlled rolling recovery section; the water pressure in the controlled rolling water section is controlled at 0.40MPa ;The temperature of the rolled piece after the controlled rolling recovery section is 925°C; after cooling, the rolled piece after the surface temperature recovery is carried out for finish ro...

Embodiment 3

[0107] Methods for producing HRB500E high-strength seismic steel bars include:

[0108] Making billets, its components are: C: 0.20-0.25%, Si: 0.40-0.70%, Mn: 1.30-1.60%, P≤0.045%, S≤0.045%, V: 0.032-0.040%, N: 0.0070- 0.010%, the rest is Fe and unavoidable impurities;

[0109] Put the steel billet into the heating furnace, the furnace temperature is 1080°C, heat it to 940°C, and leave the furnace after the heating time is ≥1.5 hours;

[0110] After rough rolling, intermediate rolling and pre-finish rolling, the steel billet is subjected to controlled rolling water cooling, and the rolled piece passes through the 4m controlled rolling cooling section and the 45m controlled rolling recovery section; the water pressure in the controlled rolling water section is controlled at 0.40MPa ;The temperature of the rolled piece after the controlled rolling recovery section is 960°C; after cooling, the rolled piece after the surface temperature recovery is carried out for finish rolling;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a production method of HRB500E high-strength anti-seismic steel bar, comprising the following steps: making a steel billet, the components of which are: C: 0.20-0.25%, Si: 0.40-0.70%, Mn: 1.30-1.60%, P≤0.045 %, S≤0.045%, V: 0.020‑0.050%, N: 0.0050‑0.0120%, and the rest are Fe and unavoidable impurities; Multi-grade steel: that is, the same chemical composition formula, by adjusting the rolling process, can produce both HRB500E and HRB400E. Therefore, a unified production process can be adopted when preparing raw materials and blanks, which is beneficial to improve production efficiency, and reduces the frequency of adjusting preparation parameters such as temperature and component ratio, improves product stability, and is conducive to improving production efficiency.

Description

technical field [0001] The invention relates to the technical field of metallurgical steelmaking and processing, in particular to a production method of HRB500E high-strength anti-seismic steel bars. Background technique [0002] The volume of concrete used in construction projects in my country is huge every year, and a large amount of steel is consumed. Except for a small amount of prestressed steel wire strands, most of them are steel bars used in concrete. There are three grades of hot-rolled ribbed steel bars in my country: HRB335, HRB400 and HRB500. H, R, and B represent hot rolled (Hot rolled), ribbed (Ribbled), and steel bars (bars), respectively, and 335, 400, and 500 represent steel bars, respectively. The minimum yield strength, the unit is MPa. The higher the grade of the steel bar, the better the quality, and the strength, toughness and elongation will be enhanced accordingly. The promotion of high-strength steel bars will undoubtedly help reduce the amount of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/60C21D8/08
CPCC21D8/08C22C38/02C22C38/04C22C38/12C22C38/60
Inventor 王长生肖立军张忠峰张红雁马庆水张晓军邓兆征袁成玺赵衍芳
Owner SHANDONG SHIHENG SPECIAL STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com