Preparation method of organic-inorganic composite adhesive

An inorganic composite and adhesive technology, applied in the field of building decoration materials, can solve problems such as easy falling off, and achieve the effects of low curing temperature, simple and convenient processing technology, and high adhesion strength

Inactive Publication Date: 2019-04-12
ZIGONG INNOVATION CENT OF ZHEJIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But bonding these particles to the substrate (stone, metal, cement, etc.) requires a suitable adhesive, otherwise it is easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of organic-inorganic composite adhesive
  • Preparation method of organic-inorganic composite adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be further described in detail below in conjunction with specific embodiments. The examples can enable those skilled in the art to understand the present invention more comprehensively, but do not limit the present invention in any way.

[0017] The preparation method of organic-inorganic composite adhesive in the present invention comprises the following steps:

[0018] (1) Under stirring at 300r / min, add 10-20 mass parts of orthosilicate and 20-30 mass parts of long-chain silane coupling agent to 20 mass parts of ethanol and 20 mass parts of isopropanol In the mixed solution, after mixing evenly, use concentrated hydrochloric acid to adjust the pH value of the solution between 1 and 2;

[0019] (2) Under stirring at 200-300 r / min, add 5-10 parts by mass of deionized water into the mixed solution obtained in step (1), and react at 40-60° C. for 6-8 hours;

[0020] (3) Add 10-15 parts by mass of six-functional UV resin to the product obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of building decoration materials, and aims to provide a preparation method of an organic-inorganic composite adhesive. The method comprises the following steps: adding tetraethyl orthosilicate and a silane coupling agent with a long chain into a mixed solution of ethanol and isopropyl alcohol under stirring, performing uniform mixing, and adjusting the pH of thesolution to 1-2 by using concentrated hydrochloric acid; adding deionized water into the mixed solution under stirring, and performing a reaction for 6-8 h at 40-60 DEG C; and adding hexafunctional UVresin into the obtained product, performing uniform mixing to obtain the organic-inorganic composite adhesive. According to the preparation method provided by the invention, the organic-inorganic composite adhesive prepared by the method has a low curing temperature and a simple and convenient processing technology, and inorganic particles have high adhesion strength on a substrate, and accidentscaused by fall are not easy to have.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a preparation method of an organic-inorganic composite adhesive. Background technique [0002] With the development of the economy, people's demand for decorative building materials with novel and beautiful appearance is increasing. Inorganic waste particle materials such as glass particles and ceramic particles are decorated on the glass to have a novel appearance, and at the same time, the raw material cost is low. But bonding these particles to the base material (stone, metal, cement, etc.) requires a suitable adhesive, otherwise it is easy to fall off. The invention prepares an organic-inorganic composite adhesive for bonding glass particles, and coats it on the surface of building flat glass to obtain a glass plate with a decorative function. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/07C09D183/06C09D183/08C09D1/00C09D175/14C09D7/61
CPCC09D1/00C09D7/61C09D175/14C09D183/04C09D183/06C09D183/08C08K3/013
Inventor 杨辉吴春春张玲洁
Owner ZIGONG INNOVATION CENT OF ZHEJIANG UNIV
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com