Plasma plasma polishing salt for silver and preparation method thereof

A plasma polishing and plasma technology, which is applied in the field of polishing salt, can solve the problems of unsatisfactory and meticulous surface roughness, low use value, complicated preparation process, etc., and achieves simple and affordable preparation of raw materials, ideal surface roughness, and preparation technology. simple effect

Inactive Publication Date: 2019-04-23
东莞市金林自动化机械科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The surface roughness of silver polishing salts on the existing market is not ideal and meticulous after polishing, and manual cleaning is required, which brings inconvenience to people's use, and the preparation process is complicated, the use value is not high, and the preparation raw materials are complicated Expensive, lower performance and less generalizable in peer field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The technical scheme adopted in this specific embodiment is: a kind of plasma plasma polishing salt for silver, which comprises the following raw materials in parts by weight: 75 parts of ammonium sulfate, 15 parts of sodium citrate, 5 parts of glucose, 5 parts of citric acid , 750 parts of water.

[0021] A kind of plasma plasma polishing salt polishing salt preparation method for silver, comprises the following steps:

[0022] Step 1: Take water, ammonium sulfate, sodium citrate, citric acid, and glucose in parts by weight respectively, add the water into a transparent glass container, then add ammonium sulfate, and fully stir with a stirring rod to obtain the first mixed solution;

[0023] Step 2. Heat the first mixed solution in step 1 to 55-75 degrees Celsius, then add sodium citrate and citric acid in turn, and stir for 0.2-0.4 hours to obtain the second mixed solution;

[0024] Step 3, taking out the second mixed solution in step 2, lowering the temperature to 2...

Embodiment 2

[0033] The difference between this example and Example 1 is that it contains the following raw materials in parts by weight: 76 parts of ammonium sulfate, 16 parts of sodium citrate, 6 parts of glucose, 6 parts of citric acid, and 760 parts of water. Other raw material composition, formula technology are all identical with embodiment 1.

Embodiment 3

[0035] The difference between this example and Example 1 is that it contains the following raw materials in parts by weight: 77 parts of ammonium sulfate, 17 parts of sodium citrate, 7 parts of glucose, 7 parts of citric acid, and 770 parts of water. Other raw material composition, formula technology are all identical with embodiment 1.

[0036] After adopting the above technical solution, the beneficial effects of the present invention are: the surface roughness after polishing is ideal and fine, no manual cleaning is required, which brings convenience to people's use, and the preparation process is simple, the use value is high, and the preparation raw materials are simple and affordable. It has superior performance and strong promotion in the field of peers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses plasma plasma polishing salt for silver and a preparation method thereof, and relate to the technical field of polishing salt. The polishing salt for silver is prepared from the following materials: ammonium sulfate, sodium citrate, glucose, citric acid and water. The raw materials are processed according to a weight ratio through the polishing salt preparation method for silver and the preparation is accomplished. After adopting the technical solution, the beneficial effects of the polishing slat are that polished surfaces have ideal roughness and are meticulous; no manual cleaning is needed; the use for people is convenient; the preparation process is simple; the use value is high; the raw materials for preparation are simple and affordable; and the polishing salthas excellent performance and high promotion in the field of peers.

Description

technical field [0001] The invention relates to the technical field of polishing salt, in particular to a plasma polishing salt for silver and a preparation method thereof. Background technique [0002] Silver (Argentum) is a transition metal. Chemical symbol Ag. Silver is one of the metals known and used in ancient times, and it is an important precious metal. Silver exists as a single substance in nature, but most of it exists in silver ore in the form of a compound state. The physical and chemical properties of silver are relatively stable, with good thermal and electrical conductivity, soft quality and rich ductility. Its reflective rate is extremely high, which can reach more than 99%. There are many important uses. [0003] Polishing refers to the use of mechanical, chemical or electrochemical effects to reduce the surface roughness of the workpiece to obtain a bright and smooth surface. It is a modification of the surface of the workpiece using polishing tools an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/06
CPCC23F3/06
Inventor 田斐田晋彭浩林
Owner 东莞市金林自动化机械科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com