Automobile engine protective agent and preparation method thereof

A technology of automobile engine and protective agent, which is applied in the direction of additives, petroleum industry, lubricating composition, etc. It can solve the problems of poor bending precision and complex structure, and achieve the goal of improving service life, prolonging oil change interval, and reducing hard impact Effect

Pending Publication Date: 2019-05-07
青岛康普顿石油化工有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem of complex structure of sheet metal bending device in the prior art and poor b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automobile engine protective agent and preparation method thereof
  • Automobile engine protective agent and preparation method thereof
  • Automobile engine protective agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of embodiment 1 automobile engine protective agent

[0027] S 1 1. Heat 70 parts by weight of paraffinic base oil to 50°C, continue to heat up 4.5 parts by weight of base oil to 110-130°C, keep the remaining 65.5 parts by weight of base oil at 50°C, add 0.5 parts by weight of thickener into the 110°C base oil, stirred and dissolved, then cooled to 50°C, and finally stirred and mixed with the remaining 65.5 parts by weight of the heat-insulating base oil to obtain a base mixed oil;

[0028] S 2 , with 1 part by weight of phenolic antioxidant, 1 part by weight of dispersant dialkyl dithiophosphate, 1 part by weight of friction reducer molybdenum dialkyl dithiocarbamate and glyceryl monooleate, 0.1 part by weight The pour point depressant polymethacrylate is gradually added to the base mixed oil, stirred for 1 hour, and mixed evenly;

[0029] S 3 , Cool down to 40°C, and after sampling and testing pass, filter and fill to obtain the finished prot...

Embodiment 2

[0031] The preparation method of embodiment 2 automobile engine protective agent

[0032] S 1 1. Raise the temperature of 90 parts by weight of base oil polyalphaolefin oil and ester oil polyol ester to 60°C, continue to heat up 9 parts by weight of base oil to 130°C, keep the remaining 81 parts by weight of base oil at 60°C, and heat 1 A thickener in parts by weight is added to the base oil at 130°C, stirred and dissolved, then cooled to 60°C, and finally mixed with the remaining 81 parts by weight of the heat-insulating base oil to obtain a base mixed oil;

[0033] S 2 , with 5 parts by weight of amine antioxidant, 5 parts by weight of dispersant dialkyl dithiophosphate, 5 parts by weight of friction reducer dialkyl molybdenum dithiophosphate and borate, 0.8 parts by weight of pour point depressant The polyalphaolefin is gradually added to the base mixed oil, stirred for 1 hour, and mixed evenly;

[0034] S 3 , Cool down to 45°C, and after sampling and testing pass, filt...

Embodiment 3

[0036] The preparation method of embodiment 3 automobile engine protective agent

[0037] S 1 1. Heat up 80 parts by weight of base oil polyester and polyol ester to 55°C, continue to heat up 6.3 parts by weight of base oil to 120°C, keep the remaining 73.7 parts by weight of base oil at 55°C, add 0.7 parts by weight of The thickener was added to the 120°C base oil, stirred and dissolved, then cooled to 55°C, and finally mixed with the remaining 73.7 parts by weight of the heat-insulating base oil to obtain a base mixed oil;

[0038] S 2 , with 3 parts by weight of phenolic antioxidant, 3 parts by weight of dispersant dialkyl dithiophosphate, 3 parts by weight of friction reducer molybdenum dialkyldithiophosphate and glyceryl monooleate, 0.45 parts by weight of The coagulant polymethacrylate is gradually added to the basic mixture, stirred for 1 hour, and mixed evenly;

[0039] S 3 , Cool down to 42°C, and after sampling and testing pass, filter and fill to obtain the fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of automobile engine lubricating protective agents, discloses an automobile engine protective agent, a preparation method thereof. The protective agent comprises thefollowing components in parts by weight: 70-90 parts of base oil, 0.5-1 part of a thickening agent, 1-5 parts of an antioxidant, 1-5 parts of a dispersing agent, 1-5 parts of a friction reducing agent and 0.1-0.8 part of a pour point depressant, the friction reducing agent is a mixture of an organic molybdenum compound and an ester compound, wherein the organic molybdenum compound is molybdenum dialkyldithiocarbamate or molybdenum dialkyldithiophosphate, the ester compound is glyceryl monooleate or boric acid ester. The protective agent has an excellent friction reducing effect and has an unexpected effect of repairing existing abrasive spots, hard impact during cold start can be effectively reduced, raw materials are easy to purchase, and the process is relatively simple.

Description

technical field [0001] The invention relates to an automobile engine lubricating and protecting agent, in particular to an automobile engine protecting agent and a preparation method. Background technique [0002] With the development of the international automobile industry, the requirements for the protection of the engine are becoming higher and higher, and the lubricating oil for the engine will develop in the direction of low viscosity with the development of the engine. Due to the increasingly stringent environmental protection regulations, It has brought more and more pressure to automobile manufacturers and lubricating oil producers. Extending the service life of the engine has become one of the direct driving forces to promote the improvement of engine technology and the upgrading of lubricating oil. Among them, the wear and tear caused by friction is the engine scrapped One of the main forms is to control and reduce the wear and tear of automobile engines, which ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/06C10M169/00C10M141/08C10M141/10C10M141/12C10N30/06C10N40/25
Inventor 朱磊韩军英蒋威宋义阳
Owner 青岛康普顿石油化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap