Rapid formation method of lead storage battery

A formation method and lead storage battery technology, applied in the field of storage batteries, can solve the problems of long formation time and high energy consumption, and achieve the effects of short formation time, low energy consumption and saving charging time.

Active Publication Date: 2019-05-14
TIANNENG BATTERY GROUP
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a rapid formation method for lead-acid batteries to solve the problems of long formation time and high energy consumption in the existing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid formation method of lead storage battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] 12Ah battery

[0046] 1. The battery to be formed is automatically acid-added by a vacuum acid-adding machine, the density of the added sulfuric acid solution is 1.265 / ml, and the temperature is 12°C. Then stand in cooling water at 20°C for 0.5h to lower the internal temperature of the battery and at the same time allow the sulfuric acid electrolyte to permeate the plate.

[0047] 2. Place the battery in a constant temperature water bath at 33°C and let it stand for 20 minutes. After standing still, the internal temperature of the battery is more uniform, and the consistency of subsequent formation is better.

[0048] 3. Formation

[0049] a. The first charging and discharging: the charging current adopts the method of gradient increase and then gradient decrease. Then discharge with a large current until the voltage of the battery cell is lower than the specified value.

[0050] 0.08C current charging for 1h, 0.15C current charging for 2h, 0.25C current charging fo...

Embodiment 2

[0058] 20AH battery

[0059] 1. The battery to be formed is automatically acid-added by a vacuum acid-adding machine, the density of the added sulfuric acid solution is 1.255g / ml, and the temperature is 5°C. Then stand in 10°C cooling water for 1.0h to lower the internal temperature of the battery and at the same time make the sulfuric acid electrolyte soak into the plate.

[0060] 2. Place the battery in a constant temperature water bath at 35°C and let it stand for 30 minutes. After standing still, the internal temperature of the battery is more uniform, and the consistency of subsequent formation is better.

[0061] 3. Formation

[0062] a. The first charging and discharging: the charging current adopts the method of gradient increase and then gradient decrease. Then discharge with a large current until the voltage of the battery cell is lower than the specified value.

[0063] 0.08C current charging for 2 hours, 0.15C current charging for 2.5 hours, 0.25C current charg...

Embodiment 3

[0071] 12Ah battery

[0072] 1. The battery to be formed is automatically acid-added by a vacuum acid-adding machine, the density of the added sulfuric acid solution is 1.240g / ml, and the temperature is 15°C. Then stand in 10°C cooling water for 0.5h to lower the internal temperature of the battery and at the same time make the sulfuric acid electrolyte soak into the plate.

[0073] 2. Place the battery in a constant temperature water bath at 38°C and let it stand for 30 minutes. After standing still, the internal temperature of the battery is more uniform, and the consistency of subsequent formation is better.

[0074] 3. Formation

[0075] a. The first charging and discharging: the charging current adopts the method of gradient increase and then gradient decrease. Then discharge with a large current until the voltage of the battery cell is lower than the specified value.

[0076] 0.08C current charging for 1h, 0.15C current charging for 2h, 0.25C current charging for 5h,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rapid formation method of a lead storage battery, and belongs to the technical field of storage batteries. The rapid formation method of the lead storage battery includes thesteps: firstly, a to-be-formed battery after adding acid is put in a thermostatic waterbath for formation,thencharged to a gassing potential in a small current gradient increasing way in the initialstage of formation and then charged in a current gradient decreasing way, and polarization is reduced; in the intermediate stage of formation, firstly, charging is conducted to the gassing potential through a large current and then conducted in a gradient decreasing way, conversion of active substances is quickly achieved, and the charging time is saved; and when polarization is large, the currentdischarge is used for discharging, depolarization is achieved, the battery charge receptivity is improved, time consumption of the stage is reduced, and the production efficiency is improved. According to the rapid formation method of the lead storage battery, through process adjustment, the water loss of a battery electrolyte is reduced, the change of the acid density is little, polar plates arerapidly converted into the active substances at the low acid density, the low acid density forms alpha-PbO2 advantageously, and the service life of the battery is prolonged advantageously.

Description

technical field [0001] The invention relates to the technical field of storage batteries, in particular to a rapid formation method for lead storage batteries. Background technique [0002] Formation is one of the key processes in the manufacture of lead-acid batteries. Formation is to charge and discharge the battery under certain conditions, and convert the inactive positive electrode active material into active material. Through chemical formation, not only can the polar plate generate a material with higher activity, but also make the obtained active material have an appropriate microstructure, so that there is better contact between the crystals, so as to ensure that the polar plate has high specificity and long life. Charge and discharge life, thereby improving the battery's charge and discharge performance, self-discharge, storage and other comprehensive performance. [0003] At present, lead-acid batteries mainly adopt the internal formation method, and the internal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/12
CPCY02E60/10Y02P70/50
Inventor 李进兴张开红姚秋实李鹏苏绍祥代飞汤序锋
Owner TIANNENG BATTERY GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap