A scale-removing and anti-scaling alloy, a scale remover and a preparation method thereof

A descaler and alloy technology, applied in the field of alloys, can solve problems that are contrary to environmental protection and sustainable development, and have not been well resolved.

Inactive Publication Date: 2021-08-20
武汉众胜斯特科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

People use water for industrial production so far and the scaling problem has not been well solved
Although the traditional chemical method has good scale inhibition effect, it is contrary to the requirements of environmental protection and sustainable development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A scale-removing and anti-scaling alloy, a scale remover and a preparation method thereof
  • A scale-removing and anti-scaling alloy, a scale remover and a preparation method thereof
  • A scale-removing and anti-scaling alloy, a scale remover and a preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1: Descaling and anti-scaling alloy

[0048] 1. In terms of mass percentage, the scale-removing and anti-scaling alloy of the present embodiment is composed of the following components:

[0049] Copper 73.54%, nickel 7.58%, tin 1.66%, zinc 10.63%, lead 6.59%.

[0050] 2. A descaling device made of the descaling and anti-scaling alloy.

[0051] 3, the preparation method of described scale remover comprises the steps:

[0052] Step 1. According to the different melting points of various metals, first put nickel and copper into the furnace in proportion to heat to 1350°C-1380°C to fully melt and mix nickel and copper, and then lower the temperature to 800°C to put tin and lead Put it in and melt it, keep it for 3 minutes after the tin and lead are fully melted, then add zinc and stir to melt;

[0053] Step 2. After the zinc is melted, the temperature is raised to 1250°C to start pouring;

[0054] Step 3: The poured and molded material is then lathe processed...

Embodiment 2

[0055] Embodiment 2: Scale-removing and anti-scaling alloy

[0056] 1. In terms of mass percentage, the scale-removing and anti-scaling alloy of the present embodiment is composed of the following components:

[0057] Copper 71%, nickel 6%, tin 0.5%, zinc 12.5%, lead 10%.

[0058] 2. A descaling device made of the descaling and anti-scaling alloy.

[0059] 3, the preparation method of described scale remover comprises the steps:

[0060] Step 1. According to the different melting points of various metals, first put nickel and copper into the furnace in proportion to heat to 1350°C-1380°C to fully melt and mix nickel and copper, and then lower the temperature to 800°C to put tin and lead Put it in and melt it, keep it for 3 minutes after the tin and lead are fully melted, then add zinc and stir to melt;

[0061] Step 2. After the zinc is melted, the temperature is raised to 1250°C to start pouring;

[0062] Step 3: The poured and molded material is then lathe processed, sli...

Embodiment 3

[0063] Embodiment 3: Scale-removing and anti-scaling alloy

[0064] 1. In terms of mass percentage, the scale-removing and anti-scaling alloy of the present embodiment is composed of the following components:

[0065] Copper 75%, nickel 10%, tin 3%, zinc 5%, lead 7%.

[0066] 2. A descaling device made of the descaling and anti-scaling alloy.

[0067] 3, the preparation method of described scale remover comprises the steps:

[0068] Step 1. According to the different melting points of various metals, first put nickel and copper into the furnace in proportion to heat to 1350°C-1380°C to fully melt and mix nickel and copper, and then lower the temperature to 800°C to put tin and lead Put it in and melt it, keep it for 3 minutes after the tin and lead are fully melted, then add zinc and stir to melt;

[0069] Step 2. After the zinc is melted, the temperature is raised to 1250°C to start pouring;

[0070] Step 3: The poured and molded material is then lathe processed, sliced ​​a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
scale inhibition rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a scale-removing and anti-scaling alloy, which comprises the following raw material components in terms of mass percentage: 71%-75% of copper, 6%-10% of nickel, 0.5%-3% of tin, and 5%-15% of zinc , lead 6.5%~10%; The present invention also discloses the descaling device and preparation method that adopts said descaling and antiscaling alloy to make; Combining the above 5 elements to conduct electric The chemical action makes the electron transfer of various ions, separates and becomes a single molecular crystal, which exists independently in the water, plays the role of anti-scaling, has good effect of descaling, and the anti-scaling rate is as high as 97.37%, which improves the production efficiency and reduces the pollution emission is reduced, and the service life of the equipment is prolonged; on average, a heat exchange equipment installed with the scale inhibitor of the present invention will save gas costs (552965+238041) ÷ 2 = 395503 yuan in one year, and the catalyst of this alloy material The lifespan is very long, so it is more economical for continuous use.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a scale-removing and anti-scaling alloy, a scale remover and a preparation method thereof. Background technique [0002] At present, during the rapid development of the industrial revolution, the fouling problem in the heat exchange process has caused confusion for enterprises. People use water for industrial production so far and the scaling problem has not been well resolved. The development of water treatment equipment has also been ever-changing, and the effect of water treatment equipment has not met the long-term production needs of enterprises. In the production of the enterprise, the production efficiency is low and the energy consumption is increased due to the fouling of the circulating water. [0003] The industrial circulating cooling water system is an essential part of industrial production equipment. With the operation of the system, scale will be formed on the he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/04C22C9/06C22C9/08C22C1/02C02F5/00
Inventor 李书召
Owner 武汉众胜斯特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap