Manufacturing method of rustproof alloy wheel hub

A manufacturing method and technology of wheel hubs, which are applied in the direction of surface coating liquid devices, spraying devices, coatings, etc., can solve the problems of muddy water, single-targeted, unsatisfactory anti-corrosion and anti-rust effects, etc., and achieve improvement effect of effect

Active Publication Date: 2019-05-24
ZHEJIANG PDW IND CO LTD
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The wheels of automobiles are not only directly exposed to the air during daily use, but also often covered with muddy water. Corrosive chemical components may be carried in muddy water, and it is very easy to rust if it is not cleaned f...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1, a method for manufacturing an anti-rust alloy wheel hub, comprising the following steps:

[0032] A. Heat the aluminum alloy material to a liquid state at a temperature of 700°C, and add monoclinic zirconia with a particle size of 8nm to the aluminum alloy solution, and stir evenly. The mass ratio of the aluminum alloy material to zirconia is 70:1 ;

[0033] B. Inject the solution obtained in step A into the wheel hub mold and perform secondary cooling. The first cooling temperature is 665° C., and the second cooling temperature is room temperature. The cooling time of the aluminum alloy solution to the first cooling temperature is 0.5 minutes, and Stay at the first cooling temperature for 4 minutes; the cooling time of the aluminum alloy solution from the first cooling temperature to the second cooling temperature is 2 minutes;

[0034] Among them, the second cooling of the aluminum alloy solution adopts the method of water cooling and quenching first an...

Embodiment 2

[0038] Embodiment 2, a method for manufacturing an antirust alloy wheel hub, comprising the following steps:

[0039] A. Heat the aluminum alloy material to a liquid state at a temperature of 730°C, and add monoclinic zirconia with a particle size of 10nm to the aluminum alloy solution, and stir evenly. The mass ratio of aluminum alloy material to zirconia is 80:1 ;

[0040] B. Inject the solution obtained in step A into the wheel hub mold and perform secondary cooling. The first cooling temperature is 670° C., and the second cooling temperature is room temperature. The cooling time for the aluminum alloy solution to the first cooling temperature is 1 minute, and Stay at the first cooling temperature for 5 minutes; the cooling time of the aluminum alloy solution from the first cooling temperature to the second cooling temperature is 3.5 minutes;

[0041] Among them, the second cooling of the aluminum alloy solution adopts the method of water cooling and quenching first and th...

Embodiment 3

[0045] Embodiment 3, a method for manufacturing an antirust alloy wheel hub, comprising the following steps:

[0046] A. Heat the aluminum alloy material to a liquid state, the heating temperature is 710°C, and add monoclinic zirconia with a particle size of 9.5nm to the aluminum alloy solution, and stir evenly. The mass ratio of the aluminum alloy material to the zirconia is 75: 1;

[0047] B. Inject the solution obtained in step A into the wheel hub mold and perform secondary cooling. The first cooling temperature is 668° C., and the second cooling temperature is room temperature. The cooling time for cooling the aluminum alloy solution to the first cooling temperature is 0.8 minutes, and Stay at the first cooling temperature for 4.5 minutes; the cooling time of the aluminum alloy solution from the first cooling temperature to the second cooling temperature is 3 minutes;

[0048]Among them, the second cooling of the aluminum alloy solution adopts the method of water cooling...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of auto parts, and particularly relates to a manufacturing method of a rustproof alloy wheel hub. The manufacturing method of the rustproof alloy wheel hubcomprises the following steps that A, an aluminum alloy material is heated to a liquid state, zirconium oxide is added into an aluminum alloy solution, and even stirring is conducted; B, a solution obtained in the step A is injected into a wheel hub mold for two passes of cooling, the temperature in the first pass of cooling is 665 DEG C to 670 DEG C, and the temperature in the second pass of cooling is the room temperature; C, a cooling-formed semi-finished wheel hub is separated from the mold, the outer side of the semi-finished wheel hub faces downwards, half immersed in wax film rustproofoil liquid for a period of time and then taken out for still standing; D, the inner side of the semi-finished wheel hub obtained in the step C is sprayed with rustproof liquid; and E, the semi-finished wheel hub obtained in the step D is subjected to overall film coating through activated carbon, and thus a finished wheel hub is obtained. The wheel hub manufactured through the manufacturing method is resistant to the high temperature and corrosion, can resist corrosion of various corrosive substances of gas, liquid and solid, and is not prone to rusting.

Description

technical field [0001] The invention belongs to the technical field of auto parts, in particular to a method for manufacturing an antirust alloy wheel hub. Background technique [0002] The wheels of automobiles are not only directly exposed to the air during daily use, but also often covered with muddy water. The muddy water may carry corrosive chemical components, and it is very easy to rust if it is not cleaned frequently. [0003] Existing hubs are usually strengthened and anti-rust for some components in the hub, such as the technical content disclosed in Chinese patent CN207212894U: a kind of anti-corrosion and anti-rust hub bolts, including a hub bolt body, one end of the hub bolt body is provided with a bolt head The other end is provided with a bolt tail, the surface of the bolt head is provided with a hub bolt stainless steel cap, and the bolt head and the hub bolt stainless steel cap are punched and riveted by a punching machine, and the lower edge of the bolt he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/10C22C1/02C22C1/10B22D27/04B05C3/10B05B13/06
Inventor 颜胜元纪刚熊军明汤荣波任滔
Owner ZHEJIANG PDW IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap