Crack-sealer for wall surface tiles

A technology for jointing agent and ceramic tile, which is applied in the field of jointing agent, can solve the problems of efflorescence, unsightly surface, weak adhesion and other problems on the surface of building joints, and achieves the advantages of inhibiting the phenomenon of efflorescence, improving flexibility and increasing viscosity. Effect

Inactive Publication Date: 2019-05-28
蔡京翠
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains a lot of free calcium hydroxide, it can cause the surface of the building joint to be blotted with alkali, and there will be an unsightly phenomenon; in addition, the existing jointing agent cannot Effectively prevent the erosion of microorganisms such as mold and algae; the joint agent has poor flexibility, weak adhesion, low water resistance and impermeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] In order to make the object, technical solution and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the examples. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0008] A jointing agent for wall tiles, including the following components: 20 parts of 32.5 white cement; 40 parts of 400-mesh heavy calcium powder; 0.84 parts of 1# colloidal crystal; 2 parts of high-activity silicon dioxide; 3 parts; 3 parts of adsorbent; 4 parts of 108 glue, 5 parts of curing agent.

[0009] The present invention can significantly reduce the content of free calcium hydroxide in the cement mortar material due to the addition of highly active silicon dioxide in the jointing agent, thereby inhibiting the occurrence of efflorescence on the surface of the cement mortar; due to the addition of the bactericide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a crack-sealer for wall surface tiles. The crack-sealer comprises the following ingredients: 10-20 parts of 32.5 white cement, 20-40 parts of 400-mesh heavy calcium powder, 0.42-0.84 part of No.1 colloidal crystal, 1-2 parts of high-activity silicon dioxide, 1-2 parts of a sterilizing agent, 1-3 parts of an adsorbing agent, 2-4 parts of 108 glue and 1-5 parts of a curing agent. The crack-sealer can effectively prevent the erosion of microorganisms such as mold and algae, is strong in adhesive strength, and has the characteristics of simple ingredients and low cost.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a grouting agent for wall tiles. Background technique [0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains a lot of free calcium hydroxide, it may cause the surface of the building joint to be blotted with alkali, and there will be an unsightly phenomenon; in addition, the existing jointing agent cannot Effectively prevent the erosion of microorganisms such as mold and algae; the jointing agent has poor flexibility, weak adhesion, low water resistance and impermeability. Contents of the invention [0003] The object of the present invention is to provide a grouting agent for wall tiles in order to overcome the deficiencies of the prior art. [0004] The present invention is realized through the following technical solutions: [0005] A jointing agent for wall tiles, including the following components: 10-2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B111/20C04B111/27
Inventor 蔡京翠
Owner 蔡京翠