Manufacturing process of dismountable-mountable type mobile house composite board

A mobile house and manufacturing process technology, applied in lamination devices, building structures, synthetic resin layered products, etc., can solve the problems of being unable to replace tents, etc., and achieve excellent fire resistance, fast assembly, and light weight

Inactive Publication Date: 2019-06-11
ANHUI MAX TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of partition wall still cannot replace tents, build barracks, and be used in the construction of field work barracks such as exploration, exploration, rescue and disaster relief, and the assembly of RVs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of dismountable-mountable type mobile house composite board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A manufacturing process of dismountable mobile house composite board adopts the following steps:

[0026] (1) Aluminum alloy outer frame production: cut and weld aluminum alloy profiles to form an outer frame structure, reserve and install riveting fasteners and installation plug-ins at designated positions on the side;

[0027] (2) Honeycomb phenolic foaming: cut the honeycomb structure of the corresponding size and thickness according to the inner diameter of the aluminum alloy frame. In this embodiment, an aluminum honeycomb is used. The honeycomb structure is filled with phenolic foaming technology. The phenolic foam used is as follows Ingredients and parts by weight of raw materials are prepared: phenolic resin 800, curing agent 160, foaming agent 80, foam stabilizer 16, wherein the phenolic resin is a thermosetting foamable phenolic resin, the viscosity of the resin is controlled at 500cps, and the curing agent is An ester curing agent prepared by pre-reaction of tolue...

Embodiment 2

[0030] A manufacturing process of dismountable mobile house composite board adopts the following steps:

[0031] (1) Aluminum alloy outer frame production: cut and weld aluminum alloy profiles to form an outer frame structure, reserve and install riveting fasteners and installation plug-ins at designated positions on the side;

[0032] (2) Honeycomb phenolic foaming: cut the honeycomb structure of the corresponding size and thickness according to the inner diameter of the aluminum alloy frame. In this embodiment, an aluminum honeycomb is used. The honeycomb structure is filled with phenolic foaming technology. The phenolic foam used is as follows Ingredients and parts by weight of raw materials are prepared: phenolic resin 900, curing agent 180, foaming agent 90, foam stabilizer 18. The phenolic resin is a thermosetting foamable phenolic resin, the viscosity of the resin is controlled at 100 cps, and the curing agent is Ester curing agent prepared by pre-reaction of phenolsulfonic ...

Embodiment 3

[0035] A manufacturing process of dismountable mobile house composite board adopts the following steps:

[0036] (1) Aluminum alloy outer frame production: cut and weld aluminum alloy profiles to form an outer frame structure, reserve and install riveting fasteners and installation plug-ins at designated positions on the side;

[0037] (2) Honeycomb phenolic foaming: cut the honeycomb structure corresponding to the size and thickness according to the inner diameter of the aluminum alloy outer frame. In this embodiment, aramid honeycomb is used. The phenolic foaming technology is used to fill the foam in the honeycomb structure. The phenolic foam used is The following components and parts by weight of raw materials are prepared: phenolic resin 900, curing agent 180, foaming agent 90, foam stabilizer 18. The phenolic resin is a thermosetting foamable phenolic resin, the viscosity of the resin is controlled at 1000cps, and the curing agent It is an ester curing agent prepared by pre-r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing process of a dismountable-mountable type mobile house composite board. The manufacturing process comprises the steps that (1) an aluminum alloy outer frame ismanufactured, specifically, aluminum alloy profiles are cut and welded to form an outer frame structure; (2) honeycomb phenolic foaming is performed, specifically, according to the inner diameter sizeof the aluminum alloy frame, a honeycomb structure with corresponding size and thickness is cut, and the honeycomb structure is filled with foam by adopting a phenolic foaming technology; and (3) thephenolic prepreg is subjected to compounding, specifically, the honeycomb structure filled with phenolic foam is embedded in the aluminum alloy frame, a phenolic prepreg plate is compounded on the surface, and then camouflage felt or decorative felt is attached to the surface of the plate. Compared with the prior art, the dismountable-mountable type mobile house composite board is excellent in heat preservation performance and fireproof performance, high in strength, good in stability and light in weight, can replace tents and build barracks, and can be used for construction of barracks of field operations such as exploration, expedition, rescue and relief work and the assembly of motor homes.

Description

Technical field [0001] The invention relates to the field of building composite board manufacturing, in particular to a manufacturing process of a dismountable mobile house composite board. Background technique [0002] At present, the field operation barracks used in barracks, exploration, exploration, rescue and disaster relief are basically tents, and some of them are mobile board houses and container-type barracks, which have many defects. The barracks built by tents have defects such as poor safety performance, no heat preservation, and no sound insulation. As a barracks, the main problem of the mobile board house is that the construction speed is slow and cannot be reused after use, which causes waste of resources and serious environmental pollution; The biggest problem with the traditional barracks is its bulkiness and inconvenient transportation. [0003] Chinese patent CN201826414U discloses a modular disassembly partition wall, which includes multiple wall panel units co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/30E04C2/36C08J9/14C08L61/06C08L83/04B32B3/12B32B9/00B32B9/04B32B27/06B32B27/42B32B37/06B32B37/10
Inventor 杨金平薛永顺
Owner ANHUI MAX TECH