Pure hydrolysis-resistant polyamide composition and preparation method thereof

A polyamide composition and hydrolysis-resistant technology, which are applied in the field of pure hydrolysis-resistant polyamide compositions and their preparation, can solve the problem of water pollution, long-term hydrolysis-resistant targets, and failure to provide pure polyamide compositions. question

Active Publication Date: 2019-06-28
江苏晋伦塑料科技有限公司
View PDF12 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of the above scheme is that the added alkali metal antioxidant is easy to precipitate, and it is polluting to the water body, so it is not suitable for the field of domestic water
Chinese patent application CN105949763A discloses an environment-friendly hot water stable polyamide composition. Although the method of adding an alkali metal antioxidant is avoided, it needs to b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pure hydrolysis-resistant polyamide composition and preparation method thereof
  • Pure hydrolysis-resistant polyamide composition and preparation method thereof
  • Pure hydrolysis-resistant polyamide composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0122] Example 2, Example 3, Comparative Example 1 and Comparative Example 2 show the hydrolysis resistance performance of polyamide 66 with different amino-terminated and carboxyl-terminated contents in hot chlorine water. These examples and comparative examples show that the amino-terminated content of the polyamide substrate increases and the carboxyl-terminated content decreases. PA66-1 is a general-purpose polyamide 66, which has about 50mmol / kg of terminal amino groups and about 80mmol / kg of terminal carboxyl groups. The resin is used as the base material composition. In Comparative Example 1, when no When using functional additives, the test piece cracked after soaking in hot chlorine water at 90°C for 500 hours, and after 1000 hours, the test piece cracked severely and completely lost its function. In comparative example 2, reference examples 2 and 3 added an appropriate amount of functional additives, but the tensile strength retention rate at 500 hours was only 35.1%...

Embodiment 1

[0123] Example 1, Example 4 and Comparative Example 3 show the hydrolysis resistance performance of the composition in hot chlorine water with different glass fiber content and long carbon chain polyamide. These examples and comparative examples show that as the proportion of glass fiber increases, the mechanical properties of the composition maintained in hot water are also better. This is mainly because the glass fiber improves the initial mechanical properties of the composition on the one hand, and reduces improve the water absorption of the composition. The substrate of Comparative Example 3 is all long carbon chain polyamide PA610, which shows excellent hydrolysis resistance. However, the cost of adding excessive long carbon chain polyamide is higher cost and lower initial mechanical properties.

[0124] Comparative Example 4 and Comparative Example 1 show that the hydrolysis resistance of the halide salt stabilizer is improved, and the hydrolysis resistance is significa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pure hydrolysis-resistant polyamide composition and a preparation method thereof, and the pure hydrolysis-resistant polyamide composition comprises the following components in percentage by mass: 40-84.80 wt% of polyamide (A), 15-60.00 wt% of glass fiber, 0.10-0.50 wt% of ethylene-maleic anhydride copolymer and 0.10-0.30 wt% of antioxidant (A), wherein the polyamide (A) is polyhexamethylene adipate and has more than 70 mmol/kg of terminal amino group or less than 60 mmol/kg of terminal carboxyl group; the polyamide and the functional auxiliary agent are added into themain feeding port of an extruder; the glass fiber is added into the feeding port at the middle section side; the pure polyamide composition with long-term heat-resistant chlorine water is obtained through screw extrusion drawing, granulation and drying; the polyamide composition has a tensile strength retention rate of at least 50% after being soaked in hot chlorine water (Cl content of 5 ppm) at90 DEG C/1000 hours.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a pure hydrolysis-resistant polyamide composition and a preparation method thereof. Background technique [0002] In the field of water pipe products and accessories, lead-free is getting more and more attention. Lead pollution will endanger human reproductive ability, kidney function and nervous system. Under the hazards of excessive lead in traditional copper products, new replacement schemes have been attracting the attention of the industry, and high-functional engineering plastics are an important direction. Compared with traditional copper and other metal materials that replace copper, engineering plastics have the advantages of light weight, corrosion resistance, and easy manufacturing. Polyamide materials are the most common choice. [0003] Tap water is generally disinfected by chlorination, so there will be free chlorine. Water pipe products used...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L77/02C08L23/08C08K7/14C08K5/527C08K5/20C08K5/134C08K5/13C08K5/3492C08K5/5393
Inventor 陈跃民陈原振林柏龄
Owner 江苏晋伦塑料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap