780mpa low-carbon low-alloy hot-dip galvanized trip steel and its rapid heat treatment method

A rapid heat treatment and hot-dip galvanizing technology, applied in heat treatment furnaces, heat treatment equipment, hot-dip plating processes, etc., can solve problems such as the increase in the cost of precious metals, and achieve the effects of superior performance, increased elongation, and increased tensile strength.

Active Publication Date: 2021-06-15
BAOSHAN IRON & STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By reducing the addition of Si and Mn, and adding P, Nb, Mo, Cr and other alloys to improve the strength, it can greatly reduce the selective oxidation in the process of continuous annealing and galvanizing, improve its platability, and ensure its strength and plasticity at 20GPa% The above, but the ultra-fast cooling technology is adopted after hot rolling, which significantly increases the requirements for equipment, and the addition of precious metals also brings about an increase in cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 780mpa low-carbon low-alloy hot-dip galvanized trip steel and its rapid heat treatment method
  • 780mpa low-carbon low-alloy hot-dip galvanized trip steel and its rapid heat treatment method
  • 780mpa low-carbon low-alloy hot-dip galvanized trip steel and its rapid heat treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] The chemical composition of the selected raw material steel is calculated by weight percentage: C-0.16%, Mn-1.6%, Si-1.4%, and the balance is Fe and unavoidable impurity elements. The steel plate before heat treatment is cold-rolled strip steel, and the cold-rolling reduction rate is 65%. The microstructure of steel plate after cold rolling is composed of pearlite and ferrite.

[0061] GI product heat treatment process steps are as follows:

[0062] 1) Heat the steel plate to 770°C at a heating rate of 300°C / s and keep it warm for 40s;

[0063] 2) Cool the steel plate to 410°C at a cooling rate of 40°C / s and keep it warm for 215s;

[0064] 3) Heating from 410°C to 460°C for hot-dip galvanizing;

[0065] 4) Rapid cooling to room temperature at a cooling rate of 50°C / s.

[0066] The heat treatment steps of GA products are as follows:

[0067] 1) Heat the steel plate to 770°C at a heating rate of 300°C / s and keep it warm for 40s;

[0068] 2) The steel strip is cooled...

Embodiment 2

[0077] The chemical composition of the selected raw material steel is calculated by weight percentage: C-0.22%, Mn-2.2%, Si-1.2%, and the balance is Fe and unavoidable impurity elements. The steel plate before heat treatment is cold-rolled strip steel, and the cold-rolling reduction rate is 55%. The microstructure of steel plate after cold rolling is composed of pearlite and ferrite.

[0078] GI product heat treatment steps are as follows:

[0079] 1) Heat the strip steel plate to 800°C at a heating rate of 30°C / s and keep it warm for 90s;

[0080] 2) The steel strip is cooled to 430°C at a cooling rate of 100°C / s, and held for 200s;

[0081] 3) The strip steel is heated from 430°C to 470°C for hot-dip galvanizing;

[0082] 4) After galvanizing, cool to room temperature at a cooling rate of 150°C / s.

[0083] The heat treatment steps of GA products are as follows:

[0084] 1) Heat the steel plate to 800°C at a heating rate of 30°C / s, and keep it warm for 90s;

[0085] 2) ...

Embodiment 3

[0094] The chemical composition of the selected raw material steel is calculated by weight percentage: C-0.18%, Mn-2.0%, Si-1.6%, and the balance is Fe and unavoidable impurity elements. The steel plate before heat treatment is cold-rolled strip steel, and the cold-rolling reduction rate is 65%. The microstructure of steel plate after cold rolling is composed of pearlite and ferrite.

[0095] GI product heat treatment steps are as follows:

[0096] 1) Heat the steel plate to 850°C at a heating rate of 200°C / s and keep it warm for 65s;

[0097] 2) The steel strip is cooled to 420°C at a cooling rate of 80°C / s, and held for 300s;

[0098] 3) The strip steel is heated from 420°C to 465°C for hot-dip galvanizing;

[0099] 4) Cool to room temperature at a cooling rate of 100°C / s.

[0100] The heat treatment steps of GA products are as follows:

[0101] 1) Heat the steel plate to 850°C at a heating rate of 200°C / s and keep it warm for 65s;

[0102] 2) The steel strip is cooled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
strong plastic productaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

780MPa level low-carbon low-alloy hot-dip galvanized TRIP steel and its rapid heat treatment method, the chemical composition of the steel is C: 0.16-0.22%, Si: 1.2-1.6%, Mn: 1.6-2.2%, and the balance is Fe and unavoidable impurities. The invention finally obtains a three-phase structure in which bainite and austenite are evenly distributed on the ferrite matrix by controlling the recrystallization and phase transformation process during heating and the phase transformation process during cooling. Among them, the average grain size of bainite and austenite is 1-3 μm; bainite is submicron granular; austenite is island-shaped and evenly distributed equiaxed grains; overall, the volume of bainite in the three-phase structure The fraction is 35%-75%, the volume fraction of ferrite is 10%-60%, and the volume fraction of austenite is 5%-15%. Rapid heat treatment improves the mechanical properties of the material while improving the heat treatment efficiency, and expands the material properties Interval range.

Description

technical field [0001] The invention belongs to the technical field of rapid heat treatment of materials, and in particular relates to a 780MPa low-carbon low-alloy hot-dip galvanized TRIP steel and a rapid heat treatment method thereof. Background technique [0002] With the gradual improvement of people's awareness of energy conservation and material safety in service, the use of high-strength steel, especially advanced high-strength steel, is increasing. This also makes iron and steel enterprises and scientific research institutes pay more and more attention to the development of advanced high-strength steel. In order to further improve the strength-plastic product of steel products, the development of advanced high-strength steel represented by TRIP (phase transformation induced plastic deformation) steel has been paid more and more attention. The cold rolling heat treatment process of cold rolled TRIP steel consists of two stages of austenitizing annealing and bainite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C21D9/52C23C2/06C23C2/40
Inventor 孟庆格李俊王健张利祥马新建
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com