Cellulose graft copolymer, and preparation method and application thereof

A technology of cellulose grafting and grafting copolymers, applied in chemical instruments and methods, drilling compositions, etc., can solve the problems of viscosity, strength improvement, little change in relative molecular weight, etc., to meet environmental protection, The effect of improving temperature resistance and temperature resistance and improving filtration effect

Pending Publication Date: 2019-07-05
CHINA UNIV OF PETROLEUM (EAST CHINA) +1
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with natural cellulose, modified cellulose has a certain improvement in performance, but the relative mo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cellulose graft copolymer, and preparation method and application thereof
  • Cellulose graft copolymer, and preparation method and application thereof
  • Cellulose graft copolymer, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0048] According to a preferred embodiment of the present invention, the method for preparing the cellulose graft copolymer includes the following steps:

[0049] 1) Add water to the reactor, add CMC under a nitrogen atmosphere, then heat to the temperature required for polymerization and stir evenly;

[0050] 2) Add NaOH solution to the reactor to adjust the pH of the solution;

[0051] 3) Add the aqueous solution of the cerium ion initiator to the reactor, and then stir it evenly;

[0052] 4) Add the respective aqueous solutions of AM, AMPS and METAC to the reactor to carry out a graft polymerization reaction to form a polymer solution containing the cellulose graft copolymer;

[0053] 5) The polymer solution is washed, filtered by suction, rinsed and dried to obtain a crude product of the graft copolymer;

[0054] 6) Extracting and drying the crude product to obtain the cellulose graft copolymer.

[0055] In the present invention, the mass ratio of the amount of water to the polymerize...

Example Embodiment

[0062] Example 1

[0063] This example is used to illustrate the cellulose graft copolymer of the present invention and its preparation method.

[0064] 1) Add deionized water to a four-necked flask placed in a water bath, then add CMC under the protection of nitrogen and heat to 45°C, and stir at constant temperature for 30 minutes;

[0065] 2) Add 30% by weight NaOH solution to the four-necked flask and adjust the pH to 7;

[0066] 3) Add the aqueous solution of cerium ammonium nitrate to a four-necked flask and stir at constant temperature for 10 minutes;

[0067] 4) Put the aqueous solution of AM, the aqueous solution of AMPS and the aqueous solution of METAC into the four-necked flask respectively, continue to pour in nitrogen, and react at a constant temperature for 4h;

[0068] Wherein, the mass ratio of the amount of water to the total amount of polymerized monomers is 100:6, the mass of CMC:AM:AMPS:METAC is 4:2:1:1, and the amount of cerium ammonium nitrate is 0.3% by weight of ...

Example Embodiment

[0075] Example 2-11

[0076] This example is used to illustrate the cellulose graft copolymer of the present invention and its preparation method.

[0077] The cellulose graft copolymer was prepared according to the method of Example 1, except that the ratio of the monomer mixture, the amount of initiator and the graft polymerization conditions were adjusted to prepare the cellulose graft copolymer A2-A11 The above adjustment and the viscosity average molecular weight of the obtained polymer are specifically shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of fluid loss agents, and discloses a cellulose graft copolymer, and a preparation method and an application thereof. The graft copolymer includes a carboxymethyl cellulose main chain and side chains, and the side chains include a structural unit represented by formula (1), a structural unit represented by formula (2), and a structural unit represented by formula(3); and a mass ratio of the carboxymethyl cellulose main chain to the structural unit of the formula (1) to the structural unit of the formula (2) to the structural unit of the formula (3) is (2-6):(1-4):(1-3):1. The cellulose graft copolymer can enhance the temperature resistance, the calcium resistance and the salt resistance of a drilling fluid and improve the fluid loss reduction effect of the drilling fluid when used in the drilling fluid as a fluid loss agent, and also can meet environmental protection requirements.

Description

technical field [0001] The invention relates to the field of fluid loss control agents, in particular to a cellulose graft copolymer, a preparation method of the cellulose graft copolymer, and an application of the cellulose graft copolymer in drilling fluid. Background technique [0002] With the development of the petroleum industry and the continuous increase of oil demand, the exploration and development of oil and gas is gradually developing towards the middle and deep areas, and the environmental protection in oil and gas exploration and development is getting more and more attention, and the drilling fluid treatment agent is indispensable in the production process. It is an indispensable part, and its requirements are getting higher and higher. Therefore, it is an urgent problem to be solved to improve the safety, high efficiency and environmental protection performance of drilling fluid. [0003] Among drilling fluid treatment agents, fluid loss control agents are us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F251/02C08F220/56C08F220/58C08F220/34C09K8/035
CPCC08F251/02C09K8/035C08F220/585
Inventor 黄维安李轩宿振国陈二丁刘均一曹杰王婧雯钟汉毅
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap