Water-based resin sand stone-like paint and preparation method thereof

A technology of water-based resin and real stone paint, applied in the field of coatings, can solve problems such as serious color difference, increased pressure on environmental protection, and increased difficulty in mining colored sand, achieving the effects of fast dispersion, improved heat resistance, and improved efficiency

Pending Publication Date: 2019-08-02
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its core raw material, natural colored sand, is a non-renewable resource. As the consumption increases year by year, resources become more and more tense. With the promotion of national environmental protection policies, the pressure on environmental protection continues to increase,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based resin sand stone-like paint and preparation method thereof
  • Water-based resin sand stone-like paint and preparation method thereof
  • Water-based resin sand stone-like paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example 1

[0034] A water-based resin sand real stone paint comprising the following components in parts by weight:

[0035]

[0036] The preparation method of the above water-based resin sand real stone paint includes the following steps:

[0037] (1) Select a suitable container, weigh 3 parts of cellulose and add 120 parts of water while stirring, and stir at room temperature for 20 minutes at a speed of 750 rpm, until the state no longer changes;

[0038] (2) Weigh 2 parts of organic bentonite and add 80 parts of water while stirring, and stir at room temperature for 20 minutes at a speed of 750 rpm, and stir until the state no longer changes;

[0039] (3) Mix the prepared cellulose solution and bentonite solution in proportion, and stir for 10 minutes at 900 rpm;

[0040] (4) Add multifunctional additives, emulsions, dispersants, antifreeze, film-forming additives, defoamers, preservatives, and thickeners in sequence at a speed of 750 rpm. When adding each component Need to ...

Example Embodiment

[0042] Example 2

[0043] A water-based resin sand real stone paint comprising the following components in parts by weight:

[0044]

[0045] The preparation method of the above water-based resin sand real stone paint includes the following steps:

[0046] (1) Select a suitable container, weigh 2 parts of cellulose and add 80 parts of water while stirring, and stir for 20 minutes at room temperature at a rotation speed of 600 rpm, until the state no longer changes;

[0047] (2) Weigh 1.5 parts of organic bentonite into 70 parts of water while stirring, and stir for 20 minutes at room temperature at a speed of 800 rpm, and stir until the state no longer changes;

[0048] (3) Mix the prepared cellulose solution and bentonite solution in proportion, and stir at 850 rpm for 10 minutes;

[0049] (4) Add multifunctional additives, emulsions, dispersants, antifreeze agents, film-forming additives, defoamers, preservatives and thickeners in sequence at a speed of 700 rpm. Need to stir for 2 min...

Example Embodiment

[0051] Example 3

[0052] A water-based resin sand real stone paint comprising the following components in parts by weight:

[0053]

[0054] The above water-based resin sand real stone paint and its preparation method include the following steps:

[0055] (1) Select a suitable container, weigh 2 parts of cellulose and add 80 parts of water while stirring, and stir for 20 minutes at room temperature at a rotation speed of 900 rpm, until the state no longer changes;

[0056] (2) Weigh 1.5 parts of organic bentonite and add 70 parts of water under stirring, and stir at room temperature at 600 rpm for 20 minutes, and stir until the state no longer changes;

[0057] (3) Mix the prepared cellulose solution and bentonite solution in proportion, and stir for 10 minutes at 900 rpm;

[0058] (4) Add multifunctional additives, emulsions, dispersants, antifreeze, film-forming additives, defoamers, preservatives, and thickeners in sequence at 900 rpm. Need to stir for 3 minutes to make the real sto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses water-based resin sand stone-like paint and a preparation method thereof, and belongs to the technical field of paint. The water-based resin sand stone-like paint comprises components as follows: water, cellulose, organobentonite, a multifunctional auxiliary, a pure acrylic emulsion, a dispersing agent, an anti-freezing agent, a coalescing agent, a defoaming agent, a corrosion remover, a thickening agent and water-based resin sand. Compared with natural color sand stone-like paint, the water-based resin sand stone-like paint has no chromatic aberration difference between batches and has excellent acid and alkali resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based resin sand real stone paint and a preparation method thereof. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. The buildings decorated with real stone paint have natural and real natural color, which gives people elegant, harmonious and solemn aesthetic feeling. It is suitable for indoor and outdoor decoration of all kinds of buildings. Especially when it is decorated on curved buildings, it is vivid and lifelike, and has an effect of returning to nature. [0003] In recent years, real stone paint and texture paint have gradually become one of the mainstream varieties of architectural paint. However, its core raw material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/04C04B20/10
CPCC04B26/04C04B20/1037C04B2111/00482C04B24/383C04B14/104C04B24/2641C04B24/2652C04B24/02C04B2103/50C04B2103/67C04B24/282C04B14/06C04B24/122C04B24/045C04B20/1033
Inventor 程志林江生锁郑毅胡中源
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap