Production technology of high-temperature-resistant stainless steel backing paper

A production process, stainless steel technology, applied in the field of papermaking, can solve the problem that the lining paper cannot meet the environmental requirements of high temperature

Pending Publication Date: 2019-09-17
ZHEJIANG HUACHUAN IND GRP
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a production process of high temperature resistant stainless steel backing paper, which solves the technical problem that the backing paper in the prior art cannot meet the high temperature environmental requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The manufacturing process of a kind of high temperature resistant stainless steel backing paper provided by the present invention comprises the following steps:

[0025] S1: put 100 parts by weight of hardwood pulp and 60 parts by weight of softwood pulp into a beater and stir to prepare a pulp liquid for use;

[0026] S2: Pour the pulp liquid in step S1 into the steam oven, add 10 parts by weight of polytetrafluoroethylene emulsion, 5 parts of cellulase, and 2 parts of hemicellulase, and pass it through the mixer at a speed of 30r / min Stir and heat to raise the temperature of the steamer to 200°C, boil the slurry, keep it warm for 1min, stop heating, and set aside;

[0027] S3: Add 10 parts by weight of silicon disulfide, 20 parts of sodium silicate and 12 parts of corundum powder into the mixing tank, add water in a ratio of 1:5 by weight, and then start the mixer at a speed of 65r / min. The above-mentioned materials are mixed with water to prepare filler, which is se...

Embodiment 2

[0038] A manufacturing process of high-temperature-resistant stainless steel backing paper, comprising the following steps:

[0039] S1: Put 120 parts by weight of hardwood pulp and 70 parts by weight of softwood pulp into a beater for stirring to prepare a pulp liquid for use;

[0040] S2: Pour the pulp liquid in step S1 into the steam oven, add 15 parts by weight of polytetrafluoroethylene emulsion, 8 parts of cellulase, and 5 parts of hemicellulase, and pass it through the mixer at a speed of 30r / min Stir and heat to raise the temperature of the steamer to 350°C, boil the slurry, keep it warm for 2 minutes, stop heating, and set aside;

[0041] S3: Add 15 parts by weight of silicon disulfide, 30 parts of sodium silicate and 15 parts of corundum powder into the mixing tank, add water at a ratio of 1:5 by weight, and then start the mixer at a speed of 65r / min. The above-mentioned materials are mixed with water to prepare filler, which is set aside;

[0042] S4: Mix the solu...

Embodiment 3

[0052] A manufacturing process of high-temperature-resistant stainless steel backing paper, comprising the following steps:

[0053] S1: Put 110 parts by weight of hardwood pulp and 65 parts by weight of softwood pulp into a beater for stirring to prepare a pulp liquid for use;

[0054] S2: Pour the pulp liquid in step S1 into the steam oven, add 12 parts by weight of polytetrafluoroemulsion emulsion, 6 parts of cellulase, and 3 parts of hemicellulase, and pass it through the mixer at a speed of 30r / min Stir and heat to raise the temperature of the steamer to 280°C, boil the slurry, keep it warm for 1min, stop heating, and set aside;

[0055] S3: Add 12 parts by weight of silicon disulfide, 25 parts of sodium silicate and 12 parts of corundum powder into the mixing tank, add water in a ratio of 1:5 by weight, and then start the mixer at a speed of 65r / min. The above-mentioned materials are mixed with water to prepare filler, which is set aside;

[0056] S4: Mix the solutions...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production technology of high-temperature-resistant stainless steel backing paper. The production technology of the high-temperature-resistant stainless steel backing paper comprises the steps of adopting hardwood pulp and softwood pulp as paper pulp, then adding filler to prepare a semi-finished product, and finally, conducting sizing and deacidification treatment. By means of the production technology of the high-temperature-resistant stainless steel backing paper, the technical problem that in the prior art, backing paper cannot meet the requirements of high-temperature environments is solved.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a manufacturing process of high-temperature-resistant stainless steel backing paper. Background technique [0002] Stainless steel lining paper is a new type of special industrial paper that is gradually matched with the domestic and foreign stainless steel industry to protect the quality of stainless steel plate products with the vigorous development of the stainless steel industry in recent years. According to the different stainless steel production process, stainless steel lining paper can be divided into: high temperature resistant stainless steel lining paper suitable for hot-pressed stainless steel plate and ordinary stainless steel lining paper suitable for cold-rolled stainless steel plate. [0003] Stainless steel lining paper is a kind of special paper used to prevent friction between stainless steel plates during cold rolling of high-grade stainless steel plates. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21F11/00D21H27/00D21H17/68D21H17/66D21H19/36
CPCD21F11/00D21H27/00D21H17/68D21H17/66D21H19/36
Inventor 冯小义冯沾善楼旭军
Owner ZHEJIANG HUACHUAN IND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com