Reflective thermal-insulating sand and preparation method thereof

A technology of quartz sand and parts by weight, applied in the field of reflective thermal insulation sand and its preparation, can solve the problems of unsatisfactory reflective thermal insulation effect of high-build coatings, difficult to master the construction effect, easy to bloom, etc., and achieve excellent reflective thermal insulation effect. Thermal effect, low cost, smooth surface effect

Inactive Publication Date: 2019-09-20
郑州科威科建筑材料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the reflective heat-insulating coatings applied to building facades are mainly thin-coated, such as reflective heat-insulating latex paint; there are also a few that use reflective heat-insulating materials to add real stone paint slurry to make reflective heat-insulating thick paste Paint, that is, reflective and heat-insulating real stone paint or texture paint, but the thick-build paint made by this method has an unsatisfactory reflective and heat-insulating effect, and the construction effect is not easy to grasp, and it is easy to fade and lose color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A reflective heat-insulating sand, comprising the following components in parts by weight: 80 parts of quartz sand, 40 parts of emulsion, 20 parts of reflective heat-insulating titanium dioxide, 20 parts of functional filler, 0.1 part of dispersing wetting agent, and 5 parts of film-forming aid 0.6 parts of thickener, 1 part of defoamer, 0.3 parts of antifreeze, 0.1 part of fungicide, 1 part of pH regulator, 1 part of toner, and 10 parts of deionized water.

[0022] A method for preparing reflective heat insulating sand, comprising the following steps:

[0023] S1: Stir and disperse the deionized water, dispersing wetting agent, thickener, defoamer, antifreeze and bactericide in the formula for 5 minutes under the condition of 2000r / min to obtain a mixed solution, which is ready for use;

[0024] S2: Stir and disperse the reflective heat-insulating titanium dioxide, functional fillers and film-forming aids at 1000r / min for 5min, add the mixed solution in step S1 to it, ...

Embodiment 2

[0027] A reflective heat-insulating sand, comprising the following components in parts by weight: 82 parts of quartz sand, 45 parts of emulsion, 25 parts of reflective heat-insulating titanium dioxide, 23 parts of functional filler, 0.1 part of dispersing wetting agent, and 6 parts of film-forming aid 0.6 parts of thickener, 1 part of defoamer, 0.3 parts of antifreeze, 0.1 part of bactericide, 1 part of pH regulator, 1 part of toner, 13 parts of deionized water.

[0028] A method for preparing reflective heat insulating sand, comprising the following steps:

[0029] S1: Stir and disperse the deionized water, dispersing wetting agent, thickener, defoamer, antifreeze and bactericide in the formula for 10 minutes under the condition of 2500r / min to obtain a mixed solution, which is ready for use;

[0030] S2: Stir and disperse the reflective heat-insulating titanium dioxide, functional fillers and film-forming aids at 1500r / min for 10min, add the mixed solution in step S1 to it, ...

Embodiment 3

[0033] A reflective heat-insulating sand, comprising the following components in parts by weight: 85 parts of quartz sand, 50 parts of emulsion, 30 parts of reflective heat-insulating titanium dioxide, 250 parts of functional fillers, 0.5 parts of dispersing wetting agent, and 8 parts of film-forming aids 1.5 parts of thickener, 1.2 parts of defoamer, 0.3 parts of antifreeze, 0.1 part of fungicide, 1 part of pH regulator, 1 part of toner, 15 parts of deionized water.

[0034] A method for preparing reflective heat insulating sand, comprising the following steps:

[0035] S1: Stir and disperse the deionized water, dispersing wetting agent, thickener, defoamer, antifreeze and bactericide in the formula for 15 minutes under the condition of 3000r / min to obtain a mixed solution, which is ready for use;

[0036] S2: Stir and disperse the reflective heat-insulating titanium dioxide, functional fillers and film-forming aids at 1800r / min for 15min, add the mixed solution in step S1 to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses reflective thermal-insulating sand and a preparation method thereof and belongs to the technical field of coating preparation. The sand comprises the following components in parts by weight: 80-90 parts of quartz sand, 40-60 parts of an emulsion, 20-40 parts of reflective thermal-insulating titanium dioxide, 20-30 parts of a functional filler, 0.1-1 part of a dispersion wetting agent, 5-10 parts of a film formation aid, 2-5 parts of other aids, 1-1.5 parts of a Ph value adjusting agent, 1-1.5 parts of a toner and 10-20 parts of deionized water. The sand has the characteristics of being excellent in reflective thermal-insulating effect, high in sunshine reflection rate and hemispherical emission rate, dense in coating film, smooth in surface, green and environment-friendly, free of VOC (volatile organic compound), free of industrial waste, good in heat preservation and dirt resistance, good in weather resistance, excellent in thermal insulation and long-lasting in thermal insulation; a color modulation process is simple, equipment requirements are low, the cost is low, and the raw material cost is low as water is adopted as a solvent.

Description

technical field [0001] The invention relates to the technical field of paint preparation, in particular to reflective heat-insulating sand and a preparation method thereof. Background technique [0002] At present, the reflective heat-insulating coatings applied to building facades are mainly thin-coated, such as reflective heat-insulating latex paint; there are also a few that use reflective heat-insulating materials to add real stone paint slurry to make reflective heat-insulating thick paste Paint, that is, reflective heat-insulating real stone paint or textured paint, but the thick-build paint made by this method has an unsatisfactory reflective heat-insulating effect, and the construction effect is not easy to grasp, and it is easy to fade and lose color. [0003] Based on this, the present invention designs a reflective heat insulating sand and its preparation method to solve the above-mentioned problems. Contents of the invention [0004] The purpose of the present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/10
CPCC04B26/10C04B2111/00482C04B14/06C04B14/24C04B18/027C04B2103/0068C04B2103/408C04B2103/0094C04B2103/54C04B2103/44C04B2103/601C04B2103/50C04B2103/69C04B14/305
Inventor 李蒙陈明张森石峰李生贵
Owner 郑州科威科建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com